Hydrogel connection

ABSTRACT

The disclosure relates to articles and components thereof, including outsoles, which can be used in conditions normally conducive to the accumulation of soil. In particular, the disclosure relates to articles and components thereof with a material including a hydrogel, where the hydrogel-containing material defines an external surface or side of an article. The hydrogel-containing material can prevent or reduce the accumulation of soil during use. A portion of the hydrogel-containing material is embedded into a substrate body, or a portion of the hydrogel-containing material is disposed on the outer side surface of the substrate body in a junction. The substrate body can have a lip extending from a shaft such that the shaft and the lip form the junction. Embedding the material in the substrate body, or disposing it in the junction, can minimize or prevent delamination of the hydrogel containing material during normal use.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of and priority to U.S. ProvisionalApplication Ser. No. 62/302,385, having the title “HYDROGEL CONNECTION”,filed on Mar. 2, 2016, the disclosure of which is incorporated herein byreference in its entirety.

FIELD

The present disclosure is directed to articles and components thereof,including outsoles, which are used in conditions conducive to theaccumulation of soil on the articles or components.

BACKGROUND

Articles of various types are frequently used for a variety ofactivities including outdoor activities, military use, and competitivesports. The articles frequently are exposed to soil during use and thusoften accumulate soil (e.g., wet or moist inorganic materials such asmud, dirt, and gravel, wet or moist organic material such as grass,turf, and excrement, and wet or moist combinations of inorganic andorganic materials) when the articles are used under conditions wheresoil is present. For example, components of a vehicle can accumulatesoil due to splattering from a roadway or surface being traveled over.Likewise, objects used in playgrounds, in construction areas, or thegarden can be subject to exposure to soil in the area of use bysplattering or direct contact with unpaved surfaces.

In some cases, these articles are footwear. The outsoles of these typesof footwear often are designed to provide traction on soft and slipperysurfaces, such as unpaved surfaces including grass and dirt. Forexample, exaggerated tread patterns, lugs, cleats or spikes (bothintegral and removable), and rubber formulations which provide improvedtraction under wet conditions, have been used to improve the level oftraction provided by the outsoles.

While these conventional means generally help give footwear improvedtraction, the outsoles often accumulate soil. In some instances, thesoil can accumulate in the tread pattern (when a tread pattern ispresent), around and between lugs (when lugs are present), or on shaftsof the cleats, in the spaces surrounding the cleats, and in theinterstitial regions between the cleats (when cleats are present). Theaccumulations of soil can weigh down these types of articles andinterfere with their normal use.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the disclosure, reference should bemade to the following detailed description and accompanying drawingswherein:

FIG. 1 is a bottom isometric view of an article of footwear in an aspectof the present disclosure having an outsole including ahydrogel-containing material (e.g., in the form of a film) in accordancewith the present disclosure;

FIG. 2 is a bottom view of the outsole of the article of footwear shownin FIG. 1, where an upper of the footwear is omitted;

FIG. 3 is a lateral side view of the outsole shown in FIG. 2;

FIG. 4 is a medial side view of the outsole shown in FIG. 2;

FIG. 5 is an expanded sectional view of a portion of the outsole,illustrating a hydrogel-containing material in accordance with thepresent disclosure in a dry state secured to a backing plate adjacent toa traction element (e.g., a cleat);

FIG. 5A is an expanded sectional view of the portion of the outsoleshown in FIG. 5, where the hydrogel-containing material is partiallysaturated and swollen;

FIG. 5B is an expanded sectional view of the portion of the outsoleshown in FIG. 5, where the material is fully saturated and swollen;

FIGS. 6-9 are expanded sectional views of the portion of the outsoleshown in FIG. 5, illustrating the soil-shedding performance of theoutsole during a foot strike motion on an unpaved surface;

FIG. 10 is a side cross-sectional view of an outsole in an aspectaccording to the disclosure including a soil-shedding material and soilbeing shed therefrom, during impact with a ground surface;

FIGS. 10A-F are side cross-sectional views of a substrate body, a shaft,and an embedded hydrogel-containing material in aspects according to thedisclosure;

FIG. 11 is a bottom view of an article of footwear in another aspect ofthe present disclosure having an outsole including a hydrogel-containingmaterial in accordance with the present disclosure, the material havingdiscrete and separate sub-segments;

FIG. 12 is an expanded sectional view of a portion of an outsole inanother aspect of the present disclosure, which includes ahydrogel-containing material in accordance with the present disclosure,the material being present in a recessed pocket of an outsole backingplate;

FIG. 13 is an expanded sectional view of a portion of an outsole inanother aspect of the present disclosure, which includes an outsolebacking plate having one or more indentations, and a hydrogel-containingmaterial in accordance with the present disclosure, thehydrogel-containing material being present in and over the indentations;

FIG. 14 is an expanded sectional view of a portion of an outsole inanother aspect of the present disclosure, which includes an outsolebacking plate having one or more indentations having locking members,and a hydrogel-containing material in accordance with the presentdisclosure, the hydrogel-containing material being present in and overthe indentations;

FIG. 15 is a bottom view of an article of footwear in another aspect ofthe present disclosure, which illustrates an example golf shoeapplication;

FIG. 16 is a bottom perspective view of an article of footwear inanother aspect of the present disclosure, which illustrates an examplebaseball shoe application;

FIG. 17 is a bottom perspective view of an article of footwear inanother aspect of the present disclosure, which illustrates an exampleAmerican football shoe application;

FIG. 18 is a bottom perspective view of an article of footwear inanother aspect of the present disclosure, which illustrates an examplehiking shoe application;

FIG. 19 is a photograph of an example a hydrogel-containing material ofthe present disclosure; and

FIGS. 20A-H include photographs of articles of footwear with and withouta hydrogel-containing material according to the disclosure after beingworn and used during wet and muddy game conditions.

The articles of footwear shown in the figures are illustrated for usewith a user's right foot. However, it is understood that the followingdiscussion applies correspondingly to left-footed articles of footwearas well.

DESCRIPTION

The present disclosure is directed to an article of manufacture, orcomponents thereof having surface-defining materials that are capable oftaking up water. It has been discovered that particular materialscomprising a polymeric hydrogel when disposed on an externally-facingsurface of an article can be effective at preventing or reducing theaccumulation of soil on externally-facing surfaces of the article.Additionally, it has been found that the selection of certain polymerichydrogel materials, in terms of their physical characteristics asmeasured using the test methods described herein, is useful to achievespecific performance benefits for the articles as disclosed herein. Thisapplication is related to the U.S. Provisional Application 62/199,083,filed Jul. 30, 2015, incorporated herein by reference in its entirety.

Additionally, it has been discovered that particular constructions canprevent or reduce the tendency of the polymeric hydrogel materials todelaminate from a substrate which does not swell significantly whenexposed to water. Specifically, it has been found that embedding aportion of the hydrogel-containing material into the substrate body orotherwise protecting a portion of the hydrogel-containing material withthe substrate body (e.g., embedding an edge of the material into thesubstrate body) can prevent or reduce delamination of thehydrogel-containing material. When swollen with water, polymerichydrogel-containing materials can delaminate from a substrate which doesnot swell to the same extent. The presence of the embedded portion ofthe hydrogel-containing material in the substrate body has been found tosignificantly reduce swelling-induced delamination of polymerichydrogel-containing materials from the area of the substrate bodysurrounding the embedded region.

Accordingly, the present disclosure describes articles, components ofarticles, use of these polymeric hydrogel materials in articles andcomponents of articles, as well as methods of manufacturing and usingthe articles and components of articles. The material which includes thepolymeric hydrogel (i.e. hydrogel-containing material) defines at leasta portion of a surface of the articles. In other words, the materialdefines at least a portion of an exterior surface of the component orarticle that is externally-facing.

As can be appreciated, preventing or reducing soil accumulation onarticles during use on unpaved, muddy, or wet surfaces can significantlyaffect the weight of accumulated soil adhered to the article during use.Preventing or reducing soil accumulation on an article can help improvesafety. Further, preventing or reducing soil accumulation on the articlecan make it easier to clean the article following use.

In a first aspect, the present disclosure is directed to an article ofmanufacture having a substrate body and a hydrogel-containing material.The substrate body has a first side. The hydrogel-containing materialcan be secured to the first side such that a portion of thehydrogel-containing material is embedded into the substrate body. Thehydrogel-containing material can define at least a portion of a firstexternal surface of the article.

In accordance with the present disclosure, the hydrogel-containingmaterial can be a material which can be characterized based on itsability to take up water. The hydrogel-containing material can be amaterial which has a water uptake capacity at 24 hours of greater than40% by weight, as characterized by the Water Uptake Capacity Test withthe Article Sampling Procedure, the Co-extruded Film Sampling Procedure,the Neat Film Sampling Procedure, or the Neat Material SamplingProcedure as described below. Additionally or alternatively, thematerial can have a water uptake capacity at 1 hour of greater than 100%by weight. The hydrogel-containing material can have a water uptake rateof greater than 20 g/(m²×min^(0.5)), as characterized by the WaterUptake Rate Test with the Article Sampling Procedure, the Co-extrudedFilm Sampling Procedure, the Neat Film Sampling Procedure, or the NeatMaterial Sampling Procedure. The hydrogel-containing material can have awater uptake rate of greater than 100 g/(m²×min^(0.5)). Thehydrogel-containing material can be a material which has both a wateruptake capacity at 24 hours of greater than 40% by weight, and a wateruptake rate of greater than 20 g/(m²×min^(0.5)). The hydrogel-containingmaterial can have a swell thickness increase at 1 hour greater than 20%,as characterize by the Swelling Capacity Test with the Article SamplingProcedure, the Co-extruded Film Sampling Procedure, or the Neat FilmSampling Procedure. The hydrogel-containing material can be a materialwhich has both a water uptake capacity at 24 hours of greater than 40%by weight, and a swell thickness increase at 1 hour greater than 20%.

Additionally, the hydrogel-containing material of the present disclosurecan be characterized based on its surface properties. Thehydrogel-containing material can be a material wherein the at least aportion of the first surface defined by the material has a wet-statecontact angle less than 80°, as characterized by the Contact Angle Testwith the Article Sampling Procedure, the Co-extruded Film SamplingProcedure, or the Neat Film Sampling Procedure; and wherein the materialwhich has a water uptake capacity at 24 hours of greater than 40% byweight, as characterized by the Water Uptake Capacity Test with theArticle Sampling Procedure, the Co-extruded Film Sampling Procedure, theNeat Film Sampling Procedure, or the Neat Material Sampling Procedure.The material can be a material wherein the at least a portion of thefirst surface defined by the material has a wet-state coefficient offriction less than 0.8, as characterized by the Coefficient of FrictionTest with the Article Sampling Procedure, the Co-extruded Film SamplingProcedure, or the Neat Film Sampling Procedure; and wherein the materialhas a water uptake capacity at 24 hours of greater than 40% by weight,as characterized by the Water Uptake Capacity Test with the ArticleSampling Procedure, the Co-extruded Film Sampling Procedure, the NeatFilm Sampling Procedure, or the Neat Material Sampling Procedure.

The hydrogel-containing material can be a material wherein the at leasta portion of the first surface defined by the material has a wet-statecontact angle less than 80°, as characterized by the Contact Angle Testwith the Article Sampling Procedure, the Co-extruded Film SamplingProcedure, or the Neat Film Sampling Procedure; and wherein the materialwhich has a water uptake capacity at 1 hour of greater than 100% byweight, as characterized by the Water Uptake Capacity Test with theArticle Sampling Procedure, the Co-extruded Film Sampling Procedure, theNeat Film Sampling Procedure, or the Neat Material Sampling Procedure.The hydrogel-containing material can be a material wherein the at leasta portion of the first surface defined by the material has a wet-statecoefficient of friction less than 0.8, as characterized by theCoefficient of Friction Test with the Article Sampling Procedure, theCo-extruded Film Sampling Procedure, or the Neat Film SamplingProcedure; and wherein the material has a water uptake capacity at 1hour of greater than 100% by weight, as characterized by the WaterUptake Capacity Test with the Article Sampling Procedure, theCo-extruded Film Sampling Procedure, the Neat Film Sampling Procedure,or the Neat Material Sampling Procedure.

Further, the hydrogel-containing material of the present disclosure canbe characterized based on changes in properties between its dry stateand its wet state. The material can be a material which has a wet-stateglass transition temperature when equilibrated at 90% relative humidityand a dry-state glass transition temperature when equilibrated at 0%relative humidity, each as characterized by the Glass TransitionTemperature Test with the Neat Material Sampling Process, wherein thewet-state glass transition temperature is more than 6° C. less than thedry-state glass transition temperature; and wherein the materialpreferably also has a water uptake capacity at 24 hours of greater than40% by weight, as characterized by the Water Uptake Capacity Test withthe Article Sampling Procedure, the Co-extruded Film Sampling Procedure,the Neat Film Sampling Procedure, or the Neat Material SamplingProcedure. The hydrogel-containing material can have a wet-state storagemodulus when equilibrated at 90% relative humidity and a dry-statestorage modulus when equilibrated at 0% relative humidity, each ascharacterized by the Storage Modulus Test with the Neat MaterialSampling Procedure, wherein the wet-state storage modulus is less thanthe dry-state storage modulus of the material; and wherein the materialpreferably also has a water uptake capacity at 24 hours of greater than40% by weight, as characterized by the Water Uptake Capacity Test withthe Article Sampling Procedure, the Co-extruded Film Sampling Procedure,the Neat Film Sampling Procedure, or the Neat Material SamplingProcedure.

The hydrogel-containing material can be a material which has a wet-stateglass transition temperature when equilibrated at 90% relative humidityand a dry-state glass transition temperature when equilibrated at 0%relative humidity, each as characterized by the Glass TransitionTemperature Test with the Neat Material Sampling Process, wherein thewet-state glass transition temperature is more than 6° C. less than thedry-state glass transition temperature; and wherein the materialpreferably also has a water uptake capacity at 1 hour of greater than100% by weight, as characterized by the Water Uptake Capacity Test withthe Article Sampling Procedure, the Co-extruded Film Sampling Procedure,the Neat Film Sampling Procedure, or the Neat Material SamplingProcedure. The hydrogel-containing material can have a wet-state storagemodulus when equilibrated at 90% relative humidity and a dry-statestorage modulus when equilibrated at 0% relative humidity, each ascharacterized by the Storage Modulus Test with the Neat MaterialSampling Procedure, wherein the wet-state storage modulus is less thanthe dry-state storage modulus of the material; and wherein the materialpreferably also has a water uptake capacity at 1 hour of greater than100% by weight, as characterized by the Water Uptake Capacity Test withthe Article Sampling Procedure, the Co-extruded Film Sampling Procedure,the Neat Film Sampling Procedure, or the Neat Material SamplingProcedure.

The hydrogel-containing material of the present disclosure can also oralternatively be characterized based on the type of hydrogel which itincludes. In some examples, the hydrogel of the material can comprise orconsist essentially of a thermoplastic hydrogel. The hydrogel of thematerial can comprise or consist essentially of one or more polymersselected from the group consisting of a polyurethane, a polyamidehomopolymer, a polyamide copolymer, and combinations thereof. Forexample, the polyamide copolymer can comprise or consist essentially ofa polyamide block copolymer.

The articles of the present disclosure can also or alternatively becharacterized based on their structure such as, for example, thethickness of the hydrogel-containing material (e.g. on the ground-facingarticle surface), how the hydrogel-containing material is arranged (e.g.on an outsole), whether or not traction elements are present, whether ornot the hydrogel-containing material is affixed to another layer (e.g. abacking plate or substrate body), and the like.

In one example, the hydrogel-containing material can be present in anarticle of footwear. The hydrogel-containing material can be present aspart of or adhering to an outsole for footwear (e.g. a ground-facingsurface). Preventing or reducing soil accumulation on outsoles duringwear on unpaved surfaces can significantly affect the weight ofaccumulated soil adhered to the outsole during wear, reducing fatigue tothe wearer caused by the adhered soil. Preventing or reducing soilaccumulation on the outsole can help preserve traction during wear. Forexample, preventing or reducing soil accumulation on the outsole canimprove or preserve the performance of traction elements present on theoutsole during wear on unpaved surfaces. When worn while playing sports,preventing or reducing soil accumulation on outsoles can improve orpreserve the ability of the wearer to manipulate sporting equipment suchas a ball with the outsole of the article of footwear.

When the article is an outsole, the outsole can be an outsole having thematerial present on at least 80% of the ground-facing surface of theoutsole. The hydrogel-containing material of the outsole can have adry-state thickness ranging from 0.1 millimeters to 2 millimeters. Theoutsole can comprises one or more traction elements present on the firstsurface of the outsole. The outsole can further comprise an outsolebacking member. The outsole backing member can form at least a portionof or be secured to the outsole, wherein the material is secured to theoutsole backing member such that the material defines the at least aportion of the first surface of the outsole.

In a second aspect, the present disclosure is directed to an article offootwear comprising an outsole as disclosed herein. The article offootwear can be an article comprising an outsole and an upper, whereinthe outsole has a first, external, ground-facing surface and a secondsurface opposing the first external surface, wherein the upper issecured to the second surface of the outsole, wherein ahydrogel-containing material defines at least a portion of theground-facing first surface of the outsole. The material can be amaterial as described above, e.g. with respect to the first aspect ofthe disclosure. The article of footwear can be an article which preventsor reduces soil accumulation such that the article retains at least 10%less soil by weight as compared to a second article of footwear which isidentical to the article except that an outsole of the second article issubstantially free of the material comprising a hydrogel.

In a third aspect, the present disclosure is directed to a method ofmanufacturing an article including the steps of receiving an outsolecomprising a substrate body, the substrate body compositionallycomprising a polymeric material having a water uptake capacity of lessthan 10% by weight, as characterized by the Water Uptake Capacity Testwith the Sampling Procedure; receiving an upper; and securing theoutsole and the upper to each other such that a hydrogel-containingmaterial defines at least a portion of a first external surface of thearticle of footwear. The method can also include thermoforming orinjection molding the hydrogel-containing material to form the outsoleand integrally forming one or more traction elements with the outsole,or attaching one or more traction elements to the outsole, or both.

In another method, the article may be manufactured by forming asubstrate body having a first side, securing a hydrogel-containingmaterial to the first side, the hydrogel-containing material defining atleast a portion of a first external surface of the article, andembedding a portion of the hydrogel-containing material into thesubstrate body. The hydrogel-containing material can be manufactured tohave at least two sides or a cross-sectional area surrounded by thesubstrate body. The forming, securing, and embedding steps may beconducted simultaneously or sequentially.

In a fourth aspect, the present disclosure is directed to use of amaterial compositionally comprising a hydrogel to prevent or reduce soilaccumulation on a first external surface of a first article. The useinvolves use of the hydrogel-containing material to prevent or reducesoil accumulation on the first external surface, wherein the firstarticle retains at least 10% less soil by weight as compared to a secondarticle which is identical except that a first external surface of thesecond article is substantially free of the hydrogel-containing material(i.e. comprising a hydrogel). The use can be a use of a materialcompositionally comprising a hydrogel to prevent or reduce soilaccumulation on a first surface of outsole, which first surfacecomprises the material, by providing the material on at least a portionof the first surface of the outsole, wherein the outsole retains atleast 10% less soil by weight as compared to a second outsole which isidentical except that the first surface of the second outsole issubstantially free of the material comprising a hydrogel. The materialcan be a material as described above, e.g. with respect to the firstaspect of the disclosure.

In a fifth aspect, the present disclosure is directed to an article ofmanufacture having a substrate body and a hydrogel-containing material.The substrate body having a first side and a shaft extending from thefirst side. The substrate body can have a lip extending from the shaftsuch that the shaft and the lip form a junction having an angle beingequal to or less than about ninety degrees. The hydrogel-containingmaterial is secured to the shaft such that a portion of thehydrogel-containing material is disposed on the outer side surface inthe junction.

Additional aspects and description of the materials, outsoles, articles,uses and methods of the present disclosure can be found below.

As used herein, the term “outsole” is understood to refer to an outerportion of the sole of an article of footwear. This outer portion of anarticle having the outsole makes up at least a portion of the articlewhich can contact ground during conventional use. In addition to theoutsole, additional sole-type structures such as a midsole, a rigidplate, cushioning, etc., may or may not be present in the article offootwear. As used herein, the terms “article of footwear” and “footwear”are intended to be used interchangeably to refer to the same article.Typically, the term “article of footwear” will be used in a firstinstance, and the term “footwear” may be subsequently used to refer tothe same article for ease of readability.

As used herein, the term “hydrogel-containing material” is understood torefer to a material which compositionally comprises a polymerichydrogel. This type of material can be referred to by other likestatements, such as a “material comprising a hydrogel,” a “materialwhich includes a polymeric hydrogel,” and the like. When present in anoutsole of the present disclosure, the material defines at least aportion of a surface or side of the outsole. In other words, thehydrogel-containing material forms at least part of an outer or externalsurface or side of the article. The material can be present as one ormore layers disposed on the surface of the article, where the layer(s)can be provided as a single continuous segment on the surface or inmultiple discontinuous segments on the surface. The hydrogel-containingmaterial is not intended to be limited by any application process (e.g.,co-extrusion, injection molding, lamination, spray coating, etc.).

The term “ground-facing” refers to the position the element is intendedto be in when the element is present in an article during normal use. Ifthe article is footwear, the element is positioned toward the groundduring normal use by a wearer when in a standing position, and thus cancontact the ground including unpaved surfaces when the footwear is usedin a conventional manner, such as standing, walking or running on anunpaved surface. In other words, even though the element may notnecessarily be facing the ground during various steps of manufacturingor shipping, if the element is intended to face the ground during normaluse by a wearer, the element is understood to be ground-facing. In somecircumstances, due to the presence of elements such as tractionelements, the ground-facing surface can be positioned toward the groundduring conventional use but may not necessarily come into contact theground. For example, on hard ground or paved surfaces, the terminal endsof traction elements on the outsole may directly contact the ground,while portions of the outsole located between the traction elements donot. As described in this example, the portions of the outsole locatedbetween the traction elements are considered to be ground-facing eventhough they may not directly contact the ground in all circumstances.

As discussed below, it has been found these articles can prevent orreduce the accumulation of soil during wear on unpaved surfaces. As usedherein, the term “soil” can include any of a variety of substancescommonly present on a ground which might otherwise adhere to an article.Soil can include inorganic substances such as mud, sand, dirt, andgravel; organic matter such as grass, turf, leaves, other vegetation,and excrement; and combinations of inorganic and organic substances suchas clay. Additionally, soil can include other substances such aspulverized rubber which may be present on or in an unpaved surface.

While not wishing to be bound by theory, it is believed that thematerial comprising a hydrogel in accordance with the presentdisclosure, when sufficiently wet with water (including water containingdissolved, dispersed or otherwise suspended materials) can providecompressive compliance and/or expulsion of uptaken water. In particular,it is believed that the compressive compliance of the wet material, theexpulsion of liquid from the wet material, or both in combination, candisrupt the adhesion of soil on or at the article, or the cohesion ofthe particles to each other, or can disrupt both the adhesion andcohesion. This disruption in the adhesion and/or cohesion of soil isbelieved to be a responsible mechanism for preventing (or otherwisereducing) the soil from accumulating on the article (due to the presenceof the wet material).

This disruption in the adhesion and/or cohesion of soil is believed tobe a responsible mechanism for preventing (or otherwise reducing) thesoil from accumulating on the article (due to the presence of the wetmaterial). As can be appreciated with footwear, preventing soil fromaccumulating on the bottom of footwear can improve the performance oftraction elements present on the outsole during wear on unpavedsurfaces, can prevent the footwear from gaining weight due toaccumulated soil during wear, can preserve ball handling performance ofthe footwear, and thus can provide significant benefits to wearer ascompared to an article of footwear without the material present on theoutsole.

As used herein, the term “weight” refers to a mass value, such as havingthe units of grams, kilograms, and the like. Further, the recitations ofnumerical ranges by endpoints include the endpoints and all numberswithin that numerical range. For example, a concentration ranging from40% by weight to 60% by weight includes concentrations of 40% by weight,60% by weight, and all water uptake capacities between 40% by weight and60% by weight (e.g., 40.1%, 41%, 45%, 50%, 52.5%, 55%, 59%, etc. . . .).

As used herein, the term “providing”, when recited in the claims, is notintended to require any particular delivery or receipt of the provideditem. Rather, the term “providing” is merely used to recite items thatwill be referred to in subsequent elements of the claim(s), for purposesof clarity and ease of readability.

As used herein, the terms “about” and “substantially” are used hereinwith respect to measurable values and ranges due to expected variationsknown to those skilled in the art (e.g., limitations and variability inmeasurements).

As used herein, the terms “at least one” and “one or more of” an elementare used interchangeably, and have the same meaning that includes asingle element and a plurality of the elements, and may also berepresented by the suffix “(s)” at the end of the element. For example,“at least one polyurethane”, “one or more polyurethanes”, and“polyurethane(s)” may be used interchangeably and have the same meaning.

It will be understood that the article having the hydrogel-containingmaterial may be a variety of articles or components of articles,including footwear, a component of footwear, sporting equipment, acomponent of sporting equipment, apparel, a component of apparel, aplumbing article, a component of a plumbing article, a component of avehicle, a transportation container, a component of a transportationcontainer, a refuse container, a component of a refuse container, anarticle of construction equipment, a component of an article ofconstruction equipment, an article of play equipment, a component of anarticle of play equipment, an article of landscaping equipment, acomponent of an article of landscaping equipment, an article offurniture, and/or a component of an article of furniture.

If the article is footwear, the article of footwear may be designed fora variety of uses, such as sporting, athletic, military, work-related,recreational, or casual use. Primarily, the article of footwear isintended for outdoor use on unpaved surfaces (in part or in whole), suchas on a ground surface including one or more of grass, turf, gravel,sand, dirt, clay, mud, and the like, whether as an athletic performancesurface or as a general outdoor surface. However, the article offootwear may also be desirable for indoor applications, such as indoorsports including dirt playing surfaces for example (e.g., indoorbaseball fields with dirt infields). As used herein, the terms “at leastone” and “one or more of” an element are used interchangeably, and havethe same meaning that includes a single element and a plurality of theelements, and may also be represented by the suffix “(s)” at the end ofthe element. For example, “at least one polyurethane”, “one or morepolyurethanes”, and “polyurethane(s)” may be used interchangeably andhave the same meaning.

In preferred aspects, the article of footwear is designed use in outdoorsporting activities, such as global football/soccer, golf, Americanfootball, rugby, baseball, running, track and field, cycling (e.g., roadcycling and mountain biking), and the like. The article of footwear canoptionally include traction elements (e.g., lugs, cleats, studs, andspikes) to provide traction on soft and slippery surfaces. Cleats, studsand spikes are commonly included in footwear designed for use in sportssuch as global football/soccer, golf, American football, rugby,baseball, and the like, which are frequently played on unpaved surfaces.Lugs and/or exaggerated tread patterns are commonly included in footwearincluding boots design for use under rugged outdoor conditions, such astrail running, hiking, and military use.

FIGS. 1-4 illustrate an example article of footwear of the presentdisclosure, referred to as an article of footwear 100, and which isdepicted as footwear for use in global football/soccer applications. Asshown in FIG. 1, the footwear 100 includes an upper 110 and an outsole112 as footwear article components, where outsole 112 includes aplurality of traction elements 114 (e.g., cleats) and a materialcomprising a hydrogel 116 at its external or ground-facing side orsurface. While many of the embodied footwear of the present disclosurepreferably include traction elements such as cleats, it is to beunderstood that in other aspects, the incorporation of cleats isoptional.

The upper 110 of the footwear 100 has a body 118 which may be fabricatedfrom materials known in the art for making articles of footwear, and isconfigured to receive a user's foot. For example, the upper body 118 maybe made from or include one or more components made from one or more ofnatural leather; a knit, braided, woven, or non-woven textile made inwhole or in part of a natural fiber; a knit, braided, woven or non-woventextile made in whole or in part of a synthetic polymer, a film of asynthetic polymer, etc.; and combinations thereof. The upper 110 andcomponents of the upper 110 may be manufactured according toconventional techniques (e.g., molding, extrusion, thermoforming,stitching, knitting, etc.). While illustrated in FIG. 1 with a genericdesign, the upper 110 may alternatively have any desired aestheticdesign, functional design, brand designators, and the like.

The outsole 112 may be directly or otherwise secured to the upper 110using any suitable mechanism or method. As used herein, the terms“secured to”, such as for an outsole that is secured to an upper, e.g.,is operably secured to an upper, refers collectively to directconnections, indirect connections, integral formations, and combinationsthereof. For instance, for an outsole that is secured to an upper, theoutsole can be directly connected to the upper (e.g., with an adhesive),the outsole can be indirectly connected to the upper (e.g., with anintermediate midsole), can be integrally formed with the upper (e.g., asa unitary component), and combinations thereof.

For example, the upper 110 may be stitched to the outsole 112, or theupper 110 may be glued to the outsole 112, such as at or near a biteline 120 of the upper 110. The footwear 100 can further include amidsole (not shown) secured between the upper 110 and the outsole 112,or can be enclosed by the outsole 112. When a midsole is present, theupper 110 may be stitched, glued, or otherwise attached to the midsoleat any suitable location, such as at or below the bite line 120.

As further shown in FIGS. 1 and 2, the layout of outsole 112 can besegregated into a forefoot region 122, a midfoot region 124, and a heelregion 126. The forefoot region 122 is disposed proximate a wearer'sforefoot, the midfoot region 124 is disposed between the forefoot region122 and the heel region 126, and the heel region 126 is disposedproximate a wearer's heel and opposite the forefoot region 122. Theoutsole 112 may also include a forward edge 128 at the forefoot region122 and a rearward edge 130 at the heel region 126. In addition to theselongitudinal designations, the left/right sides of outsole 112 can alsobe respectively designated by a medial side 132 and a lateral side 134.

Each of these designations can also apply to the upper 110 and moregenerally to the footwear 100, and are not intended to particularlydefine structures or boundaries of the footwear 100, the upper 110, orthe outsole 112. As used herein, directional orientations for anarticle, such as “upward”, “downward”, “top”, “bottom”, “left”, “right”,and the like, are used for ease of discussion, and are not intended tolimit the use of the article to any particular orientation.Additionally, references to “ground-facing surface”, “ground-facingside”, and the like refer to the surface or side of footwear that facethe ground during normal use by a wearer as standing. These terms arealso used for ease of discussion, and are not intended to limit the useof the article to any particular orientation.

The outsole 112 can optionally include a backing plate or substrate body136, which, in the shown example, extends across the forefoot region122, the midfoot region 124, and the heel region 126. The backing plate136 is an example backing member or other outsole substrate for use inan article of footwear, and can provide structural integrity to theoutsole 112. However, the backing plate 136 can also be flexible enough,at least in particular locations, to conform to the flexion of awearer's foot during the dynamic motions produced during wear. Forexample, as shown in FIGS. 1 and 2, the backing plate 136 may include aflex region 138 at the forefoot region 122, which can facilitate flexionof the wearer's toes relative to the foot in active use of the footwear100.

The backing plate 136 may have a top (or first) surface (or side) 142(best shown in FIGS. 3 and 4), a bottom (or second) surface (or side)144, and a sidewall 146, where the sidewall 146 can extend around theperimeter of the backing plate 136 at the forward edge 128, the rearwardedge 130, the medial side 132, and the lateral side 134. The top surface142 is the region of the backing plate 136 (and the outsole 112 moregenerally) that may be in contact with and secured to the upper 110and/or to any present midsole or insole.

The bottom surface 144 is a surface of the backing plate 136 that iscovered (or at least partially covered) by the material 116 securedthereto, and would otherwise be configured to contact a ground surface,whether indoors or outdoors, if the hydrogel-containing material 116were otherwise omitted. The bottom surface 144 is also the portion ofoutsole 112 that the traction elements 114 can extend from, as discussedbelow.

The optional backing plate 136 can be manufactured with one or morelayers, may be produced from any suitable material(s), and can provide agood interfacial bond to the hydrogel-containing material 116, asdiscussed below. Examples of suitable materials for the backing plate136 include one or more polymeric materials such as thermoplasticelastomers; thermoset polymers; elastomeric polymers; silicone polymers;natural and synthetic rubbers; composite materials including polymersreinforced with carbon fiber and/or glass; natural leather; metals suchas aluminum, steel and the like; and combinations thereof. The backingplate or substrate body 136 can be a polymeric material having a wateruptake capacity of less than about 10% by weight, as characterized bythe Water Uptake Capacity Test with the Article Sampling Procedurediscussed herein.

In particular aspects, when a backing plate 136 is used, the backingplate 136 is manufactured from one or more polymeric materials havingsimilar chemistries to that of the hydrogel-containing material 116. Inother words, the backing plate and the hydrogel-containing material canboth comprise or consist essentially of polymers having the same orsimilar functional groups, and/or can comprise or consist essentially ofpolymers having the same or similar levels of polarity. For example, thebacking plate and the hydrogel-containing material can both comprise orconsist essentially of one or more polyurethanes (e.g., thermoplasticpolyurethanes), one or more polyamides (e.g., thermoplastic polyamides),one or more polyethers (e.g., thermoplastic polyethers), one or morepolyesters (e.g., thermoplastic polyesters), or the like. The similarchemistries can be beneficial for improving manufacturingcompatibilities between the hydrogel-containing material 116 and thebacking plate 136, and also for improving their interfacial bondstrength. Alternatively, one or more tie layers (not shown) can beapplied between the backing plate 136 and the material 116 in order toimprove their interlayer bonding.

As used herein, the term “polymer” refers to a molecule havingpolymerized units of one or more species of monomer. The term “polymer”is understood to include both homopolymers and copolymers. The term“copolymer” refers to a polymer having polymerized units of two or morespecies of monomers, and is understood to include terpolymers and otherpolymers formed from multiple different monomers. As used herein,reference to “a” polymer or other chemical compound refers one or moremolecules of the polymer or chemical compound, rather than being limitedto a single molecule of the polymer or chemical compound. Furthermore,the one or more molecules may or may not be identical, so long as theyfall under the category of the chemical compound. Thus, for example, “a”polylaurolactam is interpreted to include one or more polymer moleculesof the polylaurolactam, where the polymer molecules may or may not beidentical (e.g., different molecular weights and/or isomers).

The traction elements 114 may each include any suitable cleat, stud,spike, or similar element configured to enhance traction for a wearerduring cutting, turning, stopping, accelerating, and backward movement.The traction elements 114 can be arranged in any suitable pattern alongthe bottom surface 144 of the backing plate 136. For instance, thetraction elements 114 can be distributed in groups or clusters along theoutsole 112 (e.g., clusters of 2-8 traction elements 114). As best shownin FIGS. 1 and 2, the traction elements 114 can be grouped into acluster 147A at the forefoot region 122, a cluster 147B at the midfootregion 124, and a cluster 147C at the heel region 126. In this example,six of the traction elements 114 are substantially aligned along themedial side 132 of the outsole 112, and the other six traction elements114 are substantially aligned along the lateral side 134 of the outsole112.

The traction elements 114 may alternatively be arranged along theoutsole 112 symmetrically or non-symmetrically between the medial side132 and the lateral side 134, as desired. Moreover, one or more of thetraction elements 114 may be arranged along a centerline of outsole 112between the medial side 132 and the lateral side 134, such as a blade114A, as desired to enhance or otherwise modify performance.

Alternatively (or additionally), traction elements can also include oneor more front-edge traction elements 114, such as one or more blades114B, one or more fins 114C, and/or one or more cleats (not shown)secured to (e.g., integrally formed with) the backing plate 136 at afront-edge region between forefoot region 122 and cluster 147A. In thisapplication, the hydrogel-containing material 116 can optionally extendacross the bottom surface 144 at this front-edge region whilemaintaining good traction performance.

Furthermore, the traction elements 114 may each independently have anysuitable dimension (e.g., shape and size). For instance, in somedesigns, each traction element 114 within a given cluster (e.g.,clusters 147A, 147B, and 147C) may have the same or substantially thesame dimensions, and/or each traction element 114 across the entirety ofthe outsole 112 may have the same or substantially the same dimensions.Alternatively, the traction elements 114 within each cluster may havedifferent dimensions, and/or each traction element 114 across theentirety of the outsole 112 may have different dimensions.

Examples of suitable shapes for the traction elements 114 includerectangular, hexagonal, cylindrical, conical, circular, square,triangular, trapezoidal, diamond, ovoid, as well as other regular orirregular shapes (e.g., curved lines, C-shapes, etc. . . . ). Thetraction elements 114 may also have the same or different heights,widths, and/or thicknesses as each other, as further discussed below.Further examples of suitable dimensions for the traction elements 114and their arrangements along the backing plate 136 include thoseprovided in soccer/global football footwear commercially available underthe tradenames “TIEMPO”, “HYPERVENOM”, “MAGISTA”, and “MERCURIAL” fromNike, Inc. of Beaverton, Oreg.

The traction elements 114 may be incorporated into the outsole includingthe optional backing plate 136 by any suitable mechanism such that thetraction elements 114 preferably extend from the bottom surface 144. Forexample, as discussed below, the traction elements 114 may be integrallyformed with the backing plate 136 through a molding process (e.g., forfirm ground (FG) footwear). Alternatively, the outsole or optionalbacking plate 136 may be configured to receive removable tractionelements 114, such as screw-in or snap-in traction elements 114. Inthese aspects, the backing plate 136 may include receiving holes (e.g.,threaded or snap-fit holes, not shown), and the traction elements 114can be screwed or snapped into the receiving holes to secure thetraction elements 114 to the backing plate 136 (e.g., for soft ground(SG) footwear).

In further examples, a first portion of the traction elements 114 can beintegrally formed with the outsole or optional backing plate 136 and asecond portion of the traction elements 114 can be secured withscrew-in, snap-in, or other similar mechanisms (e.g., for SG profootwear). The traction elements 114 may also be configured as shortstuds for use with artificial ground (AG) footwear, if desired. In someapplications, the receiving holes may be raised or otherwise protrudefrom the general plane of the bottom surface 144 of the backing plate136. Alternatively, the receiving holes may be flush with the bottomsurface 144.

The traction elements 114 can be fabricated from any suitable materialfor use with the outsole 112. For example, the traction elements 114 mayinclude one or more of polymeric materials such as thermoplasticelastomers; thermoset polymers; elastomeric polymers; silicone polymers;natural and synthetic rubbers; composite materials including polymersreinforced with carbon fiber and/or glass; natural leather; metals suchas aluminum, steel and the like; and combinations thereof. In aspects inwhich the traction elements 114 are integrally formed with the backingplate 136 (e.g., molded together), the traction elements 114 preferablyinclude the same materials as the outsole or backing plate 136 (e.g.,thermoplastic materials). Alternatively, in aspects in which thetraction elements 114 are separate and insertable into receiving holesof the backing plate 136, the traction elements 114 can include anysuitable materials that can secured in the receiving holes of thebacking plate 112 (e.g., metals and thermoplastic materials).

The optional backing plate 136 (and more generally, the outsole 112) mayalso include other features other than the traction elements 114 thatcan provide support or flexibility to the outsole and/or for aestheticdesign purposes. For instance, the outsole or backing plate 136 may alsoinclude ridges 148 that may be raised or otherwise protrude from thegeneral plane of the bottom surface 144.

As shown, ridges 148 can extend along the arrangement pathways of thetraction elements 114, if desired. These features (e.g., ridges 148) canbe integrally formed into the outsole or backing plate 136, oralternatively, be removable features that are securable to the backingplate 136. Suitable materials for these features include those discussedabove for the traction elements 114.

The backing plate 136 (and more generally, the outsole 112) may alsoinclude other features such as exaggerated tread patterns, lugs, and thelike, which are configured to contact the ground or playing surface toincrease traction, to enhance performance, or for aesthetic designpurposes. These other features can be present on the outsole in place ofor in addition to the traction elements 114, and can be formed from thesuitable materials discussed above for the traction elements 114.

As further shown in FIGS. 3 and 4, the traction elements 114 can bearranged such that when footwear 100 rests on a flat surface 149, thebottom surface 144 of backing plate 136 and the hydrogel-containingmaterial 116 (forming the layered structure) are offset from the flatsurface 149. This offset is present even when the material 116 is fullysaturated and swollen, as discussed below. As such, the tractionelements 114 can receive the greatest levels of shear and abrasivecontact with surfaces during use, such as by digging into soil duringcutting, turning, stopping, accelerating, backward movements, and thelike. In comparison, the hydrogel-containing material 116 at its offsetlocation can remain partially protected from a significant portion ofthese shear and abrasive conditions, thereby preserving its integrityduring use.

FIG. 5 is an expanded sectional view of the hydrogel-containing material116 and the bottom surface 144 of the backing plate 136 at one of thetraction elements 114. In this shown example, the traction element 114,which can be representative of one or more of the other tractionelements 114, is integrally molded with the backing plate 136 andincludes a shaft 150 that protrudes downward beyond the bottom surface144 and the hydrogel-containing material 116. The shaft 150 itself mayinclude an outer side surface 152 and a terminal edge 154. The terminaledge 154 of the shaft 150 is the distal end of the traction element 114,opposite from the bottom surface 144, and is the portion of the tractionelement 114 that can initially contact and penetrate into a playing orground surface.

As mentioned above, the traction element 114 may have any suitabledimensions and shape, where the shaft 150 (and the outer side surface152) can correspondingly have rectangular, hexagonal, cylindrical,conical, circular, square, triangular, trapezoidal, diamond, ovoid, aswell as other regular or irregular shapes (e.g., curved lines, C-shapes,etc. . . . ). Similarly, the terminal edge 154 can have dimensions andsizes that correspond to those of the outer side surface 152, and can besubstantially flat, sloped, rounded, and the like. Furthermore, in someaspects, the terminal edge 154 can be substantially parallel to thebottom surface 144 and/or the hydrogel-containing material 116.

Examples of suitable average lengths 156 for each shaft 150 relative tobottom surface 144 range from 1 millimeter to 20 millimeters, from 3millimeters to 15 millimeters, or from 5 millimeters to 10 millimeters,where, as mentioned above, each traction element 114 can have differentdimensions and sizes (i.e., the shafts 150 of the various tractionelements 114 can have different lengths).

In the example shown in FIGS. 1-5, the hydrogel-containing material 116is present on the entire bottom surface 144 of the backing plate 136between (and not including) the traction elements 114. For instance, asshown in FIG. 5, the hydrogel-containing material 116 can cover thebottom surface 144 at locations around the shaft 150 of each tractionelement 114, such that hydrogel-containing material does not cover theouter side surface 152 or the terminal edge 154 of the traction element114, other than optionally at a base region 158 of the shaft 150. Thiscan preserve the integrity of the hydrogel-containing material 116 andpreserve traction performance of the traction elements 114. In someaspects, the hydrogel-containing material 116 does not cover or contactany portion of the outer side surface 152 of the shaft 150. In otherexamples, the base region 158 that the hydrogel-containing material 116(in a dry state) covers and contacts the outer side surface 152 is lessthan 25%, less than 15%, or less than 10% of the length of the shaft150, as an average distance measured from the bottom surface 144 at thetraction element 114.

As can be seen in FIG. 5, the hydrogel-containing material 116 can be athin film to minimize or otherwise reduce its impact on the tractionelements 114. Examples of suitable average thicknesses for thehydrogel-containing material 116 in a dry state (referred to as adry-state material thickness 160) range from 0.025 millimeters to 5millimeters, from 0.5 millimeters to 3 millimeters, from 0.25millimeters to 1 millimeter, from 0.25 millimeters to 2 millimeters,from 0.25 millimeters to 5 millimeters, from 0.15 millimeters to 1millimeter, from 0.15 millimeters to 1.5 millimeters, from 0.1millimeters to 1.5 millimeters, from 0.1 millimeters to 2 millimeters,from 0.1 millimeters to 5 millimeters, from 0.1 millimeters to 1millimeter, or from 0.1 millimeters to 0.5 millimeters. As depicted, thethicknesses for the hydrogel-containing material 116 are measuredbetween the interfacial bond at the bottom surface 144 of the backingplate 136 and an exterior surface of the hydrogel-containing material116 (referred to as a material surface 162). In some aspects, thehydrogel-containing material 116 can also (or alternatively) be presenton one or more regions of the traction elements 114. For example, thematerial can be present at an exterior surface of the traction elements114. These aspects can be beneficial, for example, in applications wherethe traction element 114 has a central base with multiple shafts 150that protrude from the periphery of the central base. In such aspects,the hydrogel-containing material 116 can be present on at least thecentral base of the traction element 114. Furthermore, for someapplications, the hydrogel-containing material 116 may also cover theentirety of one or more of the traction elements 114 (e.g., on the shaft150).

Presence of the hydrogel-containing material 116 on the ground-facingside of outsole 112 (i.e., on bottom surface 144) allows thehydrogel-containing material 116 to come into contact with soil,including wet soil during use, which is believed to enhance thesoil-shedding performance for the footwear 100, as explained below.However, the hydrogel-containing material 116 can also optionally bepresent on one or more locations of the sidewall 146 of the backingplate 136.

As briefly mentioned above, the hydrogel-containing material 116compositionally includes a hydrogel. The presence of the hydrogel in thematerial can allow the hydrogel-containing material 116 to absorb orotherwise take up water. For example, the material can take up waterfrom an external environment (e.g., from mud, wet grass, presoaking, andthe like).

As used herein, the term “compliant” refers to the stiffness of anelastic material, and can be determined by the storage modulus of thematerial. Generally, when the hydrogel of the material is a crosslinkedhydrogel (e.g., includes physical crosslinks, covalent crosslinks, orboth), the lower the degree of crosslinking in the hydrogel, or thegreater the distance between crosslinks in the hydrogel, the morecompliant the material will be. In particular aspects, when the materialcomprises a crosslinked polymeric hydrogel, it is believed that thisuptake of water by the hydrogel-containing material 116 can cause thecrosslinked polymeric hydrogel to expand and stretch under the pressureof the received water, while retaining its overall structural integritythrough its crosslinking. This stretching and expansion of the hydrogelcan cause the hydrogel-containing material 116 to swell and become morecompliant (e.g., compressible, expandable, and stretchable).

In aspects where the material swells, the swelling of thehydrogel-containing material 116 can be observed as an increase inmaterial thickness from the dry-state thickness 160 of thehydrogel-containing material 116 (shown in FIG. 5), through a range ofintermediate-state thicknesses (e.g., thickness 163, shown in FIG. 5A)as additional water is absorbed, and finally to a saturated-statethickness 164 (shown in FIG. 5B), which is an average thickness of thehydrogel-containing material 116 when fully saturated with water. Forexample, the saturated-state thickness 164 for the fully saturatedmaterial 116 can be greater than 150%, greater than 200%, greater than250%, greater than 300%, greater than 350%, greater than 400%, orgreater than 500%, of the dry-state thickness 160 for the samehydrogel-containing material 116.

In some aspects, the saturated-state thickness 164 for the fullysaturated material 114 range from 150% to 500%, from 150% to 400%, from150% to 300%, or from 200% to 300% of the dry-state thickness 160 forthe same hydrogel-containing material 116. Examples of suitable averagethicknesses for the hydrogel-containing material 116 in a wet state(referred to as a saturated-state thickness 164) range from 0.2millimeters to 10 millimeters, from 0.2 millimeters to 5 millimeters,from 0.2 millimeters to 2 millimeters, from 0.25 millimeters to 2millimeters, or from 0.5 millimeters to 1 millimeter.

In particular aspects, the hydrogel-containing material 116 can quicklytake up water that is in contact with the hydrogel-containing material116. For instance, the hydrogel-containing material 116 can take upwater from mud and wet grass, such as during a warmup period prior to acompetitive match. Alternatively (or additionally), thehydrogel-containing material 116 can be pre-conditioned with water sothat the hydrogel-containing material 116 is partially or fullysaturated, such as by spraying or soaking the outsole 112 with waterprior to use.

The total amount of water that the hydrogel-containing material 116 cantake up depends on a variety of factors, such as its composition (e.g.,its hydrophilicity), its cross-linking density, its thickness, and itsinterfacial bond to the backing plate 136 when a backing plate ispresent. For example, it is believed that a material comprising ahydrogel having a higher level of hydrophilicity and a lower level ofcross-linking density can increase the water uptake capacity of thehydrogel-containing material 116. On the other hand, the interfacialbond between the hydrogel-containing material 116 and the bottom surface144 of the backing plate 136 (when a backing plate 136 is used) canpotentially restrict the swelling of the hydrogel-containing material116 due to its relatively thin dimensions. Accordingly, as describedbelow, the water uptake capacity and the swelling capacity of thehydrogel-containing material 116 can differ between thehydrogel-containing material 116 in a neat film state (isolated film byitself) and the hydrogel-containing material 116 as present on a backingplate 136.

The water uptake capacity and the water uptake rate of thehydrogel-containing material 116 are dependent on the size and shape ofits geometry, and are typically based on the same factors. However, ithas been found that, to account for part dimensions when measuring wateruptake capacity, it is possible to derive an intrinsic, steady-statematerial property. Therefore, conservation of mass can be used to definethe ratio of water weight absorbed to the initial dry weight of thehydrogel-containing material 116 at very long time scales (i.e. when theratio is no longer changing at a measurable rate).

Conversely, the water uptake rate is transient and can be definedkinetically. The three primary factors for water uptake rate for ahydrogel-containing material 116 present at a surface of an outsolegiven part geometry include time, thickness, and the exposed surfacearea available for taking up water. Once again, the weight of watertaken up can be used as a metric of water uptake rate, but the waterflux can also be accounted for by normalizing by the exposed surfacearea. For example, a thin rectangular film can be defined by 2×L×W,where L is the length of one side and W is the width. The value isdoubled to account for the two major surfaces of the film, but theprefactor can be eliminated when the film has a non-absorbing,structural layer secured to one of the major surfaces (e.g., with anoutsole backing plate).

Normalizing for thickness and time can require a more detailed analysisbecause they are coupled variables. Water penetrates deeper into thefilm as more time passes in the experiment, and therefore, there is morefunctional (e.g., absorbent) material available at longer time scales.One dimensional diffusion models can explain the relationship betweentime and thickness through material properties, such as diffusivity. Inparticular, the weight of water taken up per exposed surface area shouldyield a straight line when plotted against the square root of time.

However, several factors can occur where this model does not representthe data well. First, at long times absorbent materials become saturatedand diffusion kinetics change due to the decrease in concentrationgradient of the water. Second, as time progresses the material can beplasticized to increase the rate of diffusion, so once again the modeldo longer represents the physical process. Finally, competing processescan dominate the water uptake or weight change phenomenon, typicallythrough surface phenomenon such as physisorption on a rough surface dueto capillary forces. This is not a diffusion driven process, and thewater is not actually be taken up into the hydrogel-containing materialor film.

Even though the hydrogel-containing material 116 can swell as it takesup water and transitions between the different material states withcorresponding thicknesses 160, 163, and 164, the saturated-statethickness 164 of the hydrogel-containing material 116 can remains lessthan the length 156 of the traction element 114. This selection of thehydrogel-containing material 116 and its corresponding dry and saturatedthicknesses ensures that the traction elements 114 can continue toprovide ground-engaging traction during use of the footwear 100, evenwhen the hydrogel-containing material 116 is in a fully swollen state.For example, the average clearance difference between the lengths 156 ofthe traction elements 114 and the saturated-state thickness 164 of thehydrogel-containing material 116 is desirably at least 8 millimeters.For example, the average clearance distance can be at least 9millimeters, 10 millimeters, or more. Of course, the hydrogel-containingmaterial 116 can also cover the entire length of the traction element114 in either its dry-state or saturated-state thicknesses.

As also mentioned above, in addition to swelling, the compliance of thehydrogel-containing material 116 may also increase from being relativelystiff (i.e., dry-state) to being increasingly stretchable, compressible,and malleable (i.e., wet-state). The increased compliance accordinglycan allow the hydrogel-containing material 116 to readily compress underan applied pressure (e.g., during a foot strike on the ground), and insome aspects, to quickly expel at least a portion of its retained water(depending on the extent of compression). While not wishing to be boundby theory, it is believed that this compressive compliance alone, waterexpulsion alone, or both in combination can disrupt the adhesion and/orcohesion of soil at outsole 112, which prevents or otherwise reduces theaccumulation of soil on outsole 112.

In addition to quickly expelling water, in particular examples, thecompressed hydrogel-containing material 116 is capable of quicklyre-absorbing water when the compression is released (e.g., liftoff froma foot strike during normal use). As such, during use in a wet or dampenvironment (e.g., a muddy or wet ground), the hydrogel-containingmaterial 116 can dynamically expel and repeatedly take up water oversuccessive foot strikes, particularly from a wet surface. As such, thehydrogel-containing material 116 can continue to prevent soilaccumulation over extended periods of time (e.g., during an entirecompetitive match), particularly when there is ground water availablefor re-uptake.

FIGS. 6-9 illustrate an example method of using footwear 100 with amuddy or wet ground 166, which depict one potential mechanism by whichthe materials comprising hydrogels as disclosed herein can prevent orreduce soil accumulation on the outsole 112. It is known that the soilof the ground 166 can accumulate on an outsole (e.g., between thetraction elements) during normal athletic or casual use, in particularwhen the ground 166 is wet. The soil is believed to accumulate on theoutsole due to a combination of adhesion of the soil particles to thesurface of the outsole and cohesion of the soil particles to each other.In order to break these adhesive/cohesive forces, the soil particlesneed to be subjected to stresses high enough to exceed theiradhesive/cohesive activation energies. When this is achieved, the soilparticles can then move or flow under the applied stresses, whichdislodge or otherwise shed portions of the soil from the outsole.

However, during typical use of cleated footwear, such as duringcompetitive sporting events (e.g., global football/soccer matches,golfing events, and American football games), the actions of walking andrunning are not always sufficient to dislodge the soil from the outsole.This can result in the soil sticking to the outsoles, particularly inthe interstitial regions where compaction forces in the normal directionare maximized between the individual traction elements. As can beappreciated, this soil can quickly accumulate to increase the weight ofthe footwear and reduce the effectiveness of the traction elements(e.g., because they have less axial or normal extent capable of engagingwith the ground 166), each of which can have a significant impact onathletic performance.

The incorporation of the hydrogel-containing material 116 to a surfaceor side of the outsole 112 (e.g., a ground-facing surface or side of theoutsole) however, is believed to disrupt the adhesion and/or cohesion ofsoil at the outsole 112, thereby reducing the adhesive/cohesiveactivation energies otherwise required to induce the flow of the soilparticles. As shown in FIG. 6, the footwear 100 can be provided in apre-conditioned (e.g., pre-wet) state where the hydrogel-containingmaterial 116 is partially or fully saturated with water. This can beaccomplished in a variety of manners, such as spraying the outsole 112with water, soaking the outsole 112 in water, or otherwise exposing thehydrogel-containing material 116 to water in a sufficient amount for asufficient duration. Alternatively (or additionally), when water or wetmaterials are present on the ground 166, footwear 100 can be used in aconventional manner on the ground 166 until the hydrogel-containingmaterial 116 absorbs a sufficient amount of water from the ground 166 orwet materials to reach its pre-conditioned state.

During a foot strike, the downward motion of the footwear 100(illustrated by arrow 168) causes the traction element 114 to contactthe ground 166. As shown in FIG. 7, the continued applied pressure ofthe foot strike can cause the traction element 114 to penetrate into thesofter soil of the ground 166 until the material surface 162 of thehydrogel-containing material 116 contacts the ground 166. As shown inFIG. 8, further applied pressure of the foot strike can press thehydrogel-containing material 116 into the ground 166, thereby at leastpartially compressing the hydrogel-containing material 116 under theapplied pressure (illustrated by arrows 170).

As can be seen, this compression of the hydrogel-containing material 116into the soil of the ground 166 typically compacts the soil, increasingthe potential for the soil particles to adhere to outsole 112 and tocohesively adhere to each other (clumping together). However, thecompression of the hydrogel-containing material 116 may also expel atleast a portion of its uptaken water into the soil of the ground 166(illustrated by arrows 172). It is believed that as the water isexpelled through the material surface 162 of the hydrogel-containingmaterial 116, the pressure of the expelled water can disrupt theadhesion of the soil to the material surface 162 at this interface.

Additionally, once expelled into the soil, it is also believed that thewater may also modify the rheology of the soil adjacent to the materialsurface 162 (e.g., watering down the soil to a relatively muddier orwetter state). This is believed to essentially spread out the soilparticles in the water carrier and weaken their cohesive forces (e.g.,mechanical/ionic/hydrogen bonds). Each of these mechanisms from theexpelled water is believed to lower the required stresses need todisrupt the adhesion of the soil from the outsole 112. As such, thestresses typically applied during athletic performances (e.g., whilerunning, handling the ball with the footwear, and kicking the ball) canexceed the cohesive/adhesive activation energies more frequently.

As shown in FIG. 9, when the footwear 100 is lifted following the footstrike (illustrated by arrow 174), it is believed that the compressionapplied to the hydrogel-containing material 116 is released, and so thehydrogel-containing material 116 can be free to expand. In someexamples, it has been found that, when the outsole 112 is lifted apartfrom the ground 166, a thin water layer can remain in contact with thematerial surface 162, which can quickly re-uptake into thehydrogel-containing material 116. This quick re-uptake of water from thematerial surface 162 after compression is removed (e.g., within about 1,2, or 5 seconds) can quickly swell the hydrogel-containing material 116back at least partially to its previously-swelled state (depending onthe amount of water re-absorbed), as illustrated by arrows 176.

This cyclic compression and expansion from repeated, rapid, and/orforceful foot strikes during use of the footwear 100 can alsomechanically disrupt the adhesion of any soil still adhered to thematerial surface 162, despite the relatively small thickness of thehydrogel-containing material 116 in any of its various states of watersaturation (e.g., partially to fully saturated). In particular, theincreased compliance is believed, under some conditions, to lead toinhomogeneous shear states in the soil when compressed in the normal orvertical direction, which can also lead to increased interfacial shearstresses and a decrease in soil accumulation.

In some aspects, the hydrogel-containing material 116 can swell duringwater re-uptake (and also during initial uptake) in a non-uniformmanner. In such aspects, the uptaken water may tend to travel in a pathperpendicular to the material surface 162, and so may not migratesubstantially in a transverse direction generally in the plane of thehydrogel-containing material 116 once absorbed. This uneven,perpendicular water uptake and relative lack of transverse waterintra-material transport can form an irregular or rough texture or smallridges on the material surface 162. The presence of these small ridgeson the irregular material surface 162 from the non-uniform swelling arealso believed to potentially further disrupt the adhesion of the soil atthe material surface 162, and thus may loosen the soil and furtherpromote soil shedding. The uneven, ridged material surface 162 can alsobe seen in the photograph of FIG. 19 of an exemplary water-saturatedhydrogel-containing material 116 according to the present disclosure.

In addition to the uptake, compression, expulsion, re-uptake, andswelling cycle discussed above, the increased compliance of thehydrogel-containing material 116, for example elongational compliance inthe longitudinal direction, may allow the hydrogel-containing material116 to be more malleable and stretchable when swelled. For example, asillustrated in FIG. 10, during a foot rotation in a foot strike (e.g.,as the foot generally rolls from heel to toe during a stride), theoutsole 112 and the hydrogel-containing material 116 are correspondinglyflexed (e.g., inducing compression forces illustrated by arrows 170).One of skill will appreciate that a tie layer could be added between thehydrogel-containing material and a backing layer or substrate body.

The increased elongation or stretchiness of the hydrogel-containingmaterial 116 when partially or fully saturated with water can increasethe extent that the hydrogel-containing material 116 stretches duringthis flexing, which can induce additional shear on any soil adhered tothe material surface 162. As illustrated, a rolling ground strikecreates a curved outsole 112 and a curved compressed hydrogel-containingmaterial 116, which can cause water to be expelled therefrom andtransverse material stretching forces being induced to pull apart andshed the soil. The compression forces (illustrated by arrows 170) on thehydrogel-containing material 116, which can help to expel the water canbe particularly strong at points of contact with the ground 166 and/orwhere the radius of curvature of the curved outsole 112/curvedhydrogel-containing material 116 is relatively small or at its minimum.

The foregoing properties of the hydrogel-containing material 116 relatedto compression/expansion compliance and the elongation compliance arebelieved to be closely interrelated, and they can depend on the samehydrogel-containing material 116 properties (e.g., a hydrophilicmaterial able to able to rapidly take up and expel relatively largeamounts of water compared to the material size or thickness). Adistinction is in their mechanisms for preventing soil accumulation, forexample surface adhesion disruption versus shear inducement. The waterre-uptake is believed to potentially act to quickly expand or swell thehydrogel-containing material 116 after being compressed to expel water.Rapid water uptake can provide a mechanism for replenishing thehydrogel-containing material 116 water content between foot strikes.Rapid replenishment of the hydrogel-containing material 116 watercontent can restore the hydrogel-containing material 116 to itscompliant state, returning it to a state where stretching and shearingforces can contribute to debris shedding. In addition, replenishment ofthe hydrogel-containing material 116 water content can permit subsequentwater expulsion to provide an additional mechanism for preventing soilaccumulation (e.g., application of water pressure and modification ofsoil rheology). As such, the water absorption/expulsion cycle canprovide a unique combination for preventing soil accumulation on theoutsole 112 of the footwear 100.

In addition to being effective at preventing soil accumulation, thehydrogel-containing material 116 has also been found to be sufficientlydurable for its intended use on the ground-contacting side of theoutsole 112. Durability is based in part on the nature and strength ofthe interfacial bond of the hydrogel-containing material 116 to thebottom surface 144 of the backing plate 136, as well as the physicalproperties of the hydrogel-containing material 116 itself. For manyexamples, during the useful life of the hydrogel-containing material116, the hydrogel-containing material 116 may not delaminate from thebacking plate 136, and it can be substantially abrasion- andwear-resistant (e.g., maintaining its structural integrity withoutrupturing or tearing).

In various aspects, the useful life of the hydrogel-containing material116 (and the outsole 112 and footwear 100 containing it) is at least 10hours, 20 hours, 50 hours, 100 hours, 120 hours, or 150 hours of wear.For example, in some applications, the useful life of thehydrogel-containing material 116 ranges from 20 hours to 120 hours. Inother applications, the useful life of the hydrogel-containing material116 ranges from 50 hours to 100 hours of wear.

Interestingly, for many examples, the dry and wet states of thehydrogel-containing material 116 can allow the hydrogel-containingmaterial 116 to dynamically adapt in durability to account for dry andwet surface play. For example, when used on a dry ground 166, thehydrogel-containing material 116 can also be dry, which renders itstiffer and more wear resistant. Alternatively, when used on wet ground166 or when wet material is present on a dry ground 166, thehydrogel-containing material 116 can quickly take up water to achieve apartially or fully saturated condition, which may be a swollen and/orcompliant state. However, the wet ground 166 imposes less wear on theswollen and compliant hydrogel-containing material 116 compared to dryground 166. As such, the hydrogel-containing material 116 can be used ina variety of conditions, as desired. Nonetheless, the footwear 100 andthe outsole 112 are particularly beneficial for use in wet environments,such as with muddy surfaces, grass surfaces, and the like.

FIGS. 10A-F are partial, side views of a substrate body 13 and thehydrogel-containing material 116 that depict various examples ofsubstrate bodies having embedded portions of the hydrogel-containingmaterials. “Embedding” refers to having portions of at least two sidesor a portion of a cross-sectional area of the hydrogel-containingmaterial surrounded by the substrate body. Embedding a portion of thehydrogel-containing material in the substrate body has been found to beeffective in reducing or preventing delamination between the two.

A portion of the hydrogel-containing material can be embedded into thesubstrate body by molding the substrate body around the portion. Suchmolding techniques include injection molding or cast molding thesubstrate body onto or in the presence of the hydrogel-containingmaterial. For example, a molten thermoplastic polymeric material whichwill form the substrate body can be deposited below, above, or bothbelow and above the portion of the hydrogel-containing material.Following cooling and solidification of the molten thermoplasticpolymeric material, the portion of the hydrogel-containing material isembedded by the solidified polymeric material of the substrate body.

In another example, the portion of hydrogel-containing material can beembedded into the substrate body by, first, forming the substrate bodywith a ridge or channel therein, and securing the hydrogel-containingmaterial against the ridge or within the channel, thereby surrounding ortrapping the portion of the material with the substrate body on at leasttwo sides.

For example, as illustrated in FIG. 10A, the substrate body 13 can havea first side 10 and a second side 12. A hydrogel-containing material 116can be secured to the first side 10 such that a portion 14 of thehydrogel-containing material is embedded into the substrate body 13. Theembedded portion 14 can have a cross-sectional area 16 surrounded by thesubstrate body 13. In this aspect, the substrate body 13 can reduceand/or prevent delamination of the hydrogel-containing material 116 fromat least a portion of the substrate body adjacent to the portion of thehydrogel-containing material to the embedded portion. In some cases, theembedded portion 14 of the hydrogel-containing material 116 can be anedge 18 of the hydrogel-containing material 116. Reducing or preventingdelamination at edge regions can be effective to reduce or delaminationof the hydrogel-containing material from the entire the substrate body13.

In FIG. 10B, the substrate body 13 had a shaft 20 extending from thefirst side 10. In some cases, as illustrated in FIG. 10B, the shaft 20may be part of one or more traction elements, being part of thesubstrate body 13. The hydrogel-containing material 116 extends alongthe first side 10 and along an outer side surface of the shaft 20. Theembedded portion 14 is embedded or terminates in the shaft 20 of the oneor more traction elements.

FIG. 10C demonstrates that the embedded portion 14 may not necessarilybe an edge (as shown in FIGS. 10A-B). Instead the embedded portion 14may be a continuous portion or sheet of hydrogel-containing material116, being disposed or embedded within the shaft 20.

FIG. 10D depicts another aspect. In this aspect, the shaft 20 comprisesa lip 22. Lip 22 forms an outermost surface 24 of the shaft 20 (e.g. aspart of a traction element). The hydrogel-containing material 116 canextend along an outer side surface and embed into the shaft 20. The lip22 extends from the shaft.

In FIG. 10E, the substrate body 13 has a shaft 20 extending from thefirst side 10, and a lip 22 extending from the shaft 20 such that theshaft 20 and the lip 22 meet at a junction 29 in the outer side surface26, the junction 29 having an angle 28. The angle 28 can be equal to orless than about 90°. The hydrogel-containing material 116 can be securedto the shaft 20 such that a portion 30 of the hydrogel-containingmaterial is disposed on the outer side surface 26 in the junctionforming angle 28. By being disposed in the junction, an edge of thehydrogel-containing material 116 is embedded in the substrate body andprotected by the angle formed by the lip 22 and the shaft 20. Thisgeometry can prevent or assist in preventing delamination of thehydrogel-containing material and the substrate body.

While not wishing to be bound by any theory, when the angle is equal toor less than about 90°, this angle provides sufficient embedding andprotection for the hydrogel-containing material 116 so that it does notdelaminate from the substrate body and the shaft. In some cases, theshaft 20 may be integrally formed with the first side 10.

In FIG. 10F, the hydrogel-containing material 116 can vary in thickness,depending upon how much water has been taken up by the material. Forexample, the hydrogel-containing material 116 can have a swell thicknesssuch that when swollen, the hydrogel-containing material 116 forms theangle with the lip 22. This geometry is represented by dotted line 1(DL1). Alternatively, the hydrogel-containing material 116 can have agreater swell thickness (DL2) such that when swollen, thehydrogel-containing material 116 fills in the junction forming theangle. This geometry is represented by dotted line 2 (DL2).

In other words, the lip 22 can have a first end 32 and extend to asecond end 34 such that the increase in thickness of thehydrogel-containing material is such that the swollenhydrogel-containing material contacts both the first end and the secondend. Both the lip 22 and the shaft 20 can form part of one or moretraction elements. FIGS. 10A-F depict a partial view of a substrate bodyand a hydrogel containing material that may form a part of a largerarticle, being any of the articles discussed herein.

While the hydrogel-containing material 116 is illustrated above in FIGS.1-4 as extending across the entire bottom surface 144 of the outsole 112of the footwear 100, in alternative aspects, the hydrogel-containingmaterial 116 can alternatively be present as one or more segments thatare present at separate, discrete locations on the bottom surface 144 ofthe outsole 112. For instance, as shown in FIG. 11, thehydrogel-containing material 116 can alternatively be present as a firstsegment 116A secured to the bottom surface 144 at the forefoot region122, such as in the interstitial region between the traction elements114 of cluster 147A; a second segment 116B secured to the bottom surface144 at the midfoot region 124, such as in the interstitial regionbetween the traction elements 114 of cluster 147B; and/or a thirdsegment 116C secured to the bottom surface 144 at the heel region 126,such as in the interstitial region between the traction elements 114 ofcluster 147C. In each of these examples, the remaining regions of thebottom surface 144 can be free of the hydrogel-containing material 116.

In some arrangements, the hydrogel-containing material 116 is present asone or more segments secured to the bottom surface 144 at a region 178between the clusters 147A and 147B, at a region 180 between the clusters147B and 147C, or both. For example, the hydrogel-containing material116 may include a first segment present on the bottom surface 144 thatencompasses the locations of segment 116A, the region 178, and segment116B as well at the location of region 178; and a second segmentcorresponding to the segment 116B (at the cluster 147C). As also shownin FIG. 11, the segments of the hydrogel-containing material 116 (e.g.,segments 116A, 116B, and 116C) can optionally have surface dimensionsthat conform to the overall geometry of the backing plate 136, such asto conform to the contours of the ridges 148, the traction elements 114,and the like.

In another arrangement, the bottom surface 144 includes a front edgeregion 182 between the front edge 128 and the cluster 147A (andoptionally include a front portion of the cluster 147A) that is free ofthe hydrogel-containing material 116. As some of the examples of thehydrogel-containing material 116 may be slippery when partially or fullysaturated, having the hydrogel-containing material 116 present in thefront edge region 182 of the bottom surface 144 can potentially impacttraction and ball handling during sports. Furthermore, soil accumulationis typically most prominent in the interstitial regions of the clusters147A, 147B, and 147C, in comparison to the front edge 128.

Furthermore, the optional backing plate 136 can also include one or morerecessed pockets, such as a pocket 188 shown in FIG. 12, in which thehydrogel-containing material 116 or a sub-segment of thehydrogel-containing material 116 can reside. This can potentiallyincrease the durability of the hydrogel-containing material 116 byprotecting it from lateral delamination stresses. For instance, thebacking plate 136 can include a pocket 188 in the interstitial region ofcluster 147C, where the sub-segment 116C of the hydrogel-containingmaterial 116 can be secured to the bottom surface 144 within the pocket188. In this case, the dry-state thickness 160 of thehydrogel-containing material 116 can vary relative to a depth 190 of thepocket 188.

In some aspects, the depth 190 of the pocket 188 can range from 80% to120%, from 90% to 110%, or from 95% to 105% of the dry-state thickness160 of the hydrogel-containing material 116. Moreover, in aspects inwhich the backing plate 136 includes multiple pockets 188, each pocket188 may have the same depth 190 or the depths 190 may independently varyas desired. As can be appreciated, the increased bonding of thehydrogel-containing material 116 due to the recessed pocket 188 canpotentially reduce the swelling of the hydrogel-containing material 116when partially or fully saturated. However, a significant portion of thehydrogel-containing material 116 can be offset enough from the walls ofthe pocket 188 such that these interfacial bonds (relative to thedry-state thickness 160) will minimally affect the swelling andwater-absorbing performance of the hydrogel-containing material 116.

FIG. 13 illustrates an alternative design for the engagement between thehydrogel-containing material 116 and the bottom surface 144. In thiscase, the backing plate 136 can include one or more recessedindentations 192 having any suitable pattern(s), and in which portionsof the hydrogel-containing material 116 extend into the indentations 192to increase the interfacial bond surface area between thehydrogel-containing material 116 and the bottom surface 144 of thebacking plate 136. For example, the indentations 192 can be present asone or more geometrically-shaped holes (e.g., circular, rectangular, orother geometric shapes) or irregularly-shaped holes in the backing plate136, one or more trenches or channels extending partially or fully alongthe backing plate 136 (in the lateral, longitudinal, or diagonaldirections), and the like.

In these aspects, the hydrogel-containing material 116 can have two (ormore) thicknesses depending on whether a given portion of thehydrogel-containing material 116 extends into one of the indentations.For ease of discussion and readability, the dry-state thickness 160 ofthe hydrogel-containing material 116, as used herein, refers to aportion of the hydrogel-containing material 116 (in a dry state) thatdoes not extend into one of the indentations, such as at locations 194.As such, the dry-state thickness 160 shown in FIG. 13 is the same as thedry-state thickness 160 shown above in FIG. 5.

Each indentation 192 may independently have a depth 196, which can rangefrom 1% to 200%, from 25% to 150%, or from 50% to 100% of the dry-statethickness 160 of the hydrogel-containing material 116. In theselocations, the dry-state thickness of the hydrogel-containing material116 is the sum of the dry-state thickness 160 and the depth 196. Aninteresting result of this arrangement is that the hydrogel-containingmaterial 116 can potentially swell to different partially or fullysaturated-state thicknesses 164. In particular, because the amount thatthe hydrogel-containing material 116 swells depends on the initial,dry-state thickness of the hydrogel-containing material 116, and becausethe portions of the hydrogel-containing material 116 at the indentations192 have greater dry-state thicknesses compared to the portions of thehydrogel-containing material 116 at locations 194, this can result in anon-planar swelling of the hydrogel-containing material 116, as depictedby broken lines 198. The particular dimensions of the non-planarswelling can vary depending on the relative dry-state thicknesses of thehydrogel-containing material 116, the depth 196 of the indentations 192,the extent of saturation of the hydrogel-containing material 116, theparticular composition of the hydrogel-containing material 116, and thelike.

FIG. 14 illustrates a variation on the indentations 192 shown above inFIG. 13. In the design shown in FIG. 14, the indentations 192 can alsoextend in-plane with the backing plate 136 to form locking members 200(e.g., arms or flanged heads). This design can also be produced withco-extrusion or injection molding techniques, and can further assist inmechanically locking the hydrogel-containing material 116 to the backingplate 136. As above, one of skill in the art will appreciate that any ofFIGS. 12-14 could include a tie layer, between the backing plate 136 andthe hydrogel-containing material 116 to assist in bonding.

As discussed above, the outsole 112 with the hydrogel-containingmaterial 116 is particularly suitable for use in global football/soccerapplications. However, the hydrogel-containing material 116 can also beused in combination with other types of footwear 100, such as forarticles of footwear 100 for golf (shown in FIG. 15), for baseball(shown in FIG. 16), and for American football (shown in FIG. 17), eachof which can include traction elements 114 as cleats, studs, and thelike.

FIG. 15 illustrates an aspect in which the hydrogel-containing material116 is positioned on one or more portions of the outsole 112 and/ortraction elements 114 in an article of golf footwear 100. In some cases,the hydrogel-containing material 116 is present on one or more locationsof the ground-facing surface of the outsole 112 except the tractionelements 114 (e.g., a non-cleated surface, such as generally illustratedin FIG. 1 for the global football/soccer footwear 100). Alternatively oradditionally, the hydrogel-containing material 116 can be present as oneor more material segments 116D on one or more surfaces between treadpatterns 202 on ground-facing surface of the outsole 112.

Alternatively or additionally, the hydrogel-containing material 116 canbe incorporated onto one or more surfaces of the traction elements 114.For example, the hydrogel-containing material 116 can also be on acentral region of traction element 114 between the shafts/spikes 150A,such as a surface opposing the area where the traction element 114 ismounted to the outsole 112 backing plate 136. In many traction elementsused for golf footwear, the traction element 114 has a generally flatcentral base region 158A and a plurality of shafts/spikes 150A arrangedaround the perimeter of the central region 158A. In such tractionelements, the hydrogel-containing material 116 can be located on thegenerally flat central base region 158A.

In such aspects, remaining regions of the outsole 112 can be free of thehydrogel-containing material 116. For example, the cleats 114 havinghydrogel-containing material 116 can be separate components that can besecured to the outsole 112 (e.g., screwed or snapped in), where theoutsole 112 itself can be free of the hydrogel-containing material 116.In other words, the material-covered cleats 114 can be provided ascomponents for use with standard footwear not otherwise containing the116 (e.g., golf shoes or otherwise).

FIG. 16 illustrates an aspect in which the hydrogel-containing material116 is positioned on one or more portions of the outsole 112 in anarticle of baseball footwear 100. In some cases, the hydrogel-containingmaterial 116 is present on one or more locations of the ground-facingsurface of the outsole 112 except the cleats 114 (e.g., a non-cleatedsurface, such as generally illustrated in FIG. 1 for the globalfootball/soccer footwear 100). Alternatively or additionally, thehydrogel-containing material 116 can be present as one or more materialsegments 116D on one or more recessed surfaces 204 in the ground-facingsurface of the outsole 112, which recessed surfaces 204 can include thecleats 114 therein (e.g., hydrogel-containing material 116 is locatedonly in one or more of the recessed surfaces 204, but not substantiallyon the cleats).

FIG. 17 illustrates an aspect in which the hydrogel-containing material116 is positioned on one or more portions of the outsole 112 in anarticle of American football footwear 100. In some cases, thehydrogel-containing material 116 is present on one or more locations ofthe ground-facing surface of the outsole 112 except the cleats 114(e.g., a non-cleated surface, such as generally illustrated in FIG. 1for the global football/soccer footwear 100). Alternatively oradditionally, the hydrogel-containing material 116 can be present as oneor more material segments 116D on one or more recessed surfaces 204 inthe ground-facing surface of the outsole 112, which recessed surfaces204 can include the cleats 114 therein (e.g., hydrogel-containingmaterial 116 is located only in one or more of the recessed surfaces204, but not substantially on the cleats).

FIG. 18 illustrates an aspect in which the hydrogel-containing material116 is positioned on one or more portions of the outsole 112 in anarticle of hiking footwear 100 (e.g., hiking shoes or boots). Asillustrated, the traction elements 114 are in the form of lugs 114Dwhich are integrally formed with and protrude from the outsole 112bottom surface 144. In some cases, the hydrogel-containing material 116is present on one or more locations of the bottom surface 144 of theoutsole 112 except the lugs 114D. For example, the hydrogel-containingmaterial 116 can be located on recessed surfaces 204 between adjacentlugs 114D (e.g., but not substantially on the lugs 114D).

The foregoing discussions of footwear 100 and outsole 112 have been madeabove in the context of footwear having traction elements (e.g.,traction elements 114), such as cleats, studs, spikes, lugs, and thelike. However, footwear 100 having hydrogel-containing material 116 canalso be designed for any suitable activity, such as running, track andfield, rugby, cycling, tennis, and the like. In these aspects, one ormore segments of the hydrogel-containing material 116 are preferablylocated in interstitial regions between the traction elements, such asin the interstitial grooves of a running shoe tread pattern.

As discussed above, the material of the present disclosure, such as thehydrogel-containing material 116 for use with outsole 112 (and footwear100), can compositionally include a hydrogel which allows the materialto take up water. As used herein, the terms “take up”, “taking up”,“uptake”, “uptaking”, and the like refer to the drawing of a liquid(e.g., water) from an external source into the material, such as byabsorption, adsorption, or both. Furthermore, as briefly mentionedabove, the term “water” refers to an aqueous liquid that can be purewater, or can be an aqueous carrier with lesser amounts of dissolved,dispersed or otherwise suspended materials (e.g., particulates, otherliquids, and the like).

The ability of the material (e.g., the hydrogel-containing material 116)when used on an outsole to uptake water and to correspondingly swell andincrease in compliance can reflect its ability to prevent soilaccumulation during use with an article of footwear (e.g., footwear100). As discussed above, when the hydrogel-containing material takes upwater (e.g., through absorption, adsorption, capillary action, etc. . .. ), the water taken up by the material transitions thehydrogel-containing material from a dry, relatively more rigid state toa partially or fully saturated state that is relatively more compliant.When the hydrogel-containing material is then subjected to anapplication of pressure, either compressive or flexing, the material canreduce in volume, such as to expel at least a portion of its water.

This expelled water is believed to reduce the adhesive/cohesive forcesof soil particles at the outsole, which taken alone, or more preferablyin combination with the material compliance, can prevent or otherwisereduce soil accumulation at the outsole. Accordingly, the material canundergo dynamic transitions during and between foot strikes, such aswhile a wearer is running or walking, and these dynamic transitions canresult in forces which dislodge accumulated soil or otherwise reducesoil accumulation on the outsole as well.

Based on the multiple interacting mechanisms involved in reducing orpreventing soil accumulation on the outsoles of the present disclosure,it has been found that different properties of the material used to formall or a portion of an outsole can be used to select the desiredperformance benefits needed, such as, for example, preventing orreducing soil adherence to the outsoles or increasing compliance ordurability of the material. For instance, the article of footwear of thepresent disclosure (e.g., the footwear 100), the outsole (e.g., theoutsole 114), and the material (e.g., the hydrogel-containing material116) can be characterized in terms of material's water uptake capacityand rate, swelling capacity, contact angle when wet, coefficient offriction when wet and dry, reduction in storage modulus from dry to wet,reduction in glass transition temperature from dry to wet, and the like.

The terms “Article Sampling Procedure”, “Co-Extruded Film SamplingProcedure”, “Neat Film Sampling Procedure”, “Neat Material SamplingProcedure”, “Water Uptake Capacity Test”, “Water Uptake Rate Test”,“Swelling Capacity Test”, “Contact Angle Test”, “Coefficient of FrictionTest”, “Storage Modulus Test”, “Glass Transition Temperature Test”,“Impact Energy Test”, and “Soil Shedding Article Test” as used hereinrefer to the respective sampling procedures and test methodologiesdescribed in the Property Analysis And Characterization Proceduresection below. These sampling procedures and test methodologiescharacterize the properties of the recited materials, films, articlesand components, and the like, and are not required to be performed asactive steps in the claims.

It is to be understood that any of the Tests disclosed herein can beconducted using any of the Sampling Procedures disclosed herein todetermine a property of an article or a property which can be attributedto an article (e.g. an outsole of an article of footwear) based on ameasurement made in a simulated environment (e.g., using a sampleprepared according to the Co-extruded Film Sampling Procedure, the NeatFilm Sampling Procedure, or the Neat Material Sampling Procedure). Inother words, a measurement obtained on a neat material can be attributedto an article comprising the hydrogel-containing material where thehydrogel-containing material defines at least a portion of a surface orside of the article. Additionally, a measurement made in a simulatedenvironment can be used to select the desired performance property foran article comprising the hydrogel-containing material where thematerial defines at least a portion of a surface or side of the article.

For example, in some aspects, the hydrogel-containing material (e.g.,material present as a sample of a portion of an article preparedaccording to the Article Sampling Procedure, the article having thematerial present at or defining a side or surface of the article fromwhich the sample was taken) has a water uptake capacity at 24 hoursgreater than 40% by weight, as characterized by the Water UptakeCapacity Test with the Article Sampling Procedure, each as describedbelow. In some aspects, it is believed that if a particular article isnot capable of taking up greater than 40% by weight in water within a24-hour period, either due to its water uptake rate being too slow, orits ability to take up water is too low (e.g., due to its thinness, notenough material may be present, or the overall capacity of the materialto take up water is too low), then the article may not be effective inpreventing or reducing soil accumulation.

In further aspects, the hydrogel-containing material as secured topresent in, or defining a portion of an article or component (e.g.including a side or surface of an outsole formed of the material) has awater uptake capacity at 24 hours greater than 50% by weight, greaterthan 100% by weight, greater than 150% by weight, or greater than 200%by weight. In other aspects, outsole has a water uptake capacity at 24hours less than 900% by weight, less than 750% by weight, less than 600%by weight, or less than 500% by weight.

In particular aspects, the hydrogel-containing material as secured topresent in, or defining a portion of an article or component (e.g.including a side or surface of an outsole formed of the material) has awater uptake capacity at 24 hours ranging from 40% by weight to 900% byweight. For example, the outsole can have a water uptake capacityranging from 100% by weight to 900% by weight, from 100% by weight to750% by weight, from 100% by weight to 700% by weight, from 150% byweight to 600% by weight, from 200% by weight to 500% by weight, or from300% by weight to 500% by weight.

These water uptake capacities are determined by the Water UptakeCapacity Test with the Article Sampling Procedure, and can apply tosamples taken at any suitable representative location along the article,where the samples may be acquired pursuant to the Article SamplingProcedure. In some cases, samples can be taken from one or more of theforefoot region, the midfoot region, and/or the heel region of footwear;from each of the forefoot region, the midfoot region, and the heelregion of footwear; from within one or more of the traction elementclusters (between the traction elements) at the forefoot region, themidfoot region, and/or the heel region of footwear; from of the tractionelement clusters of footwear; on planar regions of the traction elementsof footwear (for aspects in which the material is present on thetraction elements), and combinations thereof.

As discussed below, the water uptake capacity of the hydrogel-containingmaterial as secured to present in, or defining a portion of an articleor component (e.g. including a side or surface of an outsole formed ofthe material) can alternatively be measured in a simulated environment,such as using the material co-extruded with a backing substrate orsubstrate body. The backing substrate can be produced from any suitablematerial that is compatible with the material, such as a material usedto form an outsole backing plate. As such, suitable water uptakecapacities at 24 hours for the material as co-extruded with a backingsubstrate, as characterized by the Water Uptake Capacity Test with theCo-extruded Film Sampling Procedure, include those discussed above forthe Water Uptake Capacity Test with the Article Sampling Procedure.

Additionally, it has been found that when the hydrogel-containingmaterial is secured to another surface, such as being thermally oradhesively bonded to an outsole substrate (e.g., an outsole backingplate), the interfacial bond formed between the material and the outsolesubstrate can restrict the extent that the hydrogel-containing materialcan take up water and/or swell. As such, it is believed that thehydrogel-containing material as bonded to an outsole substrate orco-extruded backing substrate can potentially have a lower water uptakecapacity and/or a lower swell capacity compared to the same material ina neat material form, including neat film form.

As such, the water uptake capacity and the water uptake rate of thehydrogel-containing material can also be characterized based on thehydrogel-containing material in neat form (e.g., an isolated film thatis not bonded to another material). The hydrogel-containing material inneat form can have a water uptake capacity at 24 hours greater than 40%by weight, greater than 100% by weight, greater than 300% by weight, orgreater than 1000% by weight, as characterized by the Water UptakeCapacity Test with the Neat Film Sampling Procedure or the Neat MaterialSampling Procedure. The material in neat form can also have a wateruptake capacity at 24 hours less than 900% by weight, less than 800% byweight, less than 700% by weight, less than 600% by weight, or less than500% by weight.

In particular aspects, the hydrogel-containing material in neat form hasa water uptake capacity at 24 hours ranging from 40% by weight to 900%by weight, from 150% by weight to 700% by weight, from 200% by weight to600% by weight, or from 300% by weight to 500% by weight.

The hydrogel-containing material as secured to present in, or defining aportion of an article or component (e.g. including a side or surface ofan outsole formed of the material) can also have a water uptake rategreater than 20 grams/(meter²-minutes^(1/2)), as characterized by theWater Uptake Rate Test with the Article Sampling Procedure. As discussedabove, in some aspects, the outsole having the hydrogel-containingmaterial 116 can take up water between the compressive cycles of footstrikes, which is believed to at least partially replenish thehydrogel-containing material between the foot strikes.

As such, in further aspects, the hydrogel-containing material as securedto present in, or defining a portion of an article or component (e.g.including a side or surface of an outsole formed of the material) has awater uptake rate greater than 20 grams/(meter²-minutes^(1/2)), greaterthan 100 grams/(meter²-minutes^(1/2)), greater than 200grams/(meter²-minutes^(1/2)), greater than 400grams/(meter²-minutes^(1/2)), or greater than 600grams/(meter²-minutes^(1/2)). In particular aspects, the article has awater uptake rate ranging from 1 to 1,500 grams/(meter²-minutes^(1/2)),20 to 1,300 grams/(meter²-minutes^(1/2)), from 30 to 1,200grams/(meter²-minutes^(1/2)), from 30 to 800grams/(meter²-minutes^(1/2)), from 100 to 800grams/(meter²-minutes^(1/2)), from 100 to 600grams/(meter²-minutes^(1/2)), from 150 to 450grams/(meter²-minutes^(1/2)), from 200 to 1,000grams/(meter²-minutes^(1/2)), from 400 to 1,000grams/(meter²-minutes^(1/2)), or from 600 to 900grams/(meter²-minutes^(1/2)).

Suitable water uptake rates for the hydrogel-containing material assecured to a co-extruded backing substrate, as characterized by theWater Uptake Rate Test with the Co-extruded Film Sampling Procedure, andas provided in neat form, as characterized by the Water Uptake Rate Testwith the Neat Film Sampling Procedure, each include those discussedabove for the Water Uptake Rate Test with the Article SamplingProcedure.

In certain aspects, the hydrogel-containing material as secured to,present in, or defining a portion of an article or component (e.g.including a side or surface of an outsole formed of the material) canalso swell, increasing the hydrogel-containing material's thicknessand/or volume, due to water uptake. This swelling of thehydrogel-containing material can be a convenient indicator showing thatthe hydrogel-containing material is taking up water, and can assist inrendering the material compliant. In some aspects, the article has anincrease in material thickness (or swell thickness increase) at 1 hourof greater than 20% or greater than 50%, for example ranging from 30% to350%, from 50% to 400%, from 50% to 300%, from 100% to 300%, from 100%to 200%, or from 150% to 250%, as characterized by the Swelling CapacityTest with the Article Sampling Procedure. In further aspects, thearticle has an increase in material thickness at 24 hours ranging from45% to 400%, from 100% to 350%, or from 150% to 300%.

Additionally, the hydrogel-containing material as secured to, presentin, or defining a portion of an article or component (e.g. including aside or surface of an outsole formed of the material) can have anincrease in hydrogel-containing material volume (or volumetric swellincrease) at 1 hour of greater than 50%, for example ranging from 10% to130%, from 30% to 100%, or from 50% to 90%. Moreover, the article canhave an increase in material volume at 24 hours ranging from 25% to200%, from 50% to 150%, or from 75% to 100%.

For co-extruded film simulations, suitable increases in materialthickness and volume at 1 hour and 24 hours for the material as securedto a co-extruded backing substrate, as characterized by the SwellingCapacity Test with the Co-extruded Film Sampling Procedure, includethose discussed above for the Swelling Capacity Test with the ArticleSampling Procedure.

The hydrogel-containing material in neat form can have an increase inmaterial thickness at 1 hour ranging from 35% to 400%, from 50% to 300%,or from 100% to 200%, as characterized by the Swelling Capacity Testwith the Neat Film Sampling Procedure. In some further aspects, thehydrogel-containing material in neat form can have an increase inmaterial thickness at 24 hours ranging 45% to 500%, from 100% to 400%,or from 150% to 300%. Correspondingly, the hydrogel-containing materialin neat form can have an increase in material volume at 1 hour rangingfrom 50% to 500%, from 75% to 400%, or from 100% to 300%.

As also discussed above, in some aspects, the surface of thehydrogel-containing material forms a side or surface of the article,wherein the side or surface has hydrophilic properties. The hydrophilicproperties of the material's surface can be characterized by determiningthe static sessile drop contact angle of the hydrogel-containingmaterial's surface. Accordingly, in some examples, thehydrogel-containing material's surface in a dry state has a staticsessile drop contact angle (or dry-state contact angle) of less than105°, or less than 95°, less than 85°, as characterized by the ContactAngle Test. The Contact Angle Test can be conducted on a sample obtainedin accordance with the Article Sampling Procedure, the Co-Extruded FilmSampling Procedure, or the Neat Film Sampling Procedure. In some furtherexamples, the hydrogel-containing material in a dry state has a staticsessile drop contact angle ranging from 60° to 100°, from 70° to 100°,or from 65° to 95°.

In other examples, the hydrogel-containing material's surface in a wetstate has a static sessile drop contact angle (or wet-state contactangle) of less than 90°, less than 80°, less than 70°, or less than 60°.In some further examples, the surface in a wet state has a staticsessile drop contact angle ranging from 45° to 75°. In some cases, thedry-state static sessile drop contact angle of the surface is greaterthan the wet-state static sessile drop contact angle of the surface byat least 10°, at least 15°, or at least 20°, for example from 10° to40°, from 10° to 30°, or from 10° to 20°.

The surface of the hydrogel-containing material, including the surfaceof an article can also exhibit a low coefficient of friction when thematerial is wet. Examples of suitable coefficients of friction for thehydrogel-containing material in a dry state (or dry-state coefficient offriction) are less than 1.5, for instance ranging from 0.3 to 1.3, orfrom 0.3 to 0.7, as characterized by the Coefficient of Friction Test.The Coefficient of Friction Test can be conducted on a sample obtainedin accordance with the Article Sampling Procedure, the Co-Extruded FilmSampling Procedure, or the Neat Film Sampling Procedure. Examples ofsuitable coefficients of friction for the hydrogel-containing materialin a wet state (or wet-state coefficient of friction) are less than 0.8or less than 0.6, for instance ranging from 0.05 to 0.6, from 0.1 to0.6, or from 0.3 to 0.5. Furthermore, the hydrogel-containing materialcan exhibit a reduction in its coefficient of friction from its drystate to its wet state, such as a reduction ranging from 15% to 90%, orfrom 50% to 80%. In some cases, the dry-state coefficient of friction isgreater than the wet-state coefficient of friction for the material, forexample being higher by a value of at least 0.3 or 0.5, such as 0.3 to1.2 or 0.5 to 1.

Furthermore, the compliance of the hydrogel-containing material,including an article comprising the material, can be characterized bybased on the hydrogel-containing material's storage modulus in the drystate (when equilibrated at 0% relative humidity (RH)), and in apartially wet state (e.g., when equilibrated at 50% RH or at 90% RH),and by reductions in its storage modulus between the dry and wet states.In particular, the hydrogel-containing material can have a reduction instorage modulus (ΔE′) from the dry state relative to the wet state. Areduction in storage modulus as the water concentration in thehydrogel-containing material increases corresponds to an increase incompliance, because less stress is required for a givenstrain/deformation.

In some aspects, the hydrogel-containing material exhibits a reductionin the storage modulus from its dry state to its wet state (50% RH) ofmore than 20%, more than 40%, more than 60%, more than 75%, more than90%, or more than 99%, relative to the storage modulus in the dry state,and as characterized by the Storage Modulus Test with the Neat FilmSampling Process. In some further aspects, the dry-state storage modulusof the hydrogel-containing material is greater than its wet-state (50%RH) storage modulus by more than 25 megaPascals (MPa), by more than 50MPa, by more than 100 MPa, by more than 300 MPa, or by more than 500MPa, for example ranging from 25 MPa to 800 MPa, from 50 MPa to 800 MPa,from 100 MPa to 800 MPa, from 200 MPa to 800 MPa, from 400 MPa to 800MPa, from 25 MPa to 200 MPa, from 25 MPa to 100 MPa, or from 50 MPa to200 MPa. Additionally, the dry-state storage modulus can range from 40MPa to 800 MPa, from 100 MPa to 600 MPa, or from 200 MPa to 400 MPa, ascharacterized by the Storage Modulus Test. Additionally, the wet-statestorage modulus can range from 0.003 MPa to 100 MPa, from 1 MPa to 60MPa, or from 20 MPa to 40 MPa.

In other aspects, the hydrogel-containing material exhibits a reductionin the storage modulus from its dry state to its wet state (90% RH) ofmore than 20%, more than 40%, more than 60%, more than 75%, more than90%, or more than 99%, relative to the storage modulus in the dry state,and as characterized by the Storage Modulus Test with the Neat FilmSampling Process. In further aspects, the dry-state storage modulus ofthe hydrogel-containing material is greater than its wet-state (90% RH)storage modulus by more than 25 megaPascals (MPa), by more than 50 MPa,by more than 100 MPa, by more than 300 MPa, or by more than 500 MPa, forexample ranging from 25 MPa to 800 MPa, from 50 MPa to 800 MPa, from 100MPa to 800 MPa, from 200 MPa to 800 MPa, from 400 MPa to 800 MPa, from25 MPa to 200 MPa, from 25 MPa to 100 MPa, or from 50 MPa to 200 MPa.Additionally, the dry-state storage modulus can range from 40 MPa to 800MPa, from 100 MPa to 600 MPa, or from 200 MPa to 400 MPa, ascharacterized by the Storage Modulus Test. Additionally, the wet-statestorage modulus can range from 0.003 MPa to 100 MPa, from 1 MPa to 60MPa, or from 20 MPa to 40 MPa.

In addition to a reduction in storage modulus, the hydrogel-containingmaterial can also exhibit a reduction in its glass transitiontemperature from the dry state (when equilibrated at 0% relativehumidity (RH) to the wet state (when equilibrated at 90% RH). While notwishing to be bound by theory, it is believed that the water taken up bythe hydrogel-containing material plasticizes the hydrogel-containingmaterial, which reduces its storage modulus and its glass transitiontemperature, rendering the hydrogel-containing material more compliant(e.g., compressible, expandable, and stretchable).

In some aspects, the hydrogel-containing material can exhibit areduction in glass transition temperature (ΔT_(g)) from its dry-state(0% RH) glass transition temperature to its wet-state glass transition(90% RH) temperature of more than a 5° C. difference, more than a 6° C.difference, more than a 10° C. difference, or more than a 15° C.difference, as characterized by the Glass Transition Temperature Testwith the Neat Film Sampling Process or the Neat Material SamplingProcess. For instance, the reduction in glass transition temperature(ΔT_(g)) can range from more than a 5° C. difference to a 40° C.difference, from more than a 6° C. difference to a 50° C. difference,form more than a 10° C. difference to a 30° C. difference, from morethan a 30° C. difference to a 45° C. difference, or from a 15° C.difference to a 20° C. difference. The hydrogel-containing material canalso exhibit a dry glass transition temperature ranging from −40° C. to−80° C., or from −40° C. to −60° C.

Alternatively (or additionally), the reduction in glass transitiontemperature (ΔT_(g)) can range from a 5° C. difference to a 40° C.difference, form a 10° C. difference to a 30° C. difference, or from a15° C. difference to a 20° C. difference. The hydrogel-containingmaterial can also exhibit a dry glass transition temperature rangingfrom −40° C. to −80° C., or from −40° C. to −60° C.

In further aspects, the hydrogel-containing material can exhibit a soilshedding ability with a relative impact energy ranging from 0 to 0.9,from 0.2 to 0.7, or from 0.4 to 0.5, as characterized by the ImpactEnergy Test with the Article Sampling Procedure, the Co-extruded FilmSampling Procedure, the Neat Film Sampling Procedure, or the NeatMaterial Sampling Procedure. Moreover, the material (e.g., thehydrogel-containing material 116) is preferably durable enough, and hasa sufficient bond to the outsole backing plate, for use over extendeddurations. For instance, it has been found that the hydrogel-containingmaterial of the present disclosure can, in some aspects, continue toperform without significant visual abrasion or delamination for morethan 80 or 100 hours, as discussed above.

In particular aspects, the hydrogel-containing material compositionallyincludes a hydrogel and one or more additives. As used herein, the term“hydrogel” refers to a composition that is capable of taking up at least10% by weight in water, based on a dry weight of the composition. Thehydrogel can be a polymeric hydrogel. The hydrogel can include acrosslinked or crosslinkable polymeric network, where crosslinksinterconnect multiple polymer chains to form the polymeric network, andwhere the crosslinks can be physical crosslinks, covalent crosslinks, orcan include both physical and covalent crosslinks (within the samepolymeric network). The hydrogel can constitute more than 50% by weightof the entire material for the article, or more than 75% by weight, ormore 85% by weight, or more than 95% by weight. In some aspects, thematerial of the articleconsists essentially of the hydrogel.

For a physical crosslink, a copolymer chain can form entangled regionsand/or crystalline regions through non-covalent bonding interactions,such as, for example, an ionic bond, a polar bond, and/or a hydrogenbond. In particular aspects, the crystalline regions create the physicalcrosslink between the copolymer chains. The crystalline regions caninclude hard segments, as described below.

In some aspects, the hydrogel can exhibit sol-gel reversibility,allowing it to function as a thermoplastic polymer, which can beadvantageous for manufacturing and recyclability. As such, in someaspects, the hydrogel of the material includes a physically crosslinkedpolymeric network to function as a thermoplastic hydrogel.

The physically crosslinked hydrogels can be characterized by hardsegments and soft segments, which can exist as phase separated regionswithin the polymeric network while the hydrogel is in a solid(non-molten) state. The hard segments can form portions of the polymerchain backbones, and can exhibit high polarities, allowing the hardsegments of multiple polymer chains to aggregate together, or interactwith each other, to form semi-crystalline regions of the polymericnetwork.

A “semi-crystalline” or “crystalline” region has an ordered molecularstructure with sharp melt points, which remains solid until a givenquantity of heat is absorbed and then rapidly changes into a lowviscosity liquid. A “pseudo-crystalline” region has properties of acrystal, but does not exhibit a true crystalline diffraction pattern.For ease of reference, the term “crystalline region” will be used hereinto collectively refer to a crystalline region, a semi-crystallineregion, and a pseudo-crystalline region of a polymeric network.

In comparison, the soft segments can be longer, more flexible,hydrophilic regions of the polymeric network that allow the polymernetwork to expand and swell under the pressure of taken up water. Thesoft segments can constitute amorphous hydrophilic regions of thehydrogel. The soft segments, or amorphous regions, can also formportions of the backbones of the polymer chains along with the hardsegments. Additionally, one or more portions of the soft segments, oramorphous regions, can be grafted or otherwise extend as pendant chainsthat extend from the backbones at the soft segments. The soft segments,or amorphous regions, can be covalently bonded to the hard segments, orcrystalline regions (e.g., through carbamate linkages). For example, aplurality of amorphous hydrophilic regions can be covalently bonded tothe crystalline regions of the hard segments.

Thus, in various aspects, the hydrogel comprises a crosslinked polymericnetwork which includes a plurality of copolymer chains wherein at leasta portion of the copolymer chains each comprise a hard segmentphysically crosslinked to other hard segments of the copolymer chainsand a soft segment covalently bonded to the hard segment, such asthrough a carbamate group or an ester group. In some cases, the hydrogelincludes a plurality of copolymer chains wherein at least a portion ofthe copolymer chains each comprise a first chain segment physicallycrosslinked to at least one other copolymer chain of the plurality ofcopolymer chains and a hydrophilic segment (e.g., a polyether chainsegment) covalently bonded to the first chain segment, such as through acarbamate group or an ester group.

In various aspects, the hydrogel includes a plurality of copolymerchains, wherein at least a portion of the copolymer chains each includea first segment forming at least a crystalline region with other hardsegments of the copolymer chains; and a second segment, such as a softsegment (e.g., a segment having polyether chains or one or more ethergroups) covalently bonded to the first segment, where the soft segmentforms amorphous regions of the hydrogel. In some cases, the hydrogelincludes a plurality of copolymer chains, where at least a portion ofthe copolymer chains have hydrophilic segments.

The soft segments, or amorphous regions, of the copolymer chains canconstitute a substantial portion of the polymeric network, allowingtheir hydrophilic segments or groups to attract water molecules. In someaspects, the soft segments, or amorphous regions, are present in thecopolymer chains in a ratio (relative to the hard segments, orcrystalline regions) that is at least or greater than 20:1 by weight,that ranges from 20:1 to 110:1 by weight, or from 40:1 to 110:1 byweight, or from 40:1 to 80:1 by weight, or from 60:1 to 80:1.

For a covalent crosslink, one polymer chain is linked to one or moreadditional polymer chains with one or more covalent bonds, typicallywith a linking segment or chain. Covalently crosslinked hydrogels (e.g.,thermoset and photocured hydrogels) can be prepared by covalentlylinking the polymer chains together using one or more multi-functionalcompounds, such as, for example, a molecule having at least twoethylenically-unsaturated groups, at least two oxirane groups (e.g.,diepoxides), or combinations thereof (e.g., glycidyl methacrylate); andcan also include any suitable intermediate chain segment, such as C₁₋₃₀,C₂₋₂₀, or C₂₋₁₀ hydrocarbon, polyether, or polyester chain segments.

The multi-functional compounds can include at least three functionalgroups selected from the group consisting of isocyanidyl, hydroxyl,amino, sulfhydryl, carboxyl or derivatives thereof, and combinationsthereof. In some aspects, such as when the polymer network includespolyurethane, the multi-functional compound can be a polyol having threeor more hydroxyl groups (e.g., glycerol, trimethylolpropane,1,2,6-hexanetriol, 1,2,4-butanetriol, trimethylolethane) or apolyisocyanate having three or more isocyanate groups. In some cases,such as when the polymer network includes polyamide, themulti-functional compound can include, for example, carboxylic acids oractivated forms thereof having three or more carboxyl groups (oractivated forms thereof, polyamines having three or more amino groups,and polyols having three or more hydroxyl groups (e.g., glycerol,trimethylolpropane, 1,2,6-hexanetriol, 1,2,4-butanetriol, andtrimethylolethane). In various cases, such as when the polymer networkincludes polyolefin, the multi-functional compound can be a compoundhaving two ethylenically-unsaturated groups.

When the hydrogel of the material is crosslinked, it has been found thatthe crosslinking density of the crosslinked hydrogel can impact thestructural integrity and water uptake capacities of the material (e.g.,the hydrogel-containing material 116). If the crosslinking density istoo high, the resulting material can be stiff and less compliant, whichcan reduce its water uptake and swelling capacity. On the other hand, ifthe crosslinking density is too low, then the resulting material canlose its structural integrity when saturated. As such, the hydrogel(s)of the material preferably have a balanced crosslinking density suchthat the material retains its structural integrity, yet is alsosufficiently compliant when partially or fully saturated with water.

The hydrogel of the material (e.g., the hydrogel-containing material116) can include any suitable polymer chains that provide the functionalproperties disclosed herein (e.g., water uptake, swelling, and moregenerally, preventing soil accumulation). For example, the hydrogel canbe a polymeric hydrogel comprising or consisting essentially of one ormore polymer chains such as one or more polyurethanes, one or morepolyamides, one or more polyolefins, and combinations thereof (e.g., ahydrogel based on polyurethane(s) and polyamide(s)). The polymerichydrogel can comprise or consist essentially of one or more polysiloxanechains (i.e., the hydrogel can comprise or consist essentially of asilicone hydrogel). The polymeric hydrogel can comprise or consistessentially of one or more ionomeric polymer chains (i.e., the hydrogelcan comprise or consist essentially of an ionomeric hydrogel). In theseaspects, the hydrogel can include a plurality of copolymer chainswherein at least a portion of the copolymer chains each include apolyurethane segment, a polyamide segment, a polyolefin segment, apolysiloxane segment, an ionomer segment, and combinations thereof. Thesegments can comprise one or more polyurethanes, one or more polyamides,one or more polyolefins, and combinations thereof.

In some aspects, the hydrogel includes a polymeric network with one ormore polyurethane copolymer chains (i.e., a plurality of polyurethanechains), referred to as a “polyurethane hydrogel”. The polyurethanehydrogel can be physically and/or covalently crosslinked. Thepolyurethane hydrogel can be produced by polymerizing one or moreisocyanates with one or more polyols to produce copolymer chains havingcarbamate linkages (—N(CO)O—) as illustrated below in Formula 1, wherethe isocyanate(s) each preferably include two or more isocyanate (—NCO)groups per molecule, such as 2, 3, or 4 isocyanate groups per molecule(although, single-functional isocyanates can also be optionallyincluded, e.g., as chain terminating units).

In these aspects, each R₁ independently is an aliphatic or aromaticsegment, and each R₂ is a hydrophilic segment.

Unless otherwise indicated, any of the functional groups or chemicalcompounds described herein can be substituted or unsubstituted. A“substituted” group or chemical compound, such as an alkyl, alkenyl,alkynyl, cycloalkyl, cycloalkenyl, aryl, heteroaryl, alkoxyl, ester,ether, or carboxylic ester refers to an alkyl, alkenyl, alkynyl,cycloalkyl, cycloalkenyl, aryl, heteroaryl, alkoxyl, ester, ether, orcarboxylic ester group, has at least one hydrogen radical that issubstituted with a non-hydrogen radical (i.e., a substitutent). Examplesof non-hydrogen radicals (or substituents) include, but are not limitedto, alkyl, cycloalkyl, alkenyl, cycloalkenyl, alkynyl, ether, aryl,heteroaryl, heterocycloalkyl, hydroxyl, oxy (or oxo), alkoxyl, ester,thioester, acyl, carboxyl, cyano, nitro, amino, amido, sulfur, and halo.When a substituted alkyl group includes more than one non-hydrogenradical, the substituents can be bound to the same carbon or two or moredifferent carbon atoms.

Additionally, the isocyanates can also be chain extended with one ormore chain extenders to bridge two or more isocyanates. This can producepolyurethane copolymer chains as illustrated below in Formula 2, whereinR₃ includes the chain extender.

Each segment R₁, or the first segment, in Formulas 1 and 2 canindependently include a linear or branched C₃₋₃₀ segment, based on theparticular isocyanate(s) used, and can be aliphatic, aromatic, orinclude a combination of aliphatic portions(s) and aromatic portion(s).The term “aliphatic” refers to a saturated or unsaturated organicmolecule that does not include a cyclically conjugated ring systemhaving delocalized pi electrons. In comparison, the term “aromatic”refers to a cyclically conjugated ring system having delocalized pielectrons, which exhibits greater stability than a hypothetical ringsystem having localized pi electrons.

In aliphatic aspects (from aliphatic isocyanate(s)), each segment R₁ caninclude a linear aliphatic group, a branched aliphatic group, acycloaliphatic group, or combinations thereof. For instance, eachsegment R₁ can include a linear or branched C₃₋₂₀ alkylene segment(e.g., C₄₋₁₅ alkylene or C₆₋₁₀ alkylene), one or more C₃₋₈ cycloalkylenesegments (e.g., cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl,cycloheptyl, or cyclooctyl), and combinations thereof.

Examples of suitable aliphatic diisocyanates for producing thepolyurethane copolymer chains include hexamethylene diisocyanate (HDI),isophorone diisocyanate (IPDI), butylene diisocyanate (BDI),bisisocyanatocyclohexylmethane (HMDI), 2,2,4-trimethylhexamethylenediisocyanate (TMDI), bisisocyanatomethylcyclohexane,bisisocyanatomethyltricyclodecane, norbornane diisocyanate (NDI),cyclohexane diisocyanate (CHDI), 4,4′-dicyclohexylmethane diisocyanate(H12MDI), diisocyanatododecane, lysine diisocyanate, and combinationsthereof.

In aromatic aspects (from aromatic isocyanate(s)), each segment R₁ caninclude one or more aromatic groups, such as phenyl, naphthyl,tetrahydronaphthyl, phenanthrenyl, biphenylenyl, indanyl, indenyl,anthracenyl, and fluorenyl. Unless otherwise indicated, an aromaticgroup can be an unsubstituted aromatic group or a substituted aromaticgroup, and can also include heteroaromatic groups. “Heteroaromatic”refers to monocyclic or polycyclic (e.g., fused bicyclic and fusedtricyclic) aromatic ring systems, where one to four ring atoms areselected from the group consisting of oxygen, nitrogen, or sulfur, andthe remaining ring atoms are carbon, and where the ring system is joinedto the remainder of the molecule by any of the ring atoms. Examples ofsuitable heteroaryl groups include pyridyl, pyrazinyl, pyrimidinyl,pyrrolyl, pyrazolyl, imidazolyl, thiazolyl, tetrazolyl, oxazolyl,isooxazolyl, thiadiazolyl, oxadiazolyl, furanyl, quinolinyl,isoquinolinyl, benzoxazolyl, benzimidazolyl, and benzothiazolyl.

Examples of suitable aromatic diisocyanates for producing thepolyurethane copolymer chains include toluene diisocyanate (TDI), TDIadducts with trimethyloylpropane (TMP), methylene diphenyl diisocyanate(MDI), xylene diisocyanate (XDI), tetramethylxylylene diisocyanate(TMXDI), hydrogenated xylene diisocyanate (HXDI), naphthalene1,5-diisocyanate (NDI), 1,5-tetrahydronaphthalene diisocyanate,para-phenylene diisocyanate (PPDI), 3,3′-dimethyldiphenyl-4,4′-diisocyanate (DDDI), 4,4′-dibenzyl diisocyanate (DBDI),4-chloro-1,3-phenylene diisocyanate, and combinations thereof. In someaspects, the copolymer chains are substantially free of aromatic groups.

In some preferred aspects, the polyurethane copolymer chains areproduced from diisocynates including HMDI, TDI, MDI, H₁₂ aliphatics, andcombinations thereof.

Examples of suitable triisocyanates for producing the polyurethanecopolymer chains include TDI, HDI, and IPDI adducts withtrimethyloylpropane (TMP), uretdiones (i.e., dimerized isocyanates),polymeric MDI, and combinations thereof.

Segment R₃ in Formula 2 can include a linear or branched C₂-C₁₀ segment,based on the particular chain extender polyol used, and can be, forexample, aliphatic, aromatic, or polyether. Examples of suitable chainextender polyols for producing the polyurethane copolymer chains includeethylene glycol, lower oligomers of ethylene glycol (e.g., diethyleneglycol, triethylene glycol, and tetraethylene glycol), 1,2-propyleneglycol, 1,3-propylene glycol, lower oligomers of propylene glycol (e.g.,dipropylene glycol, tripropylene glycol, and tetrapropylene glycol),1,4-butylene glycol, 2,3-butylene glycol, 1,6-hexanediol,1,8-octanediol, neopentyl glycol, 1,4-cyclohexanedimethanol,2-ethyl-1,6-hexanediol, 1-methyl-1,3-propanediol,2-methyl-1,3-propanediol, dihydroxyalkylated aromatic compounds (e.g.,bis(2-hydroxyethyl) ethers of hydroquinone and resorcinol,xylene-α,α-diols, bis(2-hydroxyethyl) ethers of xylene-α,α-diols, andcombinations thereof.

Segment R₂ in Formula 1 and 2 can include polyether, polyester,polycarbonate, an aliphatic group, or an aromatic group, wherein thealiphatic group or aromatic group is substituted with one or morependant hydrophilic groups selected from the group consisting ofhydroxyl, polyether, polyester, polylactone (e.g., polyvinylpyrrolidone(PVP)), amino, carboxylate, sulfonate, phosphate, ammonium (e.g.,tertiary and quaternary ammonium), zwitterion (e.g., a betaine, such aspoly(carboxybetaine (pCB) and ammonium phosphonates such asphosphatidylcholine), and combinations thereof. Therefore, thehydrophilic segment of R₂ can form portions of the hydrogel backbone, orbe grafted to the hydrogel backbone as a pendant group. In some aspects,the pendant hydrophilic group or segment is bonded to the aliphaticgroup or aromatic group through a linker. Each segment R₂ can be presentin an amount of 5% to 85% by weight, from 5% to 70% by weight, or from10% to 50% by weight, based on the total weight of the reactantmonomers.

In some aspects, at least one R₂ segment includes a polyether segment(i.e., a segment having one or more ether groups). Suitable polyethersinclude, but are not limited to polyethylene oxide (PEO), polypropyleneoxide (PPO), polytetrahydrofuran (PTHF), polytetramethylene oxide(PTMO), and combinations thereof. The term “alkyl” as used herein refersto straight chained and branched saturated hydrocarbon groups containingone to thirty carbon atoms, for example, one to twenty carbon atoms, orone to ten carbon atoms. The term C_(n) means the alkyl group has “n”carbon atoms. For example, C₄ alkyl refers to an alkyl group that has 4carbon atoms. C₁₋₇ alkyl refers to an alkyl group having a number ofcarbon atoms encompassing the entire range (i.e., 1 to 7 carbon atoms),as well as all subgroups (e.g., 1-6, 2-7, 1-5, 3-6, 1, 2, 3, 4, 5, 6,and 7 carbon atoms). Non-limiting examples of alkyl groups include,methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl (2-methylpropyl),t-butyl (1,1-dimethylethyl), 3,3-dimethylpentyl, and 2-ethylhexyl.Unless otherwise indicated, an alkyl group can be an unsubstituted alkylgroup or a substituted alkyl group.

In some cases, at least one R₂ segment includes a polyester segment. Thepolyester can be derived from the polyesterification of one or moredihydric alcohols (e.g., ethylene glycol, 1,3-propylene glycol,1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol,2-methylpentanediol-1,5, diethylene glycol, 1,5-pentanediol,1,5-hexanediol, 1,2-dodecanediol, cyclohexanedimethanol, andcombinations thereof) with one or more dicarboxylic acids (e.g., adipicacid, succinic acid, sebacic acid, suberic acid, methyladipic acid,glutaric acid, pimelic acid, azelaic acid, thiodipropionic acid andcitraconic acid and combinations thereof). The polyester also can bederived from polycarbonate prepolymers, such as poly(hexamethylenecarbonate) glycol, poly(propylene carbonate) glycol, poly(tetramethylenecarbonate)glycol, and poly(nonanemethylene carbonate) glycol. Suitablepolyesters can include, for example, polyethylene adipate (PEA),poly(1,4-butylene adipate), poly(tetramethylene adipate),poly(hexamethylene adipate), polycaprolactone, polyhexamethylenecarbonate, poly(propylene carbonate), poly(tetramethylene carbonate),poly(nonanemethylene carbonate), and combinations thereof.

In various cases, at least one R₂ segment includes a polycarbonatesegment. The polycarbonate can be derived from the reaction of one ormore dihydric alcohols (e.g., ethylene glycol, 1,3-propylene glycol,1,2-propylene glycol, 1,4-butanediol, 1,3-butanediol,2-methylpentanediol-1,5, diethylene glycol, 1,5-pentanediol,1,5-hexanediol, 1,2-dodecanediol, cyclohexanedimethanol, andcombinations thereof) with ethylene carbonate.

In various aspects, at least one R₂ segment includes an aliphatic groupsubstituted with one or more hydrophilic groups selected from the groupconsisting of hydroxyl, polyether, polyester, polylactone (e.g.,polyvinylpyrrolidone), amino, carboxylate, sulfonate, phosphate,ammonium (e.g., tertiary and quaternary ammonium), zwitterion (e.g., abetaine, such as poly(carboxybetaine (pCB) and ammonium phosphonatessuch as phosphatidylcholine), and combinations thereof. In some aspects,the aliphatic group is linear and can include, for example, a C₁₋₂₀alkylene chain or a C₁₋₂₀ alkenylene chain (e.g., methylene, ethylene,propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene,decylene, undecylene, dodecylene, tridecylene, ethenylene, propenylene,butenylene, pentenylene, hexenylene, heptenylene, octenylene,nonenylene, decenylene, undecenylene, dodecenylene, tridecenylene). Theterm “alkylene” refers to a bivalent hydrocarbon. The term C_(n) meansthe alkylene group has “n” carbon atoms. For example, C₁₋₆alkylenerefers to an alkylene group having, e.g., 1, 2, 3, 4, 5, or 6 carbonatoms. The term “alkenylene” refers to a bivalent hydrocarbon having atleast one double bond.

In some cases, at least one R₂ segment includes an aromatic groupsubstituted with one or more hydrophilic groups selected from the groupconsisting of hydroxyl, polyether, polyester, polylactone (e.g.,polyvinylpyrrolidone), amino, carboxylate, sulfonate, phosphate,ammonium (e.g., tertiary and quaternary ammonium), zwitterion (e.g., abetaine, such as poly(carboxybetaine (pCB) and ammonium phosphonatessuch as phosphatidylcholine), and combinations thereof. Suitablearomatic groups include, but are not limited to, phenyl, naphthyl,tetrahydronaphthyl, phenanthrenyl, biphenylenyl, indanyl, indenyl,anthracenyl, fluorenylpyridyl, pyrazinyl, pyrimidinyl, pyrrolyl,pyrazolyl, imidazolyl, thiazolyl, tetrazolyl, oxazolyl, isooxazolyl,thiadiazolyl, oxadiazolyl, furanyl, quinolinyl, isoquinolinyl,benzoxazolyl, benzimidazolyl, and benzothiazolyl.

The aliphatic and aromatic groups are substituted with an appropriatenumber of pendant hydrophilic and/or charged groups so as to provide theresulting hydrogel with the properties described herein. In someaspects, the pendant hydrophilic group is one or more (e.g., 2, 3, 4, 5,6, 7, 8, 9, 10 or more) hydroxyl groups. In various aspects, the pendanthydrophilic group is one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 ormore) amino groups. In some cases, the pendant hydrophilic group is oneor more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 or more) carboxylate groups.For example, the aliphatic group can include polyacrylic acid. In somecases, the pendant hydrophilic group is one or more (e.g., 2, 3, 4, 5,6, 7, 8, 9, 10 or more) sulfonate groups. In some cases, the pendanthydrophilic group is one or more (e.g., 2, 3, 4, 5, 6, 7, 8, 9, 10 ormore) phosphate groups. In some aspects, the pendant hydrophilic groupis one or more ammonium groups (e.g., tertiary and/or quaternaryammonium). In other aspects, the pendant hydrophilic group is one ormore zwitterions (e.g., a betaine, such as poly(carboxybetaine (pCB) andammonium phosphonates such as phosphatidylcholine).

In some aspects, the R₂ segment includes charged groups that are capableof binding to a counterion to ionically crosslink the polymer thepolymer network and form ionomers. In these aspects, for example, R₂ isan aliphatic or aromatic group having pendant amino, carboxylate,sulfonate, phosphate, ammonium, zwitterionic groups, or combinationsthereof. For example, R₂ can be an aliphatic or aromatic group havingone or more pendant carboxylate group.

In various cases, the pendant hydrophilic group is at least onepolyether, such as two polyethers. In other cases, the pendanthydrophilic group is at least one polyester. In various cases, thependant hydrophilic group is polylactone (e.g., polyvinylpyrrolidone).Each carbon atom of the pendant hydrophilic group can optionally besubstituted with, e.g., C₁₋₆ alkyl. In some of these aspects, thealiphatic and aromatic groups can be graft polymers, wherein the pendantgroups are homopolymers (e.g., polyethers, polyesters,polyvinylpyrrolidone).

In some preferred aspects, the pendant hydrophilic group is a polyether(e.g., polyethylene oxide and polyethylene glycol),polyvinylpyrrolidone, polyacrylic acid, or combinations thereof.

The pendant hydrophilic group can be bonded to the aliphatic group oraromatic group through a linker. The linker can be any bifunctionalsmall molecule (e.g., C₁₋₂₀) capable of linking the pendant hydrophilicgroup to the aliphatic or aromatic group. For example, the linker caninclude a diisocyanate, as previously described herein, which whenlinked to the pendant hydrophilic group and to the aliphatic or aromaticgroup forms a carbamate bond. In some aspects, the linker can be4,4′-diphenylmethane diisocyanate (MDI), as shown below.

In some exemplary aspects, the pendant hydrophilic group is polyethyleneoxide and the linking group is MDI, as shown below.

In some cases, the pendant hydrophilic group is functionalized to enableit to bond to the aliphatic or aromatic group, optionally through thelinker. In various aspects, for example, when the pendant hydrophilicgroup includes an alkene group, which can undergo a Michael additionwith a sulfhydryl-containing bifunctional molecule (i.e., a moleculehaving a second reactive group, such as a hydroxyl group or aminogroup), to result in a hydrophilic group that can react with the polymerbackbone, optionally through the linker, using the second reactivegroup. For example, when the pendant hydrophilic group ispolyvinylpyrrolidone, it can react with the sulfhydryl group onmercaptoethanol to result in hydroxyl-functionalizedpolyvinylpyrrolidone, as shown below.

In some of the aspects disclosed herein, at least one R₂ segment ispolytetramethylene oxide. In other exemplary aspects, at least one R₂segment can be an aliphatic polyol functionalized with polyethyleneoxide or polyvinylpyrrolidone, such as the polyols described in E.P.Patent No. 2 462 908. For example, the R₂ segment can be derived fromthe reaction product of a polyol (e.g., pentaerythritol or2,2,3-trihydroxypropanol) and either MDI-derivatized methoxypolyethyleneglycol (to obtain compounds as shown in Formulas 6 or 7) or withMDI-derivatized polyvinylpyrrolidone (to obtain compounds as shown inFormulas 8 or 9) that had been previously been reacted withmercaptoethanol, as shown below,

In various cases, at least one R₂ is a polysiloxane. In these cases, R₂can be derived from a silicone monomer of Formula 10, such as a siliconemonomer disclosed in U.S. Pat. No. 5,969,076:

wherein:

a is 1 to 10 or larger (e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, or 10);

each R⁴ independently is hydrogen, C₁₋₁₈ alkyl, C₂₋₁₈ alkenyl, aryl, orpolyether; and

each R⁵ independently is C₁₋₁₀alkylene, polyether, or polyurethane.

In some aspects, each R⁴ independently is H, C₁₋₁₀ alkyl, C₂₋₁₀alkenyl,C₁₋₆aryl, polyethylene, polypropylene, or polybutylene. For example,each R⁴ can independently be selected from the group consisting ofmethyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, s-butyl, t-butyl,ethenyl, propenyl, phenyl, and polyethylene.

In various aspects, each R⁵ independently is C₁₋₁₀alkylene (e.g.,methylene, ethylene, propylene, butylene, pentylene, hexylene,heptylene, octylene, nonylene, or decylene). In other cases, each R⁵ ispolyether (e.g., polyethylene, polypropylene, or polybutylene). Invarious cases, each R⁵ is polyurethane.

In some aspects, the hydrogel includes a crosslinked polymeric networkthat includes copolymer chains that are derivatives of polyurethane.This crosslinked polymeric network can be produced by polymerizing oneor more isocyanates with one or more polyamino compounds, polysulfhydrylcompounds, or combinations thereof, as shown in Formulas 11 and 12,below:

wherein the variables are as described above. Additionally, theisocyanates can also be chain extended with one or more polyamino orpolythiol chain extenders to bridge two or more isocyanates, such aspreviously described for the polyurethanes of Formula 2.

In some aspects, the polyurethane hydrogel is composed of MDI, PTMO, and1,4-butylene glycol, as described in U.S. Pat. No. 4,523,005.

In some aspects, the polyurethane hydrogel is physically crosslinkedthrough e.g., nonpolar or polar interactions between the urethane orcarbamate groups on the polymers (the hard segments), and is athermoplastic polyurethane (TPU), or specifically, what may be referredto as a hydrophilic thermoplastic polyurethane. In these aspects,component R₁ in Formula 1, and components R₁ and R₃ in Formula 2, formsthe portion of the polymer often referred to as the “hard segment”, andcomponent R₂ forms the portion of the polymer often referred to as the“soft segment”. In these aspects, the soft segment can be covalentlybonded to the hard segment.

Commercially available thermoplastic polyurethane hydrogels suitable forthe present use include, but are not limited to those under thetradename “TECOPHILIC”, such as TG-500, TG-2000, SP-80A-150, SP-93A-100,SP-60D-60 (Lubrizol, Countryside, Ill.), “ESTANE” (e.g., ALR G 500;Lubrizol, Countryside, Ill.).

In various aspects, the polyurethane hydrogel is covalently crosslinked,as previously described herein.

In some aspects, the polyamide segment of the polyamide hydrogelcomprises or consists essentially of a polyamide. The polyamide hydrogelcan be formed from the polycondensation of a polyamide prepolymer with ahydrophilic prepolymer to form a block copolyamide.

In some aspects, the polyamide segment of the polyamide hydrogel can bederived from the condensation of polyamide prepolymers, such as lactams,amino acids, and/or diamino compounds with dicarboxylic acids, oractivated forms thereof. The resulting polyamide segments include amidelinkages (—(CO)NH—). The term “amino acid” refers to a molecule havingat least one amino group and at least one carboxyl group. Each polyamidesegment of the polyamide hydrogel can be the same or different.

In some aspects, the polyamide segment is derived from thepolycondensation of lactams and/or amino acids, and includes an amidesegment having a structure shown in Formula 13, below, wherein R₆ is thesegment of the block copolymer derived from the lactam or amino acid,and R₂ is the segment derived from a hydrophilic prepolymer:

In some aspects, R₆ is derived from a lactam. In some cases, R₆ isderived from a C₃₋₂₀ lactam, or a C₄₋₁₅ lactam, or a C₆₋₁₂ lactam. Forexample, R₆ can be derived from caprolactam or laurolactam. In somecases, R₆′ is derived from one or more amino acids. In various cases, R₆is derived from a C₄₋₂₅ amino acid, or a C₅₋₂₀ amino acid, or a C₈₋₁₅amino acid. For example, R₆′ can be derived from 12-aminolauric acid or11-aminoundecanoic acid.

In some cases, Formula 13 includes a polyamide-polyether block copolymersegment, as shown below:

wherein m is 3-20, and n is 1-8. In some exemplary aspects, m is 4-15,or 6-12 (e.g., 6, 7, 8, 9, 10, 11, or 12), and n is 1 2, or 3. Forexample, m can be 11 or 12, and n can be 1 or 3.

In various aspects, the polyamide segment of the polyamide hydrogel isderived from the condensation of diamino compounds with dicarboxylicacids, or activated forms thereof, and includes an amide segment havinga structure shown in Formula 15, below, wherein R₇ is the segment of theblock copolymer derived from the diamino compound, R₈ is the segmentderived from the dicarboxylic acid compound, and R₂ is the segmentderived from a hydrophilic prepolymer:

In some aspects, R₇ is derived from a diamino compound that includes analiphatic group having C₄₋₁₅ carbon atoms, or C₅₋₁₀ carbon atoms, orC₆₋₉ carbon atoms. In some aspects, the diamino compound includes anaromatic group, such as phenyl, naphthyl, xylyl, and tolyl. Suitablediamino compounds include, but are not limited to, hexamethylene diamine(HMD), tetramethylene diamine, trimethyl hexamethylene diamine (TMD),m-xylylene diamine (MXD), and 1,5-pentamine diamine. In various aspects,R₈ is derived from a dicarboxylic acid or activated form thereof,includes an aliphatic group having C₄₋₁₅ carbon atoms, or C₅₋₁₂ carbonatoms, or C₆₋₁₀ carbon atoms. In some cases, the dicarboxylic acid oractivated form thereof includes an aromatic group, such as phenyl,naphthyl, xylyl, and tolyl. Suitable carboxylic acids or activated formsthereof include, but are not limited to adipic acid, sebacic acid,terephthalic acid, and isophthalic acid. In some aspects, the copolymerchains are substantially free of aromatic groups.

In some preferred aspects, each polyamide segment is independentlyderived from a polyamide prepolymer selected from the group consistingof 12-aminolauric acid, caprolactam, hexamethylene diamine and adipicacid.

Additionally, the polyamide hydrogels can also be chain extended withone or more polyamino, polycarboxyl (or derivatives thereof), or aminoacid chain extenders, as previously described herein. In some aspects,the chain extender can include a diol, dithiol, amino alcohol,aminoalkyl mercaptan, hydroxyalkyl mercaptan, a phosphite or abisacyllactam compound (e.g., triphenylphosphite, N,N′-terephthaloylbis-laurolactam, and diphenyl isophthalate).

Each component R₂ of Formula 13 and 15 independently is polyether,polyester, polycarbonate, an aliphatic group, or an aromatic group,wherein the aliphatic group or aromatic group is substituted with one ormore pendant hydrophilic groups, as previously described herein, whereinthe pendant group can optionally be bonded to the aliphatic or aromaticgroup through a linker, as previously described herein.

In some preferred aspects, R₂ is derived from a compound selected fromthe group consisting of polyethylene oxide (PEO), polypropylene oxide(PPO), polytetrahydrofuran (PTHF), polytetramethylene oxide (PTMO), apolyethylene oxide-functionalized aliphatic or aromatic group, apolyvinylpyrrolidone-functionalized aliphatic of aromatic group, andcombinations thereof. In various cases, R₂ is derived from a compoundselected from the group consisting of polyethylene oxide (PEO),polypropylene oxide (PPO), polytetramethylene oxide (PTMO), apolyethylene oxide-functionalized aliphatic or aromatic group, andcombinations thereof. For example, R₂ can be derived from a compoundselected from the group consisting of polyethylene oxide (PEO),polytetramethylene oxide (PTMO), and combinations thereof.

In some aspects, the polyamide hydrogel is physically crosslinkedthrough, e.g., nonpolar or polar interactions between the polyamidegroups on the polymers, and is a thermoplastic polyamide, or inparticular, a hydrophilic thermoplastic polyamide. In these aspects,component R₆ in Formula 13 and components R₇ and R₈ in Formula 15 formthe portion of the polymer often referred to as the “hard segment”, andcomponent R₂ forms the portion of the polymer often referred to as the“soft segment”. Therefore, in some aspects, the hydrogel can include aphysically crosslinked polymeric network having one or more polymerchains with amide linkages.

In some aspects, the hydrogel includes plurality of block copolymerchains, wherein at least a portion of the block copolymer chains eachinclude a polyamide block and a hydrophilic block, (e.g., a polyetherblock) covalently bonded to the polyamide block to result in athermoplastic polyamide block copolymer hydrogel (i.e., apolyamide-polyether block copolymer). In these aspects, the polyamidesegments can interact with each other to form the crystalline region.Therefore, the polyamide block copolymer chains can each comprise aplurality of polyamide segments forming crystalline regions with otherpolyamide segments of the polyamide block copolymer chains, and aplurality of hydrophilic segments covalently bonded to the polyamidesegments.

In some aspects, the polyamide is polyamide-11 or polyamide-12 and thepolyether is selected from the group consisting of polyethylene oxide,polypropylene oxide, and polytetramethylene oxide. Commerciallyavailable thermoplastic polyamide hydrogels suitable for the present useinclude those under the tradename “PEBAX” (e.g., “PEBAX MH1657” and“PEBAX MV1074”) from Arkema, Inc., Clear Lake, Tex.), and “SERENE”coating (Sumedics, Eden Prairie, Minn.).

In various aspects, the polyamide hydrogel is covalently crosslinked, aspreviously described herein.

In some aspects, the hydrogel comprises or consists essentially of apolyolefin hydrogel. The polyolefin hydrogel can be formed through freeradical, cationic, and/or anionic polymerization by methods well knownto those skilled in the art (e.g., using a peroxide initiator, heat,and/or light).

In some aspects, the hydrogel can include one or more, or a plurality,of polyolefin chains. For instance, the polyolefin can includepolyacrylamide, polyacrylate, polyacrylic acid and derivatives or saltsthereof, polyacrylohalide, polyacrylonitrile, polyallyl alcohol,polyallyl ether, polyallyl ester, polyallyl carbonate, polyallylcarbamate, polyallyl sulfone, polyallyl sulfonic acid, polyallyl amine,polyallyl cyanide, polyvinyl ester, polyvinyl thioester, polyvinylpyrrolidone, polyα-olefin, polystyrene, and combinations thereof.Therefore, the polyolefin can be derived from a monomer selected fromthe group consisting of acrylamide, acrylate, acrylic acid andderivatives or salts thereof, acrylohalide, acrylonitrile, allylalcohol, allyl ether, allyl ester, allyl carbonate, allyl carbamate,allyl sulfone, allyl sulfonic acid, allyl amine, allyl cyanide, vinylester, vinyl thioester, vinyl pyrrolidone, α-olefin, styrene, andcombinations thereof.

In some aspects, the polyolefin is derived from an acrylamide. Suitableacrylamides can include, but are not limited to, acrylamide,methacrylamide, ethylacrylamide, N,N-dimethylacrylamide,N-isopropylacrylamide, N-tert-butylacrylamide,N-isopropylmethacrylamide, N-phenylacrylamide,N-diphenylmethylacrylamide, N-(triphenylmethyl)methacrylamide,N-hydroxyethyl acrylamide, 3-acryloylamino-1-propanol,N-acryloylamido-ethoxyethanol, N-[tris(hydroxymethyl)methyl]acrylamide,N-(3-methoxypropyl)acrylamide,N-[3-(dimethylamino)propyl]methacrylamide,(3-acrylamidopropyl)trimethylammonium chloride, diacetone acrylamide,2-acrylamido-2-methyl-1-propanesulfonic acid, salts of2-acrylamido-2-methyl-1-propanesulfonic acid, 4-acryloylmorpholine, andcombinations thereof. For example, the acrylamide prepolymer can beacrylamide or methacrylamide.

In some cases, the polyolefin is derived from an acrylate (e.g.,acrylate and/or alkylacrylate). Suitable acrylates include, but are notlimited to, methyl acrylate, ethyl acrylate, propyl acrylate, isopropylacrylate, n-butyl acrylate, isobutyl acrylate, tert-butyl acrylate,hexyl acrylate, isooctyl acrylate, isodecyl acrylate, octadecylacrylate, lauryl acrylate, 2-ethylhexyl acrylate, 4-tert-butylcyclohexylacrylate, 3,5,5-trimethylhexyl acrylate, isobornyl acrylate, vinylmethacrylate, allyl methacrylate, methyl methacrylate, ethylmethacrylate, butyl methacrylate, isobutyl methacrylate, tert-butylmethacrylate, hexyl methacrylate, 2-ethylhexyl methacrylate, isodecylmethacrylate, lauryl methacrylate, stearyl methacrylate, cyclohexylmethacrylate, 3,3,5-trimethylcyclohexyl methacrylate, combinationsthereof, and the like. For example, acrylate prepolymer can be methylacrylate, ethyl methacrylate, or 2-hydroxyethyl methacrylate.

In some cases, the polyolefin is derived from an acrylic acid or aderivative or salt thereof. Suitable acrylic acids, but are not limitedto acrylic acid, sodium acrylate, methacrylic acid, sodium methacrylate,2-ethylacrylic acid, 2-propylacrylic acid, 2-bromoacrylic acid,2-(bromomethyl)acrylic acid, 2-(trifluoromethyl)acrylic acid, acryloylchloride, methacryloyl chloride, and 2-ethylacryloyl chloride.

In various aspects, the polyolefin can be derived from an allyl alcohol,allyl ether, allyl ester, allyl carbonate, allyl carbamate, allylsulfone, allyl sulfonic acid, allyl amine, allyl cyanide, or acombination thereof. For example, the polyolefin segment can be derivedfrom allyloxyethanol, 3-allyloxy-1,2-propanediol, allyl butyl ether,allyl benzyl ether, allyl ethyl ether, allyl phenyl ether, allyl2,4,6-tribromophenyl ether, 2-allyloxybenzaldehyde,2-allyloxy-2-hydroxybenzophenone, allyl acetate, allyl acetoacetate,allyl chloroacetate, allylcyanoacetate, allyl2-bromo-2-methylpropionate, allyl butyrate, allyltrifluoroacetae, allylmethyl carbonate, tert-butyl N-allylcarbamate, allyl methyl sulfone,3-allyloxy-2-hydroxy-1-propanesulfonic acid,3-allyloxy-2-hydroxy-1-propanesulfonic acid sodium salt, allylamine, anallylamine salt, and allyl cyanide.

In some cases, the polyolefin can be derived from a vinyl ester, vinylthioester, vinyl pyrrolidone (e.g., N-vinyl pyrrolidone), andcombinations thereof. For example, the vinyl monomer can be vinylchloroformate, vinyl acetate, vinyl decanoate, vinyl neodecanoate, vinylneononanoate, vinylpivalate, vinyl propionate, vinyl stearate, vinylvalerate, vinyl trifluoroacetate, vinyl benzoate, vinyl4-tert-butylbenzoate, vinyl cinnamate, butyl vinyl ether, tert-butylvinyl ether, cyclohexyl vinyl ether, dodecyl vinyl ether, ethyleneglycol vinyl ether, 2-ethylhexyl vinyl ether, ethyl vinyl ether,ethyl-1-propenyl ether, isobutyl vinyl ether, propyl vinyl ether,2-chloroethyl vinyl ether, 1,4-butanediol vinyl ether,1,4-cyclohexanedimethanol vinyl ether, di(ethylene glycol) vinyl ether,diethyl vinyl orthoformate, vinyl sulfide, vinyl halide, and vinylchloride.

In some aspects, the polyolefin can be derived from an alpha-olefin,such as 1-octene, 1-nonene, 1-decene, 1-undecene, 1-dodecene,1-tridecene, 1-tetradecene, 1-pentadecene, 1-hexadecene, 1-pentadecene,1-heptadecene, and 1-octadecene.

In various cases, the polyolefin segment containing R₇ can be derivedfrom a styrene. Suitable styrene monomers include styrene,α-bromostyrene, 2,4-diphenyl-4-methyl-1-pentene, α-methylstyrene,4-acetoxystyrene, 4-benzhydrylstyrene, 4-tert-butylstyrene,2,4-dimethylstyrene, 2,5-dimethylstyrene, 2-methylstyrene,3-methylstyrene, 4-methylstyrene, 2-(trifluoromethyl)styrene,3-(trifluoromethyl)styrene, 4-(trifluoromethyl)styrene,2,4,6-trimethylstyrene, vinylbenzyl chloride,4-benzyloxy-3-methoxystyrene, 4-tert-butoxystyrene,3,4-dimethoxystyrene, 4-ethoxystyrene, 4-vinylanisole, 2-bromostyrene,3-bromostyrene, 4-bromosytrene, 4-chloro-α-methylstyrene,2-chlorostyrene, 3-chlorostyrene, 4-chlorostyrene, 2,6-dichlorostyrene,2,6-difluorostyrene, 2-fluorostyrene, 3-fluorostyrene, 4-fluorostyrene,2,3,4,5,6-pentafluorostyrene, N,N-dimethylvinylbenzylamine,2-isopropenylaniline, 4-[N-(methylaminoethyl)aminomethyl]styrene,3-vinylaniline, 4-vinylaniline, (vinylbenzyl)trimethylammonium chloride,4-(diphenylphosphino)styrene, 3-isopropenyl-α,α-dimethylbenzylisocyanate, 3-nitrostyrene, 9-vinylanthracene, 2-vinylnaphthalene,4-vinylbenzocyclobutene, 4-vinylbiphenyl, and vinylbenzoic acid.

In some aspects, the polyolefin comprises a hydrophilic portion. Thehydrophilic portion of the polyolefin hydrogel can be pendant to thepolyolefin backbone, or the hydrophilic portion can function as acovalent crosslinker of the polyolefin hydrogel. In some aspects, thehydrophilic portion of the polyolefin hydrogel includes a pendantpolyether, polyester, polycarbonate, hydroxyl, lactone (e.g.,pyrrolidone), amino, carboxylate, sulfonate, phosphate, ammonium (e.g.,tertiary and quaternary ammonium), zwitterion group (e.g., a betaine,such as poly(carboxybetaine (pCB) and ammonium phosphonates such asphosphatidylcholine), or combinations thereof. Polyolefin hydrogelscontaining a pendant hydrophilic portion can be formed by copolymerizinga polyolefin monomer, as previously described, with a second polymerolefin monomer having a hydrophilic side chain, such as acrylic acid orpolyvinylpyrrolidone).

In some aspects, the polyolefin hydrogel includes a plurality ofpolyolefin chains wherein at least a portion of the polyolefin chainseach comprise a first chain segment physically crosslinked to at leastone other polyolefin chain of the plurality of polyolefin chains and oneor more hydrophilic chain segments covalently bonded to the first chainsegment.

In other aspects, the hydrophilic portion of the polyolefin hydrogel isa hydrophilic crosslinker. The crosslinker can include polyether,polyester, polycarbonate, hydroxyl, lactone (e.g., pyrrolidone), amino,carboxylate, sulfonate, phosphate, ammonium (e.g., tertiary andquaternary ammonium), a zwitterion (e.g., a betaine, such aspoly(carboxybetaine (pCB) and ammonium phosphonates such asphosphatidylcholine), and combinations thereof. The hydrophiliccrosslinker can be derived from a molecule having at least twoethylenically-unsaturated groups, such as a polyethylene glycoldimethacrylate.

Suitable commercially available polyolefin materials include, but arenot limited to the “POLYOX” product line by Dow Chemical, Midland Mich.,and styrenic block co-polymers. Examples of styrenic co-polymersinclude, but are not limited to TPE-s (e.g., styrene-butadiene-styrene(SBS) block copolymers, such as “SOFPRENE” andstyrene-ethylene-butylene-styrene (SEBS) block copolymer, such as“LAPRENE”, by SO.F.TER. GROUP, Lebanon, Tenn.); thermoplasticcopolyester elastomers (e.g., thermoplastic elastomer vulconates (TPE-vor TPV)), such as “FORPRENE” by SO.F.TER. GROUP), “TERMOTON-V” byTermopol, Istanbul Turkey; and TPE block copolymers, such as“SANTOPRENE” (ExxonMobil, Irving, Tex.).

In some aspects, the a monomer or prepolymer, such as the polyolefinprepolymer described above, is co-polymerized with a silicone prepolymerto form a silicone hydrogel. In these aspects, the silicone prepolymer,the polyolefin prepolymer, or both can function as the crosslinker.

Examples of silicone monomers include, but are not limited to,3-methacryloxypropyl tris(trimethylsiloxy)silane (TRIS), andmonomethacryloxypropyl terminated polydimethylsiloxane (mPDMS), mvinyl[3-[3,3,3-trimethyl-1,1bis(trimethylsiloxy)-disiloxanyl]propyl]carbamate,3-methacryloxypropyl-bis(trimethylsiloxy)methyl silane, andmethacryloxypropylpentamethyl disiloxane.

In other aspects, the hydrogel comprises or consists essentially of anionomeric hydrogel including a plurality of ionomer chains. An ionomeris a copolymer formed of both neutrally charged units and ionized unitsbonded to the polymer backbone, e.g., as pendant groups. Commonly theionized units include carboxylic acid groups. Synthesis of ionomerstypically includes the step of first introducing the ionized units(e.g., acid groups) into the polymer chain, and then neutralizing aportion of the ionized units (e.g., with a metal cation). The ionomercan comprise units of acrylic acid, methacrylic acid, or both. Theionomer can comprise a copolymer of ethylene and methacrylic acid.

As discussed above, the hydrogel-containing material can also optionallyinclude one or more additives, such as antioxidants, colorants,stabilizers, anti-static agents, wax packages, antiblocking agents,crystal nucleating agents, melt strength enhancers, anti-stain agents,stain blockers, hydrophilicity-enhancing additives, and combinationsthereof.

Examples of particularly suitable additives includehydrophilicity-enhancing additives, such as one or more super-absorbentpolymers (e.g., superabsorbent polyacrylic acid or copolymers thereof).Examples of hydrophilicity-enhancing additives include thosecommercially available under the tradenames “CREASORB” or “CREABLOCK” byEvonik, Mobile, Ala., “HYSORB” by BASF, Wyandotte, Mich., “WASTE LOCKPAM” by M² Polymer Technologies, Inc., Dundee Township, Ill., and “AQUAKEEP” by Sumitomo Seika, New York, N.Y. The incorporation of thehydrophilicity-enhancing additive can assist the hydrogel by increasingthe water uptake rate and/or capacity for the material. Examples ofsuitable concentrations of the hydrophilicity-enhancing additive in thematerial range from 0.1% to 15% by weight, from 0.5% to 10% by weight,or from 1% to 5% by weight, based on the total weight of the material.

In some aspects, the substrate body can be compositionally similar tothe hydrogel-containing material. The substrate body or backing layermay have a water uptake capacity of less than about 10% by weight, ascharacterized by the Water Uptake Test with the Article SamplingProcedure. The substrate body can compositionally contain or consistessentially of one or more polymers selected from the group consistingof an aliphatic thermoplastic polyurethane, an aliphatic polyamide, andcombinations thereof. The aliphatic polyamide comprises a caprolactamfunctional group and/or a nylon.

In some aspects, the hydrogel-containing material can define an exterioror ground-facing surface of the outsole. Alternatively, awater-permeable membrane can define the exterior or ground-facingsurface of the outsole, and can be in direct contact with the material.For example, at least a portion of the exterior surface of the outsolecan be defined by a first side of the water-permeable membrane, with thematerial present between the backing plate/outsole substrate and themembrane.

The level of water permeability of the water-permeable membrane ispreferably sufficient for water to rapidly partition from the exteriorsurface of the outsole (i.e., the first side of the membrane), acrossthe second side of the membrane, and into the material. For example, thelevel of water permeability of the water-permeable membrane can besufficient for a sample of the outsole obtained in accordance with theArticle Sampling Procedure to have a water uptake capacity of greaterthan 40% by weight at 24 hours. The level of water permeability of thewater-permeable membrane can be sufficient for a sample of the outsoleobtained in accordance with the Article Sampling Procedure to have awater uptake capacity of greater than 40% by weight at 1 hour.

The articles of the present disclosure can be manufactured using avariety of different manufacturing techniques. For example, the material(e.g., the hydrogel-containing material 116) and the optional backingplate or substrate body can be formed using methods such as injectionmolding, cast molding, thermoforming, vacuum forming, extrusion, spraycoating, and the like.

In some aspects, the outsole is formed with the use of a co-extrudedoutsole plate. In this case, the hydrogel-containing material can beco-extruded with a thermoplastic material used to form a thin backingsubstrate, where the resulting co-extruded material can be provided in aweb or sheet form. The web or sheet can then be placed in a vacuumthermoforming tool to produce the three-dimensional geometry of theoutsole ground-facing side (referred to as an outsole face precursor).The backing substrate provides a first function in this step by creatinga structural support for the relatively thinner and weaker material. Theoutsole face precursor can then be trimmed to form its perimeter andorifices to receive traction elements, thereby providing an outsoleface.

The outsole face can then be placed in a mold cavity, where the materialis preferably positioned away from the injection sprues. Anotherthermoplastic material can then be back injected into the mold to bondto the backing substrate, opposite of the material. This illustrates thesecond function of the backing substrate, namely to protect the materialfrom the injection pressure. The injected thermoplastic material can bethe same or different from the material used to produce the backingsubstrate. Preferably, they can include the same or similar materials(e.g., both being thermoplastic polyurethanes). As such, the backingsubstrate and the injected material in the mold form the outsole backingplate, which is secured to the material (during the co-extrusion step).

In other aspects, the outsole is formed with the use of injectionmolding. In this case, a substrate material is preferably injected intoa mold to produce the outsole backing plate. The outsole backing platecan then be back injected with the material to produce the materialbonded to the outsole backing plate.

In either of the above aspects, after the outsole is manufactured, itcan be directly or indirectly secured to a footwear upper (i.e., theupper portion of an article of footwear which typically forms a voidinto which a wearer's foot can be inserted during wear) to provide thearticle of footwear of the present disclosure. In particular, thematerial can function as a ground-facing surface of the outsole, whichis positioned on the opposite side of the outsole backing plate from theupper.

Property Analysis and Characterization Procedure

Various properties can be determined for the articles in accordance withthe present disclosure according to the following methodologies.

In some cases, the properties determined using these test methods may befrom samples of articles taken according to the Article SamplingProcedures. In other cases, the properties determined using these testmethods may be from samples of material taken according to theCo-extruded Film Sampling Procedure, the Neat Film Sampling Procedure,or the Neat Material Sampling Procedure. Regardless of whether the testwas conducted on a sample taken from an article or a sample of thehydrogel-containing material, the properties obtained by these tests areunderstood to be representative of the article of the presentdisclosure.

1. Sampling Procedures

As mentioned above, it has been found that when the hydrogel-containingmaterial is secured to another substrate (e.g. tie layer or substratebody), the interfacial bond can restrict the extent that thehydrogel-containing material can take up water and/or swell. As such,various properties of the hydrogel-containing material of the presentdisclosure can be characterized using samples prepared with thefollowing sampling procedures:

A. Article Sampling Procedure

This procedure can be used to obtain a sample of the hydrogel-containingmaterial from a component of an article or from the article itself. Thisprocedure may be used to obtain a sample of the hydrogel-containingmaterial when it is present on a component of an article (e.g., when thehydrogel-containing material is affixed to a substrate, or when thehydrogel-containing material is integrally formed in the component). Asample including the hydrogel-containing material in a non-wetted state(e.g., at 25° C. and 20% relative humidity) is cut from the component orarticle using a blade, or other suitable cutting instrument (e.g., saw,scissors, tin snips). Alternatively, the process may be performed byfirst separating the component of the article from an associatedcomponent of the article. The process is performed by separating thesample of the hydrogel-containing material from the remainder of thecomponent or article, and removing any other materials from the samplethat can uptake water and potentially skew the water uptake measurementsof the sample. For example, a sample surface can be skinned, abraded,scraped, or otherwise cleaned to remove any adhesives, yarns, fibers,foams, and the like that could potentially take up water themselves.Depending on the size, composition, and complexity of a particularcomponent or article, the entire component or article can constitute thesample. For example, components or articles having a small size, few orjust a single component, or that are composed largely or entirely of thehydrogel-containing material can be used directly as the sample.

The resulting sample includes the hydrogel-containing material and anysubstrate bonded thereto, and thus maintains the interfacial bondbetween the hydrogel-containing material and the associated substrate.As such, this test can simulate how the hydrogel-containing materialwill perform as part of a component or an article. Additionally, thissample is also useful in cases where the interfacial bond between thehydrogel-containing material and the substrate is less defined, such aswhere the hydrogel-containing material is highly diffused into thesubstrate (e.g., with a concentration gradient).

The sample is taken at a location on the component or article thatprovides a substantially constant thickness for the hydrogel-containingmaterial (within +/−10% of the average thickness), and has a surfacearea of 4 square centimeters (cm²). In cases where thehydrogel-containing material is not present on the substrate in anysegment having a 4 cm² surface area and/or where the material thicknessis not substantially constant for a segment having a 4 cm² surface area,sample sizes with smaller cross-sectional surface areas can be taken andthe area-specific measurements adjusted accordingly.

B. Co-Extruded Film Sampling Procedure

This procedure can be used to obtain a sample of hydrogel-containingmaterial when it is co-extruded onto a backing substrate. The backingsubstrate is produced from a second material that is compatible with thehydrogel-containing material.

It has been found that samples taken from co-extrusions are suitablesubstitutes to samples taken from components or articles. Additionally,this sample is also useful in cases where the interfacial bond betweenthe hydrogel-containing material and the backing substrate is lessdefined, such as where the hydrogel-containing material is highlydiffused into the material of the backing substrate (e.g., with aconcentration gradient).

In this case, the hydrogel-containing material is co-extruded with thebacking substrate as a web or sheet having a substantially constant filmthickness for the hydrogel-containing material (within +/−10% of theaverage thickness), and cooled to solidify the resulting web or sheet. Asample of the hydrogel-containing material secured to the backingsubstrate is then cut from the resulting web or sheet, with a samplesize surface area of 4 cm², such that the hydrogel-containing materialof the resulting sample remains secured to the backing substrate.

C. Neat Film Sampling Procedure

This procedure can be used to obtain a sample of the hydrogel-containingmaterial as a film when the hydrogel-containing material is isolated ina neat form (i.e., without any bonded substrate). In this case, thehydrogel-containing material is extruded as a web or sheet having asubstantially constant thickness for the hydrogel-containing material(within +/−10% of the average thickness), and cooled to solidify theresulting web or sheet. A sample of the hydrogel-containing materialhaving a surface area of 4 cm² is then cut from the resulting web orsheet.

Alternatively, if a source of the hydrogel-containing material is notavailable in a neat form, the hydrogel-containing material can be cutfrom a substrate of a component or an article, or from a backingsubstrate of a co-extruded sheet or web, thereby isolating thehydrogel-containing material. In either case, a sample of thehydrogel-containing material having a surface area of 4 cm² is then cutfrom the resulting isolated hydrogel-containing material.

D. Neat Material Sampling Procedure

This procedure can be used to obtain a sample of a hydrogel-containingmaterial used to form the hydrogel-containing material as a film. Inthis case, the hydrogel-containing material is provided in media form,such as flakes, granules, powders, pellets, and the like. If a source ofthe hydrogel-containing material is not available in a neat form, thematerial can be cut, scraped, or ground from a substrate, a component,or an article, or from a backing substrate of a co-extruded sheet orweb, thereby isolating the hydrogel-containing material.

2. Water Uptake Capacity Test

This test measures the water uptake capacity of the hydrogel-containingmaterial after a given soaking duration for a sample (e.g., taken withthe above-discussed Article Sampling Procedure, Co-extruded FilmSampling Procedure, or the Neat Film Sampling Procedure). The sample isinitially dried at 60° C. until there is no weight change forconsecutive measurement intervals of at least 30 minutes apart (e.g., a24-hour drying period at 60° C. is typically a suitable duration). Thetotal weight of the dried sample (Wt,_(sample,dry)) is then measured ingrams. The dried sample is then allowed to cool down to 25° C., and isfully immersed in a deionized water bath maintained at 25° C. After agiven soaking duration, the sample is removed from the deionized waterbath, blotted with a cloth to remove surface water, and the total weightof the soaked sample (Wt,_(sample,wet)) is measured in grams.

Any suitable soaking duration can be used, where a 24-hour soakingduration is believed to simulate saturation conditions for the materialof the present disclosure. Accordingly, as used herein, the expression“having a water uptake capacity at 5 minutes of . . . ” refers to asoaking duration of 5 minutes, having a water uptake capacity at 1 hourof . . . ” refers to a soaking duration of 1 hour, the expression“having a water uptake capacity at 24 hours of . . . ” refers to asoaking duration of 24 hours, and the like.

As can be appreciated, the total weight of a sample taken pursuant tothe Article Sampling Procedure or the Co-extruded Film SamplingProcedure includes the weight of the hydrogel-containing material asdried or soaked (Wt,_(film,dry) or Wt,_(film,wet)) and the weight of thebacking substrate (Wt,_(substrate)). In order to determine a change inweight of the hydrogel-containing material due to water uptake, theweight of the substrate (Wt,_(substrate)) needs to be subtracted fromthe sample measurements.

The weight of the substrate (Wt,_(substrate)) is calculated using thesample surface area (e.g., 4 cm²), an average measured thickness of thesubstrate in the sample, and the average density of the substratematerial. Alternatively, if the density of the material for thesubstrate is not known or obtainable, the weight of the substrate(Wt,_(substrate)) is determined by taking a second sample using the samesampling procedure as used for the primary sample, and having the samedimensions (surface area and film/substrate thicknesses) as the primarysample. The hydrogel-containing material of the second sample is thencut apart from the substrate of the second sample to provide an isolatedsubstrate. The isolated substrate is then dried at 60° C. for 24 hours,which can be performed at the same time as the primary sample drying.The weight of the isolated substrate (Wt,_(substrate)) is then measuredin grams.

The resulting substrate weight (Wt,_(substrate)) is then subtracted fromthe weights of the dried and soaked primary sample (Wt,_(sample,dry) andWt,_(sample,wet)) to provide the weights of the hydrogel-containingmaterial as dried and soaked (W,t_(film,dry) and Wt,_(film,wet)), asdepicted below by Equations 1 and 2:Wt, _(film,dry) =Wt, _(sample,dry) −Wt, _(substrate)   (Equation 1)Wt, _(film,wet) =Wt, _(sample,wet) −Wt, _(substrate)   (Equation 2)

For hydrogel-containing material samples taken pursuant to the Neat FilmSampling Procedure, the substrate weight (Wt,_(substrate)) is zero. Assuch, Equation 1 collapses to Wt,_(film,dry)=Wt,_(sample,dry), andEquation 2 collapses to Wt,_(film,wet)=Wt,_(sample,wet).

The weight of the dried hydrogel-containing material (Wt,_(film,dry)) isthen subtracted from the weight of the soaked hydrogel-containingmaterial (Wt,_(film,wet)) to provide the weight of water that was takenup by the hydrogel-containing material, which is then divided by theweight of the dried hydrogel-containing material (Wt,_(film,dry)) toprovide the water uptake capacity for the given soaking duration as apercentage, as depicted below by Equation 3:

$\begin{matrix}{{{{Water}\mspace{14mu}{Uptake}\mspace{14mu}{Capacity}} = {\frac{{Wt},_{{film},{wet}}{- {Wt}},_{{film},{dry}}}{{Wt},_{{film},{dry}}}( {100\%} )}}\mspace{76mu}{Asdf}} & ( {{Equation}\mspace{14mu} 3} )\end{matrix}$

For example, a water uptake capacity of 50% at 1 hour means that thesoaked hydrogel-containing material weighed 1.5 times more than itsdry-state weight after soaking for 1 hour, where there is a 1:2 weightratio of water to hydrogel-containing material. Similarly, a wateruptake capacity of 500% at 24 hours means that the soakedhydrogel-containing material weighed 5 times more than its dry-stateweight after soaking for 24 hours, where there is a 4:1 weight ratio ofwater to hydrogel-containing material.

3. Water Uptake Rate Test

This test measures the water uptake rate of the hydrogel-containingmaterial by modeling weight gain as a function of soaking time for asample with a one-dimensional diffusion model. The sample can be takenwith any of the above-discussed Article Sampling Procedure, Co-extrudedFilm Sampling Procedure, or the Neat Film Sampling Procedure. The sampleis initially dried at 60° C. until there is no weight change forconsecutive measurement intervals of at least 30 minutes apart (a24-hour drying period at 60° C. is typically a suitable duration). Thetotal weight of the dried sample (Wt,_(sample,dry)) is then measured ingrams. Additionally, the average thickness of the hydrogel-containingmaterial for the dried sample is measured for use in calculating thewater uptake rate, as explained below.

The dried sample is then allowed to cool down to 25° C., and is fullyimmersed in a deionized water bath maintained at 25° C. Between soakingdurations of 1, 2, 4, 9, 16, and 25 minutes, the sample is removed fromthe deionized water bath, blotted with a cloth to remove surface water,and the total weight of the soaked sample (Wt,_(sample,wet,t)) ismeasured, where “t” refers to the particular soaking-duration data point(e.g., 1, 2, 4, 9, 16, or 25 minutes).

The exposed surface area of the soaked sample (A_(t)) is also measuredwith calipers for determining the specific weight gain, as explainedbelow. The exposed surface area refers to the surface area that comesinto contact with the deionized water when fully immersed in the bath.For samples obtained using the Article Sampling Procedure and theCo-extruded Film Sampling Procedure, the samples only have one majorsurface exposed. However, for samples obtained using the Neat FilmSampling Procedure, both major surfaces are exposed. For convenience,the surface areas of the peripheral edges of the sample are ignored dueto their relatively small dimensions.

The measured sample is fully immersed back in the deionized water bathbetween measurements. The 1, 2, 4, 9, 16, and 25 minute durations referto cumulative soaking durations while the sample is fully immersed inthe deionized water bath (i.e., after the first minute of soaking andfirst measurement, the sample is returned to the bath for one moreminute of soaking before measuring at the 2-minute mark).

As discussed above in the Water Uptake Capacity Test, the total weightof a sample taken pursuant to the Article Sampling Procedure or theCo-extruded Film Sampling Procedure includes the weight of thehydrogel-containing material as dried or soaked (Wt,_(film,dry) orWt,_(film,wet,t)) and the weight of the backing substrate(Wt,_(substrate)). In order to determine a weight change of thehydrogel-containing material due to water uptake, the weight of thesubstrate (Wt,_(substrate)) needs to be subtracted from the sampleweight measurements. This can be accomplished using the same stepsdiscussed above in the Water Uptake Capacity Test to provide theresulting hydrogel-containing material weights Wt,_(film,dry) andWt,_(film,wet,t) for each soaking-duration measurement.

The specific weight gain (Ws,_(film,t)) from water uptake for eachsoaked sample is then calculated as the difference between the weight ofthe soaked sample (Wt,_(film,wet,t)) and the weight of the initial driedsample (Wt,_(film,dry)), where the resulting difference is then dividedby the exposed surface area of the soaked sample (A_(t)), as depictedbelow by Equation 4:

$\begin{matrix}{{Ws},_{{film},t}{- \;{= \frac{{Wt},_{{film},{wet},t}{- {Wt}},_{{film},{dry}}}{A_{t}}}}} & ( {{Equation}\mspace{14mu} 4} )\end{matrix}$where t refers to the particular soaking-duration data point (e.g., 1,2, 4, 9, 16, or 25 minutes), as mentioned above.

The water uptake rate for the hydrogel-containing material is thendetermined as the slope of the specific weight gains (Ws,_(film,t))versus the square root of time (in minutes), as determined by a leastsquares linear regression of the data points. For thehydrogel-containing material of the present disclosure, the plot of thespecific weight gains (Ws,_(film,t)) versus the square root of time (inminutes) provides an initial slope that is substantially linear (toprovide the water uptake rate by the linear regression analysis).However, after a period of time depending on the thickness of thehydrogel-containing material, the specific weight gains will slow down,indicating a reduction in the water uptake rate, until the saturatedstate is reached. This is believed to be due to the water beingsufficiently diffused throughout the hydrogel-containing material as thewater uptake approaches saturation, and will vary depending onthickness.

As such, for the hydrogel-containing material having an average driedthickness (as measured above) less than 0.3 millimeters, only thespecific weight gain data points at 1, 2, 4, and 9 minutes are used inthe linear regression analysis. In these cases, the data points at 16and 25 minutes can begin to significantly diverge from the linear slopedue to the water uptake approaching saturation, and are omitted from thelinear regression analysis. In comparison, for the hydrogel-containingmaterial having an average dried thickness (as measured above) of 0.3millimeters or more, the specific weight gain data points at 1, 2, 4, 9,16, and 25 minutes are used in the linear regression analysis. Theresulting slope defining the water uptake rate for the sampledhydrogel-containing material has units of weight/(surface area-squareroot of time), such as grams/(meter²-minutes^(1/2)).

Furthermore, some film or substrate surfaces can create surfacephenomenon that quickly attract and retain water molecules (e.g., viasurface hydrogen bonding or capillary action) without actually drawingthe water molecules into the film or substrate. Thus, samples of thesefilms or substrates can show rapid specific weight gains for the1-minute sample, and possibly for the 2-minute sample. After that,however, further weight gain is negligible. As such, the linearregression analysis is only applied if the specific weight gain datapoints at 1, 2, and 4 minutes continue to show an increase in wateruptake. If not, the water uptake rate under this test methodology isconsidered to be about zero grams/(meter²-minutes^(1/2)).

4. Swelling Capacity Test

This test measures the swelling capacity of the hydrogel-containingmaterial in terms of increases in thickness and volume after a givensoaking duration for a sample (e.g., taken with the above-discussedArticle Sampling Procedure, Co-extruded Film Sampling Procedure, or theNeat Film Sampling Procedure). The sample is initially dried at 60° C.until there is no weight change for consecutive measurement intervals ofat least 30 minutes apart (a 24-hour drying period is typically asuitable duration). The dimensions of the dried sample are then measured(e.g., thickness, length, and width for a rectangular sample; thicknessand diameter for a circular sample, etc. . . . ). The dried sample isthen fully immersed in a deionized water bath maintained at 25° C. Aftera given soaking duration, the sample is removed from the deionized waterbath, blotted with a cloth to remove surface water, and the samedimensions for the soaked sample are re-measured.

Any suitable soaking duration can be used. Accordingly, as used herein,the expressions “having a swelling thickness (or volume) increase at 5minutes of . . . ” refers to a soaking duration of 5 minutes, having aswelling thickness (or volume) increase at 1 hour of . . . ” refers to atest duration of 1 hour, the expression “having a swelling thickness (orvolume) increase at 24 hours of . . . ” refers to a test duration of 24hours, and the like.

The swelling of the hydrogel-containing material is determined by (i) anincrease in the thickness between the dried and soakedhydrogel-containing material, by (ii) an increase in the volume betweenthe dried and soaked hydrogel-containing material, or (iii) both. Theincrease in thickness between the dried and soaked hydrogel-containingmaterial is calculated by subtracting the measured thickness of theinitial dried hydrogel-containing material from the measured thicknessof the soaked hydrogel-containing material. Similarly, the increase involume between the dried and soaked hydrogel-containing material iscalculated by subtracting the measured volume of the initial driedhydrogel-containing material from the measured volume of the soakedhydrogel-containing material. The increases in the thickness and volumecan also be represented as percentage increases relative to the drythickness or volume, respectively.

5. Contact Angle Test

This test measures the contact angle of the hydrogel-containing materialsurface based on a static sessile drop contact angle measurement for asample (e.g., taken with the above-discussed Article Sampling Procedure,Co-extruded Film Sampling Procedure, or the Neat Film SamplingProcedure). The contact angle refers to the angle at which a liquidinterface meets a solid surface, and is an indicator of how hydrophilicthe surface is.

For a dry test (i.e., to determine a dry-state contact angle), thesample is initially equilibrated at 25° C. and 20% humidity for 24hours. For a wet test (i.e., to determine a wet-state contact angle),the sample is fully immersed in a deionized water bath maintained at 25°C. for 24 hours. After that, the sample is removed from the bath andblotted with a cloth to remove surface water, and clipped to a glassslide if needed to prevent curling.

The dry or wet sample is then placed on a moveable stage of a contactangle goniometer commercially available under the tradename “RAME-HARTF290” from Rame-Hart Instrument Co., Succasunna, N.J. A 10-microliterdroplet of deionized water is then placed on the sample using a syringeand automated pump. An image is then immediately taken of the droplet(before hydrogel-containing material can take up the droplet), and thecontact angle of both edges of the water droplet are measured from theimage. The decrease in contact angle between the dried and wet samplesis calculated by subtracting the measured contact angle of the wethydrogel-containing material from the measured contact angle of the dryhydrogel-containing material.

6. Coefficient of Friction Test

This test measures the coefficient of friction of thehydrogel-containing material surface for a sample (e.g., taken with theabove-discussed Article Sampling Procedure, Co-extruded Film SamplingProcedure, or the Neat Film Sampling Procedure). For a dry test (i.e.,to determine a dry-state coefficient of friction), the sample isinitially equilibrated at 25° C. and 20% humidity for 24 hours. For awet test (i.e., to determine a wet-state coefficient of friction), thesample is fully immersed in a deionized water bath maintained at 25° C.for 24 hours. After that, the sample is removed from the bath andblotted with a cloth to remove surface water.

The measurement is performed with an aluminum sled mounted on analuminum test track, which is used to perform a sliding friction testfor test sample on an aluminum surface of the test track. The test trackmeasures 127 millimeters wide by 610 millimeters long. The aluminum sledmeasures 76.2 millimeters×76.2 millimeters, with a 9.5 millimeter radiuscut into the leading edge. The contact area of the aluminum sled withthe track is 76.2 millimeters×66.6 millimeters, or 5,100 squaremillimeters).

The dry or wet sample is attached to the bottom of the sled using a roomtemperature-curing two-part epoxy adhesive commercially available underthe tradename “LOCTITE 608” from Henkel, Düsseldorf, Germany. Theadhesive is used to maintain the planarity of the wet sample, which cancurl when saturated. A polystyrene foam having a thickness of about 25.4millimeters is attached to the top surface of the sled (opposite of thetest sample) for structural support.

The sliding friction test is conducted using a screw-driven load frame.A tow cable is attached to the sled with a mount supported in thepolystyrene foam structural support, and is wrapped around a pulley todrag the sled across the aluminum test track. The sliding or frictionalforce is measured using a load transducer with a capacity of 2,000Newtons. The normal force is controlled by placing weights on top of thealuminum sled, supported by the polystyrene foam structural support, fora total sled weight of 20.9 kilograms (205 Newtons). The crosshead ofthe test frame is increased at a rate of 5 millimeters/second, and thetotal test displacement is 250 millimeters. The coefficient of frictionis calculated based on the steady-state force parallel to the directionof movement required to pull the sled at constant velocity. Thecoefficient of friction itself is found by dividing the steady-statepull force by the applied normal force. Any transient value relatingstatic coefficient of friction at the start of the test is ignored.

7. Storage Modulus Test

This test measures the resistance of the hydrogel-containing material tobeing deformed (ratio of stress to strain) when a vibratory oroscillating force is applied to it, and is a good indicator of filmcompliance in the dry and wet states. For this test, a sample isprovided in neat form using the Neat Film Sampling Procedure, which ismodified such that the surface area of the test sample is rectangularwith dimensions of 5.35 millimeters wide and 10 millimeters long. Thethickness can range from 0.1 millimeters to 2 millimeters, and thespecific range is not particularly limited as the end modulus result isnormalized according to thickness.

The storage modulus (E′) with units of megaPascals (MPa) of the sampleis determined by dynamic mechanical analysis (DMA) using a DMA analyzercommercially available under the tradename “Q800 DMA ANALYZER” from TAInstruments, New Castle, Del., which is equipped with a relativehumidity accessory to maintain the sample at constant temperature andrelative humidity during the analysis.

Initially, the thickness of the test sample is measured using calipers(for use in the modulus calculations). The test sample is then clampedinto the DMA analyzer, which is operated at the following stress/strainconditions during the analysis: isothermal temperature of 25° C.,frequency of 1 Hertz, strain amplitude of 10 micrometers, preload of 1Newton, and force track of 125%. The DMA analysis is performed at aconstant 25° C. temperature according to the following time/relativehumidity (RH) profile: (i) 0% RH for 300 minutes (representing the drystate for storage modulus determination), (ii) 50% RH for 600 minutes,(iii) 90% RH for 600 minutes (representing the wet state for storagemodulus determination), and (iv) 0% RH for 600 minutes.

The E′ value (in MPa) is determined from the DMA curve according tostandard DMA techniques at the end of each time segment with a constantRH value. Namely, the E′ value at 0% RH (i.e., the dry-state storagemodulus) is the value at the end of step (i), the E′ value at 50% RH isthe value at the end of step (ii), and the E′ value at 90% RH (i.e., thewet-state storage modulus) is the value at the end of step (iii) in thespecified time/relative humidity profile.

The hydrogel-containing material can be characterized by its dry-statestorage modulus, its wet-state storage modulus, or the reduction instorage modulus between the dry-state and wet-state, where wet-statestorage modulus is less than the dry-state storage modulus. Thisreduction in storage modulus can be listed as a difference between thedry-state storage modulus and the wet-state storage modulus, or as apercentage change relative to the dry-state storage modulus.

8. Glass Transition Temperature Test

This test measures the glass transition temperature (T_(g)) of thehydrogel-containing material for a sample, where the hydrogel-containingmaterial is provided in neat form, such as with the Neat Film SamplingProcedure or the Neat Material Sampling Procedure, with a 10-milligramsample weight. The sample is measured in both a dry state and a wetstate (i.e., after exposure to a humid environment as described herein).

The glass transition temperature is determined with DMA using a DMAanalyzer commercially available under the tradename “Q2000 DMA ANALYZER”from TA Instruments, New Castle, Del., which is equipped with aluminumhermetic pans with pinhole lids, and the sample chamber is purged with50 milliliters/minute of nitrogen gas during analysis. Samples in thedry state are prepared by holding at 0% RH until constant weight (lessthan 0.01% weight change over 120 minute period). Samples in the wetstate are prepared by conditioning at a constant 25° C. according to thefollowing time/relative humidity (RH) profile: (i) 250 minutes at 0% RH,(ii) 250 minutes at 50% RH, and (iii) 1,440 minutes at 90% RH. Step(iii) of the conditioning program can be terminated early if sampleweight is measured during conditioning and is measured to besubstantially constant within 0.05% during an interval of 100 minutes.

After the sample is prepared in either the dry or wet state, it isanalyzed by DSC to provide a heat flow versus temperature curve. The DSCanalysis is performed with the following time/temperature profile: (i)equilibrate at −90° C. for 2 minutes, (ii) ramp at +10° C./minute to250° C., (iii) ramp at −50° C./minute to −90° C., and (iv) ramp at +10°C./minute to 250° C. The glass transition temperature value (in Celsius)is determined from the DSC curve according to standard DSC techniques.

9. Impact Energy Test

This test measures the ability of a hydrogel-containing material sampleto shed soil under particular test conditions, where the sample isprepared using the Co-extruded Film Sampling Procedure or the Neat FilmSampling Procedure (to obtain a suitable sample surface area).Initially, the sample is fully immersed in a water bath maintained at25° C. for 24 hours), and then removed from the bath and blotted with acloth to remove surface water.

The saturated test sample is then adhered to an aluminum block having a25.4-millimeter thickness and a 76.2 millimeters×76.2 millimeterssurface area, using a room temperature-curing two-part epoxy adhesivecommercially available under the tradename “LOCTITE 608” from Henkel,Düsseldorf, Germany. The adhesive is used to maintain the planarity ofthe soaked sample, which can curl when saturated.

To expose the sample to soil, a bed of soil of about 75 millimeters inheight is placed on top of a flat plastic plate. The soil iscommercially available under the tradename “TIMBERLINE TOP SOIL”, model50051562, from Timberline (subsidiary of Old Castle, Inc., Atlanta, Ga.)and was sifted with a square mesh with a pore dimension of 1.5millimeter on each side. The sample is then compressed into the soilunder body weight. The weight is removed from the sample, and the sampleis then twisted by 90 degrees in the plane of the plate and then liftedvertically. If no soil clogs the sample, no further testing isconducted.

However, if soil does clog the sample, the soil is knocked loose bydropping a 25.4-millimeter diameter steel ball weighing 67 grams ontothe top side of the aluminum block (opposite of the test sample andclogged soil). The initial drop height is 152 millimeters (6 inches)above the aluminum block. If the soil does not come loose, the ball dropheight is increased by an additional 152 millimeters (6 inches) anddropped again. This procedure of increasing the ball drop height by 152millimeter (6 inch) increments is repeated until the soil on the bottomof the aluminum block (i.e., on the sample) is knocked loose.

This test is run 10 times per test sample. For each run, the ball dropheight can be converted into unclogging impact energy by multiplying theball drop height by the ball mass (67 grams) and the acceleration ofgravity (9.8 meters/second²). The unclogging impact energy in Joulesequals the ball drop height in inches multiplied by 0.0167. Theprocedure is performed on both the aluminum block with thehydrogel-containing material sample and a control aluminum block withoutthe hydrogel-containing material, and the relative ball drop height, andtherefore relative impact energy, is determined as the ball drop heightfor the aluminum block with the hydrogel-containing material sampledivided by the control aluminum block without the hydrogel-containingmaterial. A result of zero for the relative ball drop height (orrelative impact energy) indicates that no soil clogged to the aluminumblock initially when the sample was compressed into the test soil (i.e.,in which case the ball drop and control portions of the test areomitted).

10. Soil Shedding Article Test

This test measures the mud shedding ability of a component or anarticle, and does not require any sampling procedure. Initially, thecomponent or article is fully immersed in a water bath maintained at 25°C. for 20 minutes), and then removed from the bath and blotted with acloth to remove surface water, and its initial weight is measured.

The soaked component/article is then placed on a support and positionedas the article is positioned during normal use. The component or articleis then exposed to test soil in a manner which approximates the mannerin which the component or article is exposed to mud or dirt duringnormal use. Soil is sprayed at the article. The amount and velocity ofthe soil are selected to approximate the conditions which the componentor article would be exposed to during normal use. The test soil iscommercially available under the tradename “TIMBERLINE TOP SOIL”, model50051562, from Timberline (subsidiary of Old Castle, Inc., Atlanta,Ga.), and the moisture content is adjusted so that the shear strengthvalue is between 3 and 4 kilograms/cm² on a shear vane tester availablefrom Test Mark Industries (East Palestine, Ohio.

After the test is complete, the component/article is carefully removedfrom the support and its post-test weight is measured. The differencebetween the post-test weight and the initial weight of the component orarticle, due to soil accumulation, is then determined.

Although the present disclosure has been described with reference toparticular examples, workers skilled in the art will recognize thatchanges may be made in form and detail without departing from the spiritand scope of the disclosure.

EXAMPLES

The present disclosure is more particularly described in the followingexamples that are intended as illustrations only, since numerousmodifications and variations within the scope of the present disclosurewill be apparent to those skilled in the art. Unless otherwise noted,all parts, percentages, and ratios reported in the following examplesare on a weight basis, and all reagents used in the examples wereobtained, or are available, from the chemical suppliers described below,or may be synthesized by conventional techniques.

1. Footwear Outsole Water Uptake Analysis

Test samples for Examples 1-5 were measured for water uptake capacitiesover multiple soaking durations. Each test sample was taken from aglobal football/soccer shoe outsole having an outsole of the presentdisclosure. Each outsole was initially manufactured by co-extruding thehydrogel-containing material with a substrate body having a substratethickness of 0.4 millimeters, where the substrate body material was anaromatic thermoplastic polyurethane commercially available under thetradename “ESTANE 2103-87AE” from Lubrizol Corporation, Wickliffe, Ohio.

For Examples 1-3, the hydrogel-containing material was a thermoplasticpolyurethane hydrogel commercially available under the tradename“TECOPHILIC TG-500” from the Lubrizol Corporation, Wickliffe, Ohio,which included copolymer chains having aliphatic hard segments andhydrophilic soft segments (with polyether chains). For Examples 4 and 5,the hydrogel-containing material was a lower-water-uptake thermoplasticpolyurethane hydrogel commercially available under the tradename“TECOPHILIC HP-60D-60” from the Lubrizol Corporation, Wickliffe, Ohio.

For each example, the resulting co-extruded web was then sheeted, vacuumthermoformed, and trimmed to dimensions for an outsole face. The outsoleface was then back injected with another thermoplastic polyurethanecommercially available under the tradename “DESMOPAN DP 8795 A” fromBayer MaterialScience AG, Leverkusen, Germany to produce the outsolehaving the hydrogel-containing material defining the ground-facingsurface, and the extruded substrate body and back-injected materialcollectively forming the outsole backing plate. Footwear uppers werethen adhered to the top sides of the produced outsoles to provide thearticle of footwear.

Test samples for each example were then taken as described above in theArticle Sampling Procedure, with the exception of the sample sizesdescribed below. In particular, annular test samples including thehydrogel-containing material and the outsole backing plate were cut outof the footwear. This was performed by initially cutting off the upperfrom the outsole near the biteline where the outsole and upper meet.

A small guide hole in the center of the sample was then created(creating an inner diameter for the sample) to assist in cutting theannular sample with the desired outer diameter. All removable layersremaining on the top side of the outsole backing plate after cuttingwere peeled away from the test samples, including the sockliner,strobel, and insole board, while some residual adhesive remained on thesample. Each sample was taken from a central location in its respectiveregion (i.e., near a longitudinal midline) and generally in-between thecleats.

Test samples for Examples 1-3 were respectively taken from the forefootregion, the midfoot region, and the heel region of the outsole. Testsamples for Examples 4 and 5 were respectively taken from the forefootregion and the midfoot region. Each sample was taken from a centrallocation in its respective region (i.e., near a longitudinal midline)and generally in-between the cleats.

For comparison purposes, outsole samples were also taken from a globalfootball/soccer footwear having a thermoplastic polyurethanecommercially available under the tradename “DESMOPAN DP 8795 A” fromBayer MaterialScience AG, Leverkusen, Germany; where the outsoles didnot include any hydrogel-containing material of the present disclosure.For Comparative Example A, an annular test sample was taken from theforefoot region of the outsole using the same technique as discussedabove for Examples 1-5. For Comparative Example B, a rectangular testsample was taken from the midfoot region of the outsole. Each sample wastaken from a central location in its respective region (i.e., near alongitudinal midline) and generally in-between the cleats.

The material thickness, outsole thickness, surface area, and materialvolume of each test sample was then measured and calculated. The wateruptake capacity for each test sample was then measured for differentsoaking durations, pursuant to the Water Uptake Capacity Test. Aftereach soaking duration, the total sample weight was recorded, and thewater uptake weight for each soaking duration was calculated bysubtracting out the dry sample weight from the given recorded totalsample weight.

The material weight was also calculated for each soaking duration bysubtracting out the weight of the sample outsole substrate, as describedin the Water Uptake Capacity Test. The outsole substrate weight wasdetermined by calculating its volume (from the outsole thickness andsurface area) and using the known density of the outsole backing platematerial. The water uptake capacity was then calculated for each soakingduration, as also described in the Water Uptake Capacity Test. Tables1A-1G shown below list the total sample weights, the water uptakeweights, the material weights, and the water uptake capacities for thetest samples of Examples 1-5 and Comparative Examples A and B overdifferent soaking durations.

TABLE 1A Total Uptaken Soak Sample Water Material Water Time WeightWeight Weight Uptake Sample (minutes) (grams) (grams) (grams) CapacityExample 1 0 1.54 0.00 0.64  0% Example 1 2 1.72 0.18 0.77  28% Example 15 1.75 0.21 0.84  33% Example 1 10 1.84 0.30 0.90  47% Example 1 30 2.010.47 1.10  74% Example 1 60 2.18 0.64 1.22 101%

TABLE 1B Total Uptaken Soak Sample Water Material Water Time WeightWeight Weight Uptake Sample (minutes) (grams) (grams) (grams) CapacityExample 2 0 1.50 0.00 0.51  0% Example 2 2 1.68 0.18 0.67  35% Example 25 1.75 0.25 0.73  49% Example 2 10 1.84 0.34 1.04  66% Example 2 30 2.150.65 1.33 127% Example 2 60 2.40 0.90 1.49 176%

TABLE 1C Total Uptaken Soak Sample Water Material Water Time WeightWeight Weight Uptake Sample (minutes) (grams) (grams) (grams) CapacityExample 3 0 1.21 0.00 0.46  0% Example 3 2 1.36 0.15 0.51  32% Example 35 1.44 0.23 0.72  50% Example 3 10 1.52 0.31 0.88  67% Example 3 30 1.630.42 0.79  91% Example 3 60 1.80 0.59 1.12 127% Example 3 180 2.15 0.941.58 203% Example 3 300 2.30 1.09 1.72 235% Example 3 1260 2.57 1.361.93 294%

TABLE 1D Total Uptaken Soak Sample Water Material Water Time WeightWeight Weight Uptake Sample (minutes) (grams) (grams) (grams) CapacityExample 4 0 1.06 0.00 0.18  0% Example 4 2 1.08 0.02 0.31 11% Example 45 1.11 0.05 0.35 28% Example 4 10 1.06 0.00 0.34  0% Example 4 30 1.110.05 0.28 28% Example 4 60 1.12 0.06 0.41 33% Example 4 180 1.14 0.080.38 44% Example 4 300 1.10 0.04 0.38 22% Example 4 1260 1.10 0.04 0.3622%

TABLE 1E Total Uptaken Soak Sample Water Material Water Time WeightWeight Weight Uptake Sample (minutes) (grams) (grams) (grams) CapacityExample 5 0 1.14 0.00 0.21  0% Example 5 2 1.17 0.03 0.21 61% Example 55 1.07 −0.07  0.24  6% Example 5 10 1.19 0.05 0.26 72% Example 5 30 1.180.04 0.26 66% Example 5 60 1.19 0.05 0.27 72% Example 5 180 1.20 0.060.29 77% Example 5 300 1.19 0.05 0.36 72% Example 5 1260 1.20 0.06 0.2477%

TABLE 1F Soak Time Total Sample Uptaken Water Sample (minutes) Weight(grams) Weight (grams) Comparative Example A 0 1.26 0.00 ComparativeExample A 2 1.60 0.34 Comparative Example A 5 1.62 0.36 ComparativeExample A 10 1.56 0.30 Comparative Example A 30 1.62 0.36 ComparativeExample A 60 1.57 0.31 Comparative Example B 0 1.05 0.00 ComparativeExample B 2 1.05 0.00 Comparative Example B 5 1.05 0.00 ComparativeExample B 10 1.05 0.00 Comparative Example B 30 1.05 0.00 ComparativeExample B 60 1.05 0.00 Comparative Example B 180 1.06 0.01 ComparativeExample B 300 1.05 0.00 Comparative Example B 1260 1.06 0.01

As shown in Tables 1A-1C, there is significant change in the weight ofthe samples for Example 1-3, which was believed to be due to the highabsorbance of the material. The samples of Examples 4 and 5 were basedon a lower-absorbent material and used a thinner application whencompared to Examples 1-3. Both of these differences lead to lessresolution in the measurement, although the uptake percent (˜50% averagefor the two samples) is measurable. This illustrates how the wateruptake of a hydrogel-containing material is dependent on the wateruptake properties of the material as well as the material thickness.

In comparison, the samples of Comparative Examples A and B demonstratedthe lack of water uptake for the non-hydrogel thermoplastic. Inparticular, the sample of Comparative Example A only showed a change inweight at the first time point, but no subsequent change. This isbelieved to be due to surface phenomenon of the sample (e.g., capillaryaction) rather than water uptake into the outsole. In particular, thebacking layer for Comparative Example A was rough (i.e., has microporesunrelated to the polymer chemistry) and fibers associated with shoeconstruction adhered to the backing layer that were not fully removedduring sample preparation. On the other hand, the sample of ComparativeExample B had a smooth outsole surface and all potential contaminantsare removed.

Examples 1-3 of a material comprising a hydrogel all had average wateruptake capacities at 1 hour of greater than 40% by weight. In fact, thehydrogel-containing material had average water uptake capacities at 1hour of greater than 80% by weight. Examples 4 and 5 of a differentmaterial comprising a hydrogel had average water uptake capacities at180 minutes of greater than 40% by weight. In comparison, thecomparative samples of non-hydrogel materials had average water uptakecapacities at 24 hours of less than 1% by weight.

In addition to the water uptake capacities, the test samples of Examples1-5 and Comparative Examples A and B were measured for thickness andvolumetric swelling, pursuant to the Swelling Capacity Test, over thesame soaking durations referred to above. Tables 2A-2G list the measuredsurface areas and material thicknesses, and the calculated materialvolumes for the test samples, and Tables 3A-3E list the materialthickness increase, the percentage material thickness increase, thematerial volume increase, the percentage material volume increase.

TABLE 2A Soak Surface Sample Material Material Time Area Thicknessthickness volume Sample (minutes) (mm²) (mm) (mm) (mm³) Example 1 0 3803.66 1.44 548 Example 1 2 379 3.75 1.75 664 Example 1 5 410 3.75 1.77726 Example 1 10 410 3.90 1.90 779 Example 1 30 451 4.18 2.11 951Example 1 60 481 4.34 2.18 1049

TABLE 2B Soak Surface Sample Material Material Time Area Thicknessthickness volume Sample (minutes) (mm²) (mm) (mm) (mm³) Example 2 0 4213.50 1.05 442 Example 2 2 415 3.70 1.40 582 Example 2 5 436 4.22 1.45633 Example 2 10 472 4.20 1.90 897 Example 2 30 561 4.15 2.05 1150Example 2 60 612 4.18 2.10 1285

TABLE 2C Soak Surface Sample Material Material Time Area Thicknessthickness volume Sample (minutes) (mm²) (mm) (mm) (mm³) Example 3 0 3472.95 1.15 399 Example 3 2 347 3.08 1.28 444 Example 3 5 369 3.46 1.68620 Example 3 10 399 3.58 1.89 755 Example 3 30 404 3.70 1.68 678Example 3 60 449 3.75 2.15 964 Example 3 180 513 4.00 2.65 1359 Example3 300 530 4.18 2.80 1485 Example 3 1260 581 4.35 2.87 1667

TABLE 2D Soak Surface Sample Material Material Time Area Thicknessthickness volume Sample (minutes) (mm²) (mm) (mm) (mm³) Example 4 0 3632.41 0.43 156 Example 4 2 366 2.56 0.73 267 Example 4 5 372 2.57 0.80298 Example 4 10 371 2.47 0.78 290 Example 4 30 374 2.47 0.65 243Example 4 60 379 2.55 0.93 352 Example 4 180 373 2.55 0.87 324 Example 4300 386 2.53 0.85 328 Example 4 1260 379 2.40 0.81 307

TABLE 2E Sample Material Material Soak Time Surface Area Thicknessthickness volume Sample (minutes) (mm²) (mm) (mm) (mm³) Example 5 0 3782.42 0.47 178 Example 5 2 377 2.50 0.48 181 Example 5 5 386 2.50 0.54208 Example 5 10 385 2.52 0.58 223 Example 5 30 384 2.53 0.59 227Example 5 60 388 2.50 0.59 229 Example 5 180 389 2.57 0.65 253 Example 5300 394 2.57 0.78 307 Example 5 1260 388 2.55 0.54 209

TABLE 2F Sample Soak Time Surface Area Thickness Sample (minutes) (mm²)(mm) Comparative 0 405 2.90 Example A Comparative 2 417 2.90 Example AComparative 5 425 3.15 Example A Comparative 10 407 2.77 Example AComparative 30 416 2.77 Example A Comparative 60 426 2.87 Example A

TABLE 2G Sample Soak Time Surface Area Thickness Sample (minutes) (mm²)(mm) Comparative 0 501 1.77 Example B Comparative 2 500 1.77 Example BComparative 5 502 1.77 Example B Comparative 10 503 1.75 Example BComparative 30 503 1.75 Example B Comparative 60 496 1.73 Example BComparative 180 499 1.73 Example B Comparative 300 503 1.74 Example BComparative 1260 501 1.73 Example B

TABLE 3A Material Percent Material Percent thickness Material volumeMaterial Soak Time Increase thickness Increase volume Sample (minutes)(mm) Increase (mm) Increase Example 1 0 0  0% 0  0% Example 1 2 0.31 22%116 21% Example 1 5 0.33 23% 178 33% Example 1 10 0.46 32% 231 42%Example 1 30 0.67 47% 403 74% Example 1 60 0.74 51% 501 92%

TABLE 3B Material Percent Material Percent thickness Material volumeMaterial Soak Time Increase thickness Increase volume Sample (minutes)(mm) Increase (mm) Increase Example 2 0 0  0% 0  0% Example 2 2 0.35 33%140  32% Example 2 5 0.40 38% 191  43% Example 2 10 0.85 81% 455 103%Example 2 30 1.00 95% 708 160% Example 2 60 1.05 100%  843 191%

TABLE 3C Material Percent Material Percent thickness Material volumeMaterial Soak Time Increase thickness Increase volume Sample (minutes)(mm) Increase (mm) Increase Example 3 0 0  0% 0  0% Example 3 2 0.13 11%45 11% Example 3 5 0.53 46% 221 55% Example 3 10 0.74 64% 356 89%Example 3 30 0.53 46% 279 70% Example 3 60 1.00 87% 565 142%  Example 3180 1.50 130%  960 240%  Example 3 300 1.65 143%  1086 272%  Example 31260 1.72 150%  1268 318% 

TABLE 3D Material Percent Material Percent thickness Material volumeMaterial Soak Time Increase thickness Increase volume Sample (minutes)(mm) Increase (mm) Increase Example 4 0 0  0% 0  0% Example 4 2 0.30 70%111 71% Example 4 5 0.37 86% 142 91% Example 4 10 0.35 81% 134 85%Example 4 30 0.22 51% 87 56% Example 4 60 0.50 116%  196 125%  Example 4180 0.44 102%  168 107%  Example 4 300 0.42 98% 172 110%  Example 4 12600.38 88% 151 96%

TABLE 3E Material Percent Material Percent thickness Material volumeMaterial Soak Time Increase thickness Increase volume Sample (minutes)(mm) Increase (mm) Increase Example 5 0 0  0% 0  0% Example 5 2 0.01  2%3  2% Example 5 5 0.07 15% 30 17% Example 5 10 0.11 23% 45 26% Example 530 0.12 26% 49 28% Example 5 60 0.12 26% 51 29% Example 5 180 0.18 38%75 42% Example 5 300 0.31 66% 129 73% Example 5 1260 0.07 15% 31 18%

As can be seen in Tables 2A-2G and 3A-3E, the samples of Examples 1-5all show significant changes in both thickness and volume upon wateruptake. The thickness and volume change is even resolved for Examples 3and 4, where the water uptake test showed less change. The samples forComparative Examples A and B, however, did not show any change inthickness or volume. Even when Comparative Example A showed a change inweight, as discussed above, there was no corresponding thickness changebecause the uptaken water was not acting to swell the samples, as is thecase for Examples 1-5.

For Examples 1-5 of materials comprising a hydrogel, thehydrogel-containing materials had an average swell thickness increase at1 hour of greater than 20%. In fact, the hydrogel-containing material ofExamples 1-3 had an average swell thickness increase at 1 hour ofgreater than 75%. In comparison, the comparator non-hydrogel materialsdid not increase in thickness.

2. Material Water Uptake Capacity

Various samples of hydrogel-containing materials for Examples 6-18 werealso tested to determine their uptake capacities at 1 hour and 24 hours,pursuant to the Water Uptake Capacity Test with either the Co-ExtrudedFilm Sampling Procedure (co-extruded form) or the Neat Film SamplingProcedure (neat film form). For the co-extruded forms, the backingsubstrate was a thermoplastic polyurethane commercially available underthe tradename “DESMOPAN DP 8795 A” from Bayer MaterialScience AG,Leverkusen, Germany.

The hydrogel-containing material for Examples 6-8 was a thermoplasticpolyurethane hydrogel commercially available under the tradename“TECOPHILIC TG-500” from the Lubrizol Corporation, Wickliffe, Ohio (samematerial as for Examples 1-3). For Example 6, the material was in neatfilm form with a 0.25-millimeter material thickness. For Example 7, thematerial was in a co-extruded form with a 0.13-millimeter materialthickness. For Example 8, the material was also in a co-extruded filmform, but with a 0.25-millimeter material thickness.

The material for Examples 9 and 10 was a lower-water-uptakethermoplastic polyurethane hydrogel commercially available under thetradename “TECOPHILIC HP-60D-60” from the Lubrizol Corporation,Wickliffe, Ohio (same as for Examples 4 and 5). For Example 9, thematerial was in a co-extruded film form with a 0.25-millimeter materialthickness. For Example 10, the material was in a neat film form with a0.13-millimeter material thickness.

The hydrogel-containing material for Example 11 was a thermoplasticpolyurethane hydrogel commercially available under the tradename“TECOPHILIC TG-2000” from the Lubrizol Corporation, Wickliffe, Ohio,where the material was in a neat film form with a 0.13-millimetermaterial thickness. The hydrogel-containing material of Example 12 was athermoplastic polyurethane hydrogel commercially available under thetradename “TECOPHILIC HP-93A-100” from the Lubrizol Corporation,Wickliffe, Ohio, where the material was in a co-extruded film form witha 0.13-millimeter material thickness.

The hydrogel-containing materials for Examples 13-17 were alsothermoplastic polyurethane hydrogels derived from chain-extended TDIisocyanates and polyether glycols, where the polyether glycolconcentrations were varied to adjust the water uptake capacities. Forthese examples, the hydrogel-containing materials were pressed intothick neat films having 3-millimeter material thicknesses.

The hydrogel-containing material for Example 18 was a thermoplasticpolyamide-polyether block copolymer hydrogel commercially availableunder the tradename “PEBAX MH1657” from Arkema, Inc., Clear Lake, Tex.,where the material was in a neat film form with a 0.13-millimetermaterial thickness. Table 4 lists the water uptake capacities for thesamples of Examples 6-18.

TABLE 4 Water Uptake Water Uptake Capacity Capacity Sample (1 hour) (24hours) Example 6 341%  468% Example 7 260%  — Example 8 153%  168%Example 9 —  44% Example 10 29%  80% Example 11 415%  900% Example 1244% — Example 13 55% 238% Example 14 60% 250% Example 15 35% 184%Example 16 40% 167% Example 17 15%  69% Example 18 116%  100%

As shown, Examples 6-8 in Table 4 demonstrate the effects ofconstraining the material to a co-extruded backing substrate. Examples 9and 10 demonstrate the same effects with a lower uptake material.Example 11 is a neat film with relatively high water uptake, whileExample 12 is a coextruded form of a neat resin that has a water uptakecapacity in-between those of Examples 6 and 10. Examples 13-17 alsoexhibited good water uptakes, and included considerably thickermaterials (by about a factor of 10).

All of the materials of Examples 6-18 comprise a hydrogel. Examples 6,8, 9, 10, 11, 13, 14, 15, 16, 17 and 18 were all found to have wateruptake capacities of 40% or greater a 1 hour. Examples 6, 7, 8, 11, and18 were found to have water uptake capacities of greater than 100% at 1hour. Examples 6, 7, 8, 11, 13, 14, 16, and 18 were found to have wateruptake capacities of greater than 40% at 24 hours. Examples 6, 8, 11,13, 14, 15, 16, and 18 were found to have water uptake capacities of atleast 100% at 24 hours.

3. Material Water Uptake Rate and Swelling

Several samples (for Examples 1, 4, 6-8, and 10-12) were also tested todetermine their water uptake rates and swell capacities, pursuant to theWater Uptake Rate Test and the Swell Capacity Test. Table 5 lists thetest results for the samples of Examples 1, 4, 6-8, and 10-12.

TABLE 5 Percent Percent Material Material thickness volume Water UptakeRate Increase Increase Sample (grams/m²-minutes^(1/2)) (1 hour) (1 hour)Example 1 235 73% 130%  Example 4 58 72% 75% Example 6 752 89% 117% Example 7 173 318%  64% Example 8 567 177%  77% Example 10 33 43% 88%Example 11 1270 69% 92% Example 12 172 153%  70%

As shown, the tested samples exhibited varying water uptake rates, wherethe samples having higher water uptake capacities (from Table 4) andthat were in neat form exhibited faster water uptake rates. Moreover,the swelling thickness and volume increases shown in Table 5 generallycorresponded to the water uptake capacities shown above in Table 4.

Examples 1, 4, 6, 7, 8, 10, 11 and 12 were found to have water uptakerates of greater than 20 grams/m²-minutes^(1/2). Examples 1, 6, 7, 8, 11and 12 were found to have water uptake rates of greater than 150grams/m²-minutes^(1/2). Examples 1, 4, 6, 7, 8, 10, 11 and 12 were foundto have swell thickness increases of greater than 20% at 1 hour. Infact, Examples 1, 4, 6, 7, 8, 10, 11 and 12 were found to have swellthickness increases of greater than 40% at 1 hour, and Examples 1, 4, 6,7, 8, 11 and 12 were found to have swell thickness increases of greaterthan 60% at 1 hour. Examples 1, 4, 6, 7, 8, 10, 11 and 12 were found tohave swell volume increases of at least 70%.

4. Material Contact Angle

The samples for Examples 6, 7, 10-12, and 18 were also tested todetermine their dry-state and wet-state contact angles, pursuant to theContact Angle Test. Table 6 below lists the corresponding dry and wetstatic sessile drop contact angles with their variations, as well as thedifference in contact angle between the dry and wet measurements.

TABLE 6 Average Average Dry Dry Wet Wet Material Material MaterialMaterial Contact Contact Contact Contact Contact Angle Angle Angle AngleAngle Differ- Sample (degrees) (std dev) (degrees) (std dev) enceExample 6 87.6 2.6 66.9 4.9 20.7 Example 7 86.6 1.1 57.4 5.5 29.2Example 10 95.6 3.2 72.5 2.5 23.1 Example 11 79.5 2.4 64.7 2.3 14.8Example 12 97.1 2.5 95.5 4.7 1.7 Example 18 66.2 5.0 52.0 3.7 14.2

The samples of Examples 6 and 7 show that there is no difference incontact angles between a neat film and the co-extruded film at therelevant thicknesses because contact angle is a surface property. Thesamples of Examples 10 and 11 show that a higher contact angle isgenerally present on a lower water uptake material (Example 10) comparedto a high water uptake material (Example 11) The sample of Example 18,based on polyamide copolymer chemistry, demonstrates that the basechemistry can affect the dry contact angle. However, in all cases, asubstantial reduction in contact angle is seen for wet materials whencompared to dry samples. As can be appreciated from the discussionherein, a low wet state contact angle, or a decrease in contact anglefrom dry state to wet state, or both, can be predictive of outsoles andmaterials which can effectively prevent or reduce accumulation of soil.

Examples 6, 7, 10, 11 and 18 had wet-state static sessile drop contactangles of less than 80 degrees. Examples 6, 7, 11 and 18 had wet-statestatic sessile drop contact angles of less than 70 degrees. Examples 6,7, 10, 11, and 18 had a drop in static sessile drop contact angle fromthe dry state to the wet state of at least 10 degrees. Examples 6, 7,10, and 11 had a drop in static sessile drop contact angle from the drystate to the wet state of at least 20 degrees.

5. Material Coefficient of Friction

The samples for Examples 7, 10-12, and 18-21 were also tested fordry-state and wet-state coefficients of friction, pursuant to theCoefficient Of Friction Test. The material for Example 19 was the samethermoplastic polyamide hydrogel as used for Example 18, where thematerial was in a co-extruded film form with a 0.13-millimeter materialthickness.

The material for Examples 20 and 21 was a thermoplasticpolyamide-polyether block copolymer hydrogel commercially availableunder the tradename “PEBAX MV1074” from Arkema, Inc., Clear Lake, Tex.For Example 20, the material was in a neat film form with a0.13-millimeter material thickness. For Example 21, the material was ina co-extruded film form with a 0.13-millimeter material thickness.

For comparison purposes, a film of a thermoplastic polyurethane(commercially available under the tradename “DESMOPAN DP 8795 A” fromBayer MaterialScience AG, Leverkusen, Germany; Comparative Example C),and a non-hydrogel thermoplastic polyamide (commercially available fromArkema, Inc., Clear Lake, Tex.; Comparative Example D) were also tested.Table 7 below lists the corresponding dry and wet coefficients offriction, as well as the percent reductions in the coefficients offriction between the dry and wet measurements.

TABLE 7 Percent Coefficient Coefficient Reduction in of Friction ofFriction Coefficient Sample (dry) (wet) of Friction Example 7 0.3 0.1357% Example 10 0.63 0.11 83% Example 11 0.29 0.06 79% Example 12 1.220.54 56% Example 18 0.6 0.76 −27%  Example 19 0.65 0.31 52% Example 200.59 0.47 20% Example 21 0.53 0.26 51% Comparative 0.59 0.71 −20% Example C Comparative 0.37 0.35  5% Example D

A comparison the results between Examples 7, 10-12, and 19-21 toComparative Examples C and D in Table 7 illustrate how the water take upby the materials of the present disclosure can reduce the coefficient offriction of the material surfaces. Example 18 exhibited an increase incoefficient of friction after soaking. This is believed to be due to apartial saturation state for the material, where the water present at ornear the material surface is being drawn into the material, creating atransitory tackier surface. As the material for Example 18 took upadditional water (data not shown), its coefficient of friction alsoreduced below its dry-state value.

Examples 7, 10, 11, 12, 19, 20, and 21 showed a difference between thedry-state coefficient of friction and the wet-state coefficient offriction (wet subtracted from dry) of at least 0.1, or of at least 20%.Examples 10, 11, 12, 19, and 21 had a difference of at least 0.2, or ofat least 50%.

6. Material Storage Modulus

The samples for Examples 6, 8-12, and 18 were also tested to determinetheir dry-state and wet-state storage modulus values, pursuant to theStorage Modulus Test. Table 8 lists the storage modulus values at 0%relative humidity (RH), 50% RH, and 90%, as well as the percentreductions between the 0% and 50% RH, and between the 0% and 90% RH.

TABLE 8 E′ (MPa) E′ (MPa) E′ (MPa) ΔE′50 ΔE′90 Sample 0% RH 50% RH 90%RH (%) (%) Example 6 766.6 548.3 0.03 29% 100%  Example 8 151.7 119 41.922% 72% Example 9 60.16 52.68 45.93 12% 24% Example 10 43.44 34.05 29.5822% 32% Example 11 514.9 396.8 0.86 23% 100%  Example 12 44.7 38.2 34.515% 23% Example 18 119.7 105.3 64.6 12% 46%

The mechanical properties of the sample materials and their changes uponwater uptake can demonstrate both soil shedding and durabilityproperties. First, storage modulus is inversely related to compliance,and a compliant surface is useful in preventing or reducing the adhesionof soil to the outsole, as discussed above. A decrease in the modulusupon exposure to moisture is representative of an increase in complianceof the material which has been found to be predictive of soil sheddingperformance of the material on an outsole. Additionally, the materialsof the present disclosure when dry are less compliant, which increasesdurability of the materials under dry conditions, while still allowingthe materials to increase in compliance when wet.

Examples 6, 8, 9, 10, 11, 12 and 18, when equilibrated at 50% RH, havewet-state storage moduli at least 10% below their dry state (0% RH)moduli. Additionally, Examples 6, 8, 9, 10, 11, 12 and 18, whenequilibrated at 90% RH, have wet-state storage moduli at least 20% belowtheir dry state (0% RH) moduli. Examples 6, 8, 11 and 18, whenequilibrated at 90% RH, have wet-state storage moduli at least 40% belowtheir dry state (0% RH) moduli.

7. Material Glass Transition Temperature

The samples for Examples 6, 8-12, and 18 were also tested to determinetheir dry-state and wet-state glass transition temperatures, pursuant tothe Glass Transition Temperature Test. Table 9 lists the dry and wetglass transition temperatures, as well as their reductions between thedry and wet states.

TABLE 9 T_(g, dry) T_(g, wet) ΔT_(γ) Sample (° C.) (° C.) (° C.) Example6 −27.5 −70 −42.5 Example 8 −30 −63 −33 Example 9 −25 −31 −6 Example 10−20 −37.1 −17.1 Example 11 — −63 — Example 12 −49.59 −60.59 −11 Example18 −54.93 −64.76 −9.83

As can be seen in Table 9, when water is taken up into the materialscomprising a hydrogel (Examples 6, 8, 9, 10, 11, 12 and 18), itplasticizes the hydrogel. A larger drop in the glass transitiontemperature will typically be seen for a neat film (Examples 6 and 10)compared to a co-extruded version (Examples 8 and 9, respectively.)Interestingly, Example 11 showed no measurable glass transition whendry, which suggests that there is not enough amorphous material in thesample to create a measurable signal. The appearance of a glasstransition temperature after water uptake suggests that the material iseither significantly plasticized and/or the absorbent regions are highlycrystalline in the absence of water. The plasticization of thehydrogel-containing materials as evidenced by a drop in glass transitiontemperature from the dry-state to the wet-state can distinguish thehydrogel material from materials which take up water but are notplasticized by the water.

Examples 6, 8, 9, 10, 12 and 18 have wet-state glass transitiontemperatures at least 5 degrees below their dry-state glass transitiontemperatures. In fact, Examples 6, 8, and 10 have wet-state glasstransition temperatures at least 55 degrees below their dry-state glasstransition temperatures.

8. Impact Energy Test

The samples for Examples 7, 12, 14, 16, 17, 19, and 21 were also testedfor their abilities to shed soil, pursuant to the Impact Energy Test, asshown below in Table 10.

TABLE 10 Sample Relative Impact Energy Example 7 0.60 Example 12 0.90Example 14 0.00 Example 16 0.00 Example 17 0.83 Example 19 1.03 Example21 0.95

All of the samples listed in Table 10, with the exception of Example 19,show a reduction in the relative impact energy required to dislodgeadhered wet soil from the material when compared to the unmodifiedaluminum block. Example 19 showed a slight increase in adhesion energy.However, this is believed to be due to the thickness of the sample (3millimeters), which prevented the material from taking up sufficientwater during the soaking step.

Examples 7, 12, 14, 16, 17, and 21 required a relative impact energy ofless than 1.0 in order to dislodge adhered wet soil. Examples 7, 14, and16 required a relative impact energy of less than 0.65 in order todislodge adhered wet soil.

9. Soil Shedding from Footwear

Global football/soccer footwear for Examples 22 and 23 were also testedfor soil shedding abilities, pursuant to the Soil Shedding Article Test,where Example 22 included the same footwear and materials as discussedabove for Examples 1-3, and where Example 23 included the same footwearand materials as discussed above for Examples 4 and 5.

After the test, the sample for Example 22 had an average weight gain of28.3% as compared to a control without the material, and the sample forExample 23 had an average weight gain of 37.4% as compared to thecontrol. Both examples demonstrated that the use of the materials whenpre-soaked in water are effective in preventing or reducing wet soilaccumulation. Furthermore, the material with a higher water uptakecapacity, water uptake rate, and swelling capacity (Example 22) was moreeffective in reducing wet soil accumulation as compared to a materialhaving a lower water uptake capacity (Example 23).

10. Field Use

Global football/soccer footwear for Examples 24 and 25 were also testedon a closed course during game play, where Example 24 included the samefootwear and materials as discussed above for Examples 1-3 and 22, andwhere Example 25 included the same footwear and materials as discussedabove for Examples 4, 5, and 23. Five pairs of the footwear for Example24 were tested, one pair of the footwear for Example 25 was tested, andtwo pairs of control footwear were tested (which did not include anmaterial) (Comparative Examples E and F). The footwear, initially freeof soil, were then worn by players on the closed course while playingsoccer for 90 minutes during a rainy day.

The first 45 minutes were played on a natural grass field, and second 45minutes were played on an organic/sand/clay mix field. After the90-minute playing session, the shoes were investigated for theaccumulation of soil on the outsoles over the course of the game. Asseen from the images in FIGS. 20B-20F, the five pairs of shoes with thematerial of Example 24 accumulated little to no soil, while the twopairs of control footwear for Comparative Examples E and F accumulated asubstantial amount of soil. The pair of shoes with the material ofExample 25 also accumulated soil (as shown in FIG. 20A), but theaccumulated amount was somewhat less than the control footwear ofComparative Examples E and F (as shown in FIGS. 20G and 20H). Thisillustrates the effectiveness of the materials of the present disclosurein preventing or reducing the adherence of soil.

Additionally, the footwear for Examples 24 and 25 were also used forextended durations during games on the closed course to demonstrate thelimits of their durabilities. The materials for the footwear of bothExamples 24 and 25 continue to be effective in preventing or reducingthe accumulation of soil after 100 hours of game play without anysignificant abrasion or delamination. As such, the materials of thepresent disclosure are suitable for use as ground-facing surfaces forfootwear outsoles.

CLAUSES

1. An article of manufacture comprising: a substrate body having a firstside; a hydrogel-containing material secured to the first side such thata portion of the hydrogel-containing material is embedded into thesubstrate body, the hydrogel-containing material defining at least aportion of a first external surface of the article.

2. The article of clause 1, wherein the embedded portion of thehydrogel-containing material has a cross-sectional area surrounded bythe substrate body.

3. The article as in clause 1 or 2, wherein the embedded portion of thehydrogel-containing material is an edge of the hydrogel-containingmaterial.

4. The article as in any of the preceding clauses, wherein the substratebody comprises one or more traction elements extending from the firstside such that the embedded portion of the hydrogel-containing materialis embedded into the one or more traction elements.

5. The article of clause 4, wherein at least one of the one or moretraction elements comprises a lip forming an outermost surface of thetraction element.

6. The article as in any of the preceding clauses, wherein the articleis an article of footwear.

7. The article of clause 6, wherein the article of footwear comprises anoutsole, the outsole comprising the substrate body and thehydrogel-containing material.

8. The article of clause 7, wherein the outsole comprises the firstexternal surface and a second surface opposing the first externalsurface, and the article further comprises an upper secured to thesecond surface of the outsole.

9. The article as in any of the preceding clauses, wherein the at leasta portion of the first external surface collects soil or is exposed tosoil during use of the article.

10. The article as in any of clauses 1-5, wherein the article isselected from the group consisting of footwear, a component of footwear,sporting equipment, a component of sporting equipment, apparel, acomponent of apparel, a plumbing article, a component of a plumbingarticle, a component of a vehicle, a transportation container, acomponent of a transportation container, a refuse container, a componentof a refuse container, an article of construction equipment, a componentof an article of construction equipment, an article of play equipment, acomponent of an article of play equipment, an article of landscapingequipment, a component of an article of landscaping equipment, anarticle of furniture, and a component of an article of furniture.

11. The article as in any of the preceding clauses, wherein thesubstrate body comprises a polymeric material having a water uptakecapacity of less than 10% by weight, as characterized by the WaterUptake Capacity Test with the Sampling Procedure.

12. The article of clause as in any of the preceding clauses, whereinthe substrate body compositionally comprises one or more polymersselected from the group consisting of an aliphatic thermoplasticpolyurethane, an aromatic thermoplastic polyurethane, an aliphaticpolyamide, an aromatic polyamide, and combinations thereof.

13. The article of clause 12, wherein the aliphatic polyamide comprisesa caprolactam functional group.

14. The article as in any of the preceding clauses, wherein thehydrogel-containing material has a water uptake capacity at 1 hour ofgreater than 40% by weight, as characterized by the Water UptakeCapacity Test with the Sampling Procedure.

15. The article of clause 14, wherein the water uptake capacity of thehydrogel-containing material at 1 hour is greater than 100% by weight,as characterized by the Water Uptake Capacity Test with the SamplingProcedure.

16. The article as in any of the preceding clauses, wherein thehydrogel-containing material has a water uptake rate greater than 20g/(m²×min^(0.5)), as characterized by the Water Uptake Rate Test withthe Sampling Procedure.

17. The article as in any of the preceding clauses, wherein thehydrogel-containing material has a swell thickness increase at 1 hourgreater than 20%, as characterize by the Swelling Capacity Test with theSampling Procedure.

18. The article as in any of the preceding clauses, wherein the at leasta portion of the first external surface defined by thehydrogel-containing material has a wet-state contact angle less than80°, as characterized by the Contact Angle Test with the SamplingProcedure.

19. The article as in any of the preceding clauses, wherein the at leasta portion of the first external surface defined by thehydrogel-containing material has a wet-state coefficient of frictionless than 0.8, as characterized by the Coefficient Of Friction Test withthe Sampling Procedure.

20. The article as in any of the preceding clauses, wherein thehydrogel-containing material has a wet-state glass transitiontemperature when equilibrated at 90% relative humidity and a dry-stateglass transition temperature when equilibrated at 0% relative humidity,each as characterized by the Glass Transition Temperature Test with theNeat Material Sampling Procedure, and wherein the wet-state glasstransition temperature is more than 6° C. less than the dry-state glasstransition temperature.

21. The article as in any of the preceding clauses, wherein thehydrogel-containing material has a wet-state storage modulus whenequilibrated at 90% relative humidity and a dry-state storage moduluswhen equilibrated at 0% relative humidity, each as characterized by theStorage Modulus Test with the Neat Material Sampling Procedure, andwherein the wet-state storage modulus is less than the dry-state storagemodulus of the hydrogel-containing material.

22. The article as in any of the preceding clauses, wherein thehydrogel-containing material comprises one or more polymers selectedfrom the group consisting of a polyurethane, a polyamide homopolymer, apolyamide copolymer, and combinations thereof.

23. The article of clause 22, wherein the polyamide copolymer is apolyamide block copolymer.

24. The article as in any of the preceding clauses, wherein thehydrogel-containing material comprises a thermoplastic hydrogel.

25. The article as in clause 7 or 8, wherein the hydrogel-containingmaterial is present on at least 80% of a ground-facing surface of theoutsole.

26. The article as in any of the preceding clauses, wherein thehydrogel-containing material has a dry-state thickness ranging from 0.1millimeters to 2 millimeters.

27. The article as in any of the preceding clauses, wherein thehydrogel-containing material compositionally comprises a thermoplasticpolyurethane hydrogel, and wherein the substrate body comprises a secondthermoplastic polyurethane.

28. A method of manufacturing an article of footwear, the methodcomprising: receiving an outsole comprising a substrate body, thesubstrate body compositionally comprising a polymeric material having awater uptake capacity of less than 10% by weight, as characterized bythe Water Uptake Capacity Test with the Sampling Procedure; receiving anupper; and securing the outsole and the upper to each other such that ahydrogel-containing material defines at least a portion of a firstexternal surface of the article of footwear.

29. The method of clause 28, wherein the method further comprises a stepof thermoforming or injection molding the hydrogel-containing materialto form the outsole.

30. The method as in clause 29, wherein the method further comprisesintegrally forming one or more traction elements with the outsole, orattaching one or more traction elements to the outsole, or both.

31. Use of a material compositionally comprising a hydrogel to preventor reduce soil accumulation on a first external surface of a firstarticle, which first external surface comprises the material, byproviding the material on the first external surface of the firstarticle, wherein the first article retains at least 10% less soil byweight as compared to a second article which is identical except that afirst external surface of the second article is substantially free ofthe material.

32. An article of manufacture comprising: a substrate body having afirst side and a shaft extending from the first side, the substrate bodyhaving a lip extending from the shaft such that the shaft and the lipform a junction having an angle being equal to or less than about ninetydegrees; and a hydrogel-containing material secured to the shaft suchthat a portion of the hydrogel-containing material is disposed on theouter side surface in the junction.

33. The article of clause 32, wherein the shaft is integrally formedwith the first side.

34. The article as in clause 32 or 33, wherein the hydrogel-containingmaterial is secured to the first side and the shaft, thehydrogel-containing material defining at least a portion of a firstexternal surface of the article.

35. The article as in any of clauses 32-34, wherein the angle is aboutninety degrees.

36. The article as in any of clauses 32-34, wherein the angle is lessthan about ninety degrees.

37. The article as in any of clauses 32-36, wherein the lip has a firstend extending to a second end, and the hydrogel-containing material hasa swell thickness such that, when swollen under the conditions of theSwelling Capacity Test, the increase in thickness of thehydrogel-containing material is such that the swollenhydrogel-containing material contacts the first end and the second end.

38. The article as in any of clauses 32-37, wherein the shaft and lipform a traction element.

39. The article as in any of clauses 32-38, wherein the article is anarticle of footwear.

40. The article of clause 39, wherein the article of footwear comprisesan outsole, the outsole comprising the substrate body and thehydrogel-containing material.

41. The article of clause 40, wherein the outsole comprises a firstexternal surface and a second surface opposing the first externalsurface, and the article further comprising an upper secured to thesecond surface of the outsole.

42. The article as in any of clauses 32-41, wherein the at least aportion of the outer side surface collects soil or is exposed to soilduring use of the article.

43. The article as in any of clauses 32-38, wherein the article isselected from the group consisting of footwear, a component of footwear,sporting equipment, a component of sporting equipment, apparel, acomponent of apparel, a plumbing article, a component of a plumbingarticle, a component of a vehicle, a transportation container, acomponent of a transportation container, a refuse container, a componentof a refuse container, an article of construction equipment, a componentof an article of construction equipment, an article of play equipment, acomponent of an article of play equipment, an article of landscapingequipment, a component of an article of landscaping equipment, anarticle of furniture, and a component of an article of furniture.

44. The article as in any of clauses 32-43, wherein the substrate bodycomprises a polymeric material having a water uptake capacity of lessthan 10% by weight, as characterized by the Water Uptake Capacity Testwith the Sampling Procedure.

45. The article as in any of clauses 32-44, wherein the substrate bodycompositionally comprises one or more polymers selected from the groupconsisting of an aliphatic thermoplastic polyurethane, an aromaticthermoplastic polyurethane, an aliphatic polyamide, an aromaticpolyamide, and combinations thereof.

46. The article of clause 45, wherein the aliphatic polyamide comprisesa caprolactam functional group.

47. The article as in any of clauses 32-46, wherein thehydrogel-containing material has a water uptake capacity at 1 hour ofgreater than 40% by weight, as characterized by the Water UptakeCapacity Test with the Sampling Procedure.

48. The article of clause 47, wherein the water uptake capacity of thehydrogel-containing material at 1 hour is greater than 100% by weight,as characterized by the Water Uptake Capacity Test with the SamplingProcedure.

49. The article as in any of clauses 32-48, wherein thehydrogel-containing material has a water uptake rate greater than 20g/(m²×min^(0.5)), as characterized by the Water Uptake Rate Test withthe Sampling Procedure.

50. The article as in any of clauses 32-49, wherein thehydrogel-containing material has a swell thickness increase at 1 hourgreater than 20%, as characterize by the Swelling Capacity Test with theSampling Procedure.

51. The article as in any of clauses 32-50, wherein thehydrogel-containing material has a wet-state contact angle less than80°, as characterized by the Contact Angle Test with the SamplingProcedure.

52. The article as in any of clauses 32-51, wherein thehydrogel-containing material has a wet-state coefficient of frictionless than 0.8, as characterized by the Coefficient Of Friction Test withthe Sampling Procedure.

53. The article as in any of clauses 32-52, wherein thehydrogel-containing material has a wet-state glass transitiontemperature when equilibrated at 90% relative humidity and a dry-stateglass transition temperature when equilibrated at 0% relative humidity,each as characterized by the Glass Transition Temperature Test with theNeat Material Sampling Procedure, and wherein the wet-state glasstransition temperature is more than 6° C. less than the dry-state glasstransition temperature.

54. The article as in any of clauses 32-53, wherein thehydrogel-containing material has a wet-state storage modulus whenequilibrated at 90% relative humidity and a dry-state storage moduluswhen equilibrated at 0% relative humidity, each as characterized by theStorage Modulus Test with the Neat Material Sampling Procedure, andwherein the wet-state storage modulus is less than the dry-state storagemodulus of the hydrogel-containing material.

55. The article as in any of clauses 32-54, wherein thehydrogel-containing material comprises one or more polymers selectedfrom a polyurethane, a polyamide homopolymer, a polyamide copolymer, andcombinations thereof.

56. The article of clause 55, wherein the polyamide copolymer is apolyamide block copolymer.

57. The article as in any of clauses 32-56, wherein thehydrogel-containing material comprises a thermoplastic hydrogel.

58. The article as in clause 40 or 41, wherein the hydrogel-containingmaterial is present on at least 80% of a ground-facing surface of theoutsole.

59. The article as in any of clauses 32-58, wherein thehydrogel-containing material has a dry-state thickness ranging from 0.1millimeters to 2 millimeters.

60. The article as in any of clauses 32-59, wherein thehydrogel-containing material compositionally comprises a thermoplasticpolyurethane hydrogel, and wherein the substrate body comprises a secondthermoplastic polyurethane.

61. A method of manufacturing an article, comprising: forming asubstrate body having a first side; securing a hydrogel-containingmaterial to the first side, the hydrogel-containing material defining atleast a portion of a first external surface of the article; andembedding a portion of the hydrogel-containing material into thesubstrate body.

62. The method of clause 61, wherein the embedding comprises embeddingthe portion of the hydrogel-containing material such that the materialhas a cross-sectional area surrounded by the substrate body.

63. The method of clause 61 or 62, wherein the embedding comprisesembedding an edge of the hydrogel-containing material.

64. The method of any of clauses 61-63, wherein the forming, securingand embedding steps are conducted sequentially.

65. The article of any of clauses 61-64, wherein the method furthercomprises forming one or more traction elements extending from the firstside, and the embedding comprises embedding the portion of thehydrogel-containing material into the one or more traction elements.

What is claimed is:
 1. An article of manufacture comprising: a substratebody having a first side; a hydrogel-containing material secured to thefirst side such that a portion of the hydrogel-containing material isembedded into the substrate body, the hydrogel-containing materialdefining at least a portion of a first external surface of the article,wherein the substrate body comprises one or more traction elementsextending from the first side such that the embedded portion of thehydrogel-containing material is embedded into the one or more tractionelements.
 2. The article of claim 1, wherein the embedded portion of thehydrogel-containing material has a cross-sectional area surrounded bythe substrate body.
 3. The article as in claim 1, wherein the embeddedportion of the hydrogel-containing material is an edge of thehydrogel-containing material.
 4. The article of claim 1, wherein atleast one of the one or more traction elements comprises a lip formingan outermost surface of the traction element.
 5. The article of claim 1,wherein the at least a portion of the first external surface collectssoil or is exposed to soil during use of the article.
 6. The article asin any of claim 1, wherein the article is selected from the groupconsisting of footwear, a component of footwear, sporting equipment, acomponent of sporting equipment, apparel, a component of apparel, aplumbing article, a component of a plumbing article, a component of avehicle, a transportation container, a component of a transportationcontainer, a refuse container, a component of a refuse container, anarticle of construction equipment, a component of an article ofconstruction equipment, an article of play equipment, a component of anarticle of play equipment, an article of landscaping equipment, acomponent of an article of landscaping equipment, an article offurniture, and a component of an article of furniture.
 7. The article ofclaim 1, wherein the substrate body comprises a polymeric materialhaving a water uptake capacity of less than 10% by weight, ascharacterized by the Water Uptake Capacity Test with the SamplingProcedure.
 8. The article of claim 1, wherein the substrate bodycompositionally comprises one or more polymers selected from the groupconsisting of an aliphatic thermoplastic polyurethane, an aromaticthermoplastic polyurethane, an aliphatic polyamide, an aromaticpolyamide, and combinations thereof.
 9. The article of claim 1, whereinthen hydrogel-containing material comprises a crosslinked polymericnetwork.
 10. The article of claim 9, wherein the crosslinked polymericnetwork comprises crystalline regions and amorphous hydrophilic regions,wherein the amorphous regions are covalently bonded to the crystallineregions.
 11. The article of claim 10, wherein the amorphous hydrophilicregions are bonded to the crystalline regions with carbamate linkages.12. The article of claim 9, wherein the crosslinked polymeric network isa physically crosslinked polymer network.
 13. The article of claim 9,wherein the crosslinked polymeric network includes carbamate linkages.14. The article of claim 1, wherein each of the one or more tractionelements comprises a terminal edge, and wherein the hydrogel-containingmaterial is not present on the terminal edges of any of the one or moretraction elements.
 15. The article of claim 1, wherein one or more ofthe traction elements is selected from the group consisting of: a cleat,a stud, a spike, and a lug.
 16. The article of claim 1, wherein thetraction elements are integrally formed with the substrate body.
 17. Thearticle of claim 1, wherein the traction elements are removable tractionelements.
 18. An article of manufacture comprising: a substrate bodyhaving a first side; a hydrogel-containing material secured to the firstside such that a portion of the hydrogel-containing material is embeddedinto the substrate body, the hydrogel-containing material defining atleast a portion of a first external surface of the article, wherein thearticle is an article of footwear.
 19. The article of claim 18, whereinthe article of footwear comprises an outsole, the outsole comprising thesubstrate body and the hydrogel-containing material.
 20. The article ofclaim 19, wherein the substrate body comprises one or more tractionelements extending from the first side such that the embedded portion ofthe hydrogel-containing material is embedded into the one or moretraction elements.
 21. The article of claim 19, wherein the outsolecomprises the first external surface and a second surface opposing thefirst external surface, and the article further comprises an uppersecured to the second surface of the outsole.
 22. The article of claim20, wherein at least one of the one or more traction elements comprisesa lip forming an outermost surface of the traction element.
 23. Thearticle of claim 22, wherein each of the one or more traction elementscomprises a terminal edge, and wherein the hydrogel-containing materialis not present on the terminal edges of any of the one or more tractionelements.
 24. The article of claim 22, wherein one or more of thetraction elements is selected from the group consisting of: a cleat, astud, a spike, and a lug.
 25. The article of claim 22, wherein thetraction elements are integrally formed with the outsole.
 26. Thearticle of claim 22, wherein the traction elements are removabletraction elements.
 27. The article of claim 18, wherein the embeddedportion of the hydrogel-containing material has a cross-sectional areasurrounded by the substrate body.
 28. The article of claim 18, whereinthe embedded portion of the hydrogel-containing material is an edge ofthe hydrogel-containing material.
 29. The article of claim 18, whereinthe substrate body comprises a polymeric material having a water uptakecapacity of less than 10% by weight, as characterized by the WaterUptake Capacity Test with the Sampling Procedure.
 30. The article ofclaim 18, wherein the substrate body compositionally comprises one ormore polymers selected from the group consisting of an aliphaticthermoplastic polyurethane, an aromatic thermoplastic polyurethane, analiphatic polyamide, an aromatic polyamide, and combinations thereof.31. The article of claim 18, wherein then hydrogel-containing materialcomprises a crosslinked polymeric network.
 32. The article of claim 31,wherein the crosslinked polymeric network comprises crystalline regionsand amorphous hydrophilic regions, wherein the amorphous regions arecovalently bonded to the crystalline regions.
 33. The article of claim32, wherein the amorphous hydrophilic regions are bonded to thecrystalline regions with carbamate linkages.
 34. The article of claim31, wherein the crosslinked polymeric network is a physicallycrosslinked polymer network.
 35. The article of claim 31, wherein thecrosslinked polymeric network includes carbamate linkages.
 36. Anarticle of manufacture comprising: a substrate body having a first sideand a shaft extending from the first side, the substrate body having alip extending from the shaft such that the shaft and the lip form ajunction having an angle being equal to or less than about ninetydegrees; and a hydrogel-containing material secured to the shaft suchthat a portion of the hydrogel-containing material is disposed on anouter side surface of the shaft and in the junction.
 37. The article ofclaim 36, wherein the shaft is integrally formed with the substratebody.
 38. The article as in claim 36, wherein the hydrogel-containingmaterial is secured to the first side and the shaft, thehydrogel-containing material defining at least a portion of a firstexternal surface of the article.
 39. The article as in claim 36, whereinthe angle is about ninety degrees.
 40. The article as in claim 36,wherein the article is an article of footwear.
 41. The article of claim36, wherein the substrate body comprises one or more traction elementsextending from the first side and wherein the shaft is part of atraction element of the one or more traction elements.
 42. The articleof claim 41, wherein each of the one or more traction elements comprisesa terminal edge, and wherein the hydrogel-containing material is notpresent on the terminal edges of any of the one or more tractionelements.
 43. The article of claim 41, wherein one or more of thetraction elements is selected from the group consisting of: a cleat, astud, a spike, and a lug.
 44. The article of claim 41, wherein thetraction elements are integrally formed with the substrate body.
 45. Thearticle of claim 41, wherein the traction elements are removabletraction elements.
 46. The article of claim 36, wherein thenhydrogel-containing material comprises a crosslinked polymeric network.47. The article of claim 46, wherein the crosslinked polymeric networkcomprises crystalline regions and amorphous hydrophilic regions, whereinthe amorphous regions are covalently bonded to the crystalline regions.48. The article of claim 47, wherein the amorphous hydrophilic regionsare bonded to the crystalline regions with carbamate linkages.
 49. Thearticle of claim 46, wherein the crosslinked polymeric network is aphysically crosslinked polymer network.
 50. The article of claim 46,wherein the crosslinked polymeric network includes carbamate linkages.